The technics of combined treatment of ion nitrocarburizing-ion sulphurizing of CrMoCu alloy cast iron has been investigated and the compound layer with nitrocarbonide and sulphide has been made on the surface of CrMoC...The technics of combined treatment of ion nitrocarburizing-ion sulphurizing of CrMoCu alloy cast iron has been investigated and the compound layer with nitrocarbonide and sulphide has been made on the surface of CrMoCu alloy cast iron. The compound layer is composed of sulfide surface layer and the nitrocarbonide hypo-surface layer and its diffusing layer. The size of sulfide globular grains distributing equably on the surface is in nano-rnicron-scale, and the phase structure of the compound layer is composed of FeS^ FeSi^ Fe2C and Fe3N. Under dry sliding condition, the friction-reducing of sulphurized surface is good, but its function time can’t last very long. The nitrocarbonided+sulphurized surface can greatly improve the wear-resistance and the friction-reducing of CrMoCu alloy cast iron, and its integrated friction and wear properties are better than plain and sulphurized surfaces’.展开更多
Low-temperature sulfurizing after nitrocarburizing are compared with only low-temperature sulfurizing on the surface of CrMoCu alloyed cast iron, the surface morphologies and microstructures are investigated by SEM an...Low-temperature sulfurizing after nitrocarburizing are compared with only low-temperature sulfurizing on the surface of CrMoCu alloyed cast iron, the surface morphologies and microstructures are investigated by SEM and EDS. Results show that under proper treatment parameters, there are sulfide layer on both of the surfaces, and can more easily obtain sulfide layers on the surface of nitrocarburizing. Forming mechanism of sulfides were also studied elementarily.展开更多
基金This rescarch is granted by National Natural Science Foundation of China(50235030)“973”Project(G1999065009).
文摘The technics of combined treatment of ion nitrocarburizing-ion sulphurizing of CrMoCu alloy cast iron has been investigated and the compound layer with nitrocarbonide and sulphide has been made on the surface of CrMoCu alloy cast iron. The compound layer is composed of sulfide surface layer and the nitrocarbonide hypo-surface layer and its diffusing layer. The size of sulfide globular grains distributing equably on the surface is in nano-rnicron-scale, and the phase structure of the compound layer is composed of FeS^ FeSi^ Fe2C and Fe3N. Under dry sliding condition, the friction-reducing of sulphurized surface is good, but its function time can’t last very long. The nitrocarbonided+sulphurized surface can greatly improve the wear-resistance and the friction-reducing of CrMoCu alloy cast iron, and its integrated friction and wear properties are better than plain and sulphurized surfaces’.
文摘Low-temperature sulfurizing after nitrocarburizing are compared with only low-temperature sulfurizing on the surface of CrMoCu alloyed cast iron, the surface morphologies and microstructures are investigated by SEM and EDS. Results show that under proper treatment parameters, there are sulfide layer on both of the surfaces, and can more easily obtain sulfide layers on the surface of nitrocarburizing. Forming mechanism of sulfides were also studied elementarily.