Fracture behavior of CrN coatings deposited on the surface of silicon and AISI52100 steel by different energy ion beam assisted magnetron sputtering technique （IBAMS） was studied using indentation and dynamic cycle ...Fracture behavior of CrN coatings deposited on the surface of silicon and AISI52100 steel by different energy ion beam assisted magnetron sputtering technique （IBAMS） was studied using indentation and dynamic cycle impact. It is found that, for the coatings on silicon substrate, the cracks form in the indentation corners and then propagate outward under Vickers indentation. The coating prepared using ion assisted energy of 800 eV shows the highest fracture resistance due to its compact structure. Under Rockwell indentation, only finer radial cracks are found in the CrN coating on AISI 52100 steel without ion assisting while in the condition of ion assisting energy of 800 eV, radial, lateral cracks and spalling appear in the vicinity of indentation. The fracture of CrN coatings under dynamic cycle impact is similar to fatigue. The impact fracture resistance of CrN coatings increases with the increase of ion assisting energy.展开更多
TiN/CrN multilayered hard coatings with TiCrN interlayer were deposited onhigh speed steel substrates by using a filtered cathodic vacuum arc technique. The structure andcomposition of the coatings were characterized ...TiN/CrN multilayered hard coatings with TiCrN interlayer were deposited onhigh speed steel substrates by using a filtered cathodic vacuum arc technique. The structure andcomposition of the coatings were characterized by scanning electron microscopy (SEM) and Augerelectron spectroscopy (AES). A high adhesion of up to 80 N was demonstrated by scratching tests forthe multi-layered coatings. Nanoindentation tests were performed to determine the hardness andelastic modulus of the coatings as a function of the multiplayer modulation period. It was observedthat the hardness of the multilayered coatings is higher than those of either TiN or CrN singlecoatings, and it increases with decreasing modulation periods, which is consistent with predictionsfrom the Hall-Petch type strengthening mechanism, though at small modulation periods, deviation fromthe Hall-Petch relation has been observed for the multilayered coatings. The life-span of drillscoated with TiN/CrN multilayered is triple as long as that coated with TiN layer.展开更多
Titanium and its alloys are widely used as materials for bio-medical applications, such as implants. However, ions of the alloy can release to the body region and spread into the blood circulation. In this study, plas...Titanium and its alloys are widely used as materials for bio-medical applications, such as implants. However, ions of the alloy can release to the body region and spread into the blood circulation. In this study, plasma nitriding and CrN coating techniques are used in order to overcome the problem of ion release. The objective of this study was to investigate the effects of plasma nitrided pure titanium on the structural properties and corrosion behaviors before and after CrN coating in Ringer＇s solution at 37℃. The structural properties were investigated using Scanning Electron Microscopy （SEM） and X-ray diffraction （XRD）. A diffusion layer and a compound layer composed of δ-TiN and ε-Ti2N phases were observed on the surface of nitrided pure titanium. Corrosion tests were made for the determination of electrochemical properties with the help of Potentio- stat/Galvanostat device. The results show that corrosion behaviors of untreated and treated samples have similar characteristic.展开更多
基金Funded by the National Natural Science Foundation of China(No. 50771070)Shanxi Province Science and Technology Key Projects (No. 20100321078-02)
文摘Fracture behavior of CrN coatings deposited on the surface of silicon and AISI52100 steel by different energy ion beam assisted magnetron sputtering technique （IBAMS） was studied using indentation and dynamic cycle impact. It is found that, for the coatings on silicon substrate, the cracks form in the indentation corners and then propagate outward under Vickers indentation. The coating prepared using ion assisted energy of 800 eV shows the highest fracture resistance due to its compact structure. Under Rockwell indentation, only finer radial cracks are found in the CrN coating on AISI 52100 steel without ion assisting while in the condition of ion assisting energy of 800 eV, radial, lateral cracks and spalling appear in the vicinity of indentation. The fracture of CrN coatings under dynamic cycle impact is similar to fatigue. The impact fracture resistance of CrN coatings increases with the increase of ion assisting energy.
基金This work was financially supported by the Science Foundation of Lanzhou Institute Chemistry and Physics, Chinese Academy of Science (No.01-03).
文摘TiN/CrN multilayered hard coatings with TiCrN interlayer were deposited onhigh speed steel substrates by using a filtered cathodic vacuum arc technique. The structure andcomposition of the coatings were characterized by scanning electron microscopy (SEM) and Augerelectron spectroscopy (AES). A high adhesion of up to 80 N was demonstrated by scratching tests forthe multi-layered coatings. Nanoindentation tests were performed to determine the hardness andelastic modulus of the coatings as a function of the multiplayer modulation period. It was observedthat the hardness of the multilayered coatings is higher than those of either TiN or CrN singlecoatings, and it increases with decreasing modulation periods, which is consistent with predictionsfrom the Hall-Petch type strengthening mechanism, though at small modulation periods, deviation fromthe Hall-Petch relation has been observed for the multilayered coatings. The life-span of drillscoated with TiN/CrN multilayered is triple as long as that coated with TiN layer.
文摘Titanium and its alloys are widely used as materials for bio-medical applications, such as implants. However, ions of the alloy can release to the body region and spread into the blood circulation. In this study, plasma nitriding and CrN coating techniques are used in order to overcome the problem of ion release. The objective of this study was to investigate the effects of plasma nitrided pure titanium on the structural properties and corrosion behaviors before and after CrN coating in Ringer＇s solution at 37℃. The structural properties were investigated using Scanning Electron Microscopy （SEM） and X-ray diffraction （XRD）. A diffusion layer and a compound layer composed of δ-TiN and ε-Ti2N phases were observed on the surface of nitrided pure titanium. Corrosion tests were made for the determination of electrochemical properties with the help of Potentio- stat/Galvanostat device. The results show that corrosion behaviors of untreated and treated samples have similar characteristic.