Experimental study is performed on the probabilistic models for the long fatigue crack growth rates (da/dN) of LZ50 axle steel. An equation for crack growth rate was derived to consider the trend of stress intensity f...Experimental study is performed on the probabilistic models for the long fatigue crack growth rates (da/dN) of LZ50 axle steel. An equation for crack growth rate was derived to consider the trend of stress intensity factor range going down to the threshold and the average stress effect. The probabilistic models were presented on the equation. They consist of the probabilistic da/dN-ΔK relations, the confidence-based da/dN-ΔK relations, and the probabilistic- and confidence-based da/dN-ΔK relations. Efforts were made respectively to characterize the effects of probabilistic assessments due to the scattering regularity of test data, the number of sampling, and both of them. These relations can provide wide selections for practice. Analysis on the test data of LZ50 steel indicates that the present models are available and feasible.展开更多
Experimental study is performed on the probabilistic models for the long fatigue crack growth rates （da/dN） of LZ50 axle steel. An equation for crack growth rate was derived to consider the trend of stress intensity...Experimental study is performed on the probabilistic models for the long fatigue crack growth rates （da/dN） of LZ50 axle steel. An equation for crack growth rate was derived to consider the trend of stress intensity factor range going down to the threshold and the average stress effect. The probabilistic models were presented on the equation. They consist of the probabilistic da/dN-△K relations, the confidence-based da/dN-△K relations, and the probabilistic- and confidence-based da/dN-△K relations. Efforts were made respectively to characterize the effects of probabilistic assessments due to the scattering regularity of test data, the number of sampling, and both of them. These relations can provide wide selections for practice. Analysis on the test data of LZ50 steel indicates that the present models are available and feasible.展开更多
SEM microfractography of near-threshold fatigue crack propagation were carried out in the dual-phase steels of 3 martensite morphologies and 6 volume fractions of martensite (V_m). All of them are featured by cyclic c...SEM microfractography of near-threshold fatigue crack propagation were carried out in the dual-phase steels of 3 martensite morphologies and 6 volume fractions of martensite (V_m). All of them are featured by cyclic cleavage characteristics in near-threshold region,i.e.,main- ly controlled by mode Ⅱ stress.In the higher ΔK regions,the fracture surfaces are character- ized by mixed modes including cyclic cleavage facets,two types of secondary cracks and striations,etc..The roughness-induced crack closure of fracture surface is attributed primarily to extreme high fatigue crack growth threshold values.展开更多
It is obtained in this paper that the fatigue threshold value of mode H was 1.9 times of that of mode Ⅰ in dual-phase steel(DPS),and the normal stress intensity factor range oJ mode Ⅱ branch crack tip was 2.2 times ...It is obtained in this paper that the fatigue threshold value of mode H was 1.9 times of that of mode Ⅰ in dual-phase steel(DPS),and the normal stress intensity factor range oJ mode Ⅱ branch crack tip was 2.2 times of that of mode Ⅰ.Above results illustrate that the resistance of mode Ⅱ crack growth was higher than that of mode Ⅰ,the former resulting from roughness-induced shear resistance,the latter,crack closure. The mode Ⅱ component can play two important roles in near-threshold fatigue crack growth:(1)increasing crack tip plasticity which accelerates the crack growth and(2)intro- ducing crack surface contact and rubbing to reduce the crack propagation rate.By means of crack closure,the quantity of shear resistance was easily solved in this paper.The friction shear stress strength factor range of mode Ⅱ,K_,is still much higher than the closure stress strength factor range of mode Ⅰ,K_(Ⅰ,cl).This illustrated that the roughness enlarged the second role and played a role of shielding crack tip from mode Ⅱ crack.展开更多
Determination was carried out of fatigue crack propagation rate of steel 65Cr5Mo3W2VSiTi (LM2)with various bainite contents and M/B duplex structure tempered at various tempera- tures.The threshold value of fatigue fo...Determination was carried out of fatigue crack propagation rate of steel 65Cr5Mo3W2VSiTi (LM2)with various bainite contents and M/B duplex structure tempered at various tempera- tures.The threshold value of fatigue for each processing was estimated by experimental data. The mechanism for fatigue crack propagation of M/B duplex structure in steel LM2 seems to be non-continuous.The calculated fatigue crack micro-propagation rates are found to agree with the experimental data.展开更多
基金Project supported by the National Natural Science Foundation of China (Nos.50375130and50323003), the Special Foundation of National Excellent Ph.D.Thesis (No.200234) and thePlanned Itemforthe Outstanding Young Teachers ofMinistry ofEducationofChina (No.2101)
文摘Experimental study is performed on the probabilistic models for the long fatigue crack growth rates (da/dN) of LZ50 axle steel. An equation for crack growth rate was derived to consider the trend of stress intensity factor range going down to the threshold and the average stress effect. The probabilistic models were presented on the equation. They consist of the probabilistic da/dN-ΔK relations, the confidence-based da/dN-ΔK relations, and the probabilistic- and confidence-based da/dN-ΔK relations. Efforts were made respectively to characterize the effects of probabilistic assessments due to the scattering regularity of test data, the number of sampling, and both of them. These relations can provide wide selections for practice. Analysis on the test data of LZ50 steel indicates that the present models are available and feasible.
基金国家自然科学基金，Special Foundation of National Excellent Ph.D.Thesis，Outstanding Young Teachers of Ministry of Education of China
文摘Experimental study is performed on the probabilistic models for the long fatigue crack growth rates （da/dN） of LZ50 axle steel. An equation for crack growth rate was derived to consider the trend of stress intensity factor range going down to the threshold and the average stress effect. The probabilistic models were presented on the equation. They consist of the probabilistic da/dN-△K relations, the confidence-based da/dN-△K relations, and the probabilistic- and confidence-based da/dN-△K relations. Efforts were made respectively to characterize the effects of probabilistic assessments due to the scattering regularity of test data, the number of sampling, and both of them. These relations can provide wide selections for practice. Analysis on the test data of LZ50 steel indicates that the present models are available and feasible.
文摘SEM microfractography of near-threshold fatigue crack propagation were carried out in the dual-phase steels of 3 martensite morphologies and 6 volume fractions of martensite (V_m). All of them are featured by cyclic cleavage characteristics in near-threshold region,i.e.,main- ly controlled by mode Ⅱ stress.In the higher ΔK regions,the fracture surfaces are character- ized by mixed modes including cyclic cleavage facets,two types of secondary cracks and striations,etc..The roughness-induced crack closure of fracture surface is attributed primarily to extreme high fatigue crack growth threshold values.
文摘It is obtained in this paper that the fatigue threshold value of mode H was 1.9 times of that of mode Ⅰ in dual-phase steel(DPS),and the normal stress intensity factor range oJ mode Ⅱ branch crack tip was 2.2 times of that of mode Ⅰ.Above results illustrate that the resistance of mode Ⅱ crack growth was higher than that of mode Ⅰ,the former resulting from roughness-induced shear resistance,the latter,crack closure. The mode Ⅱ component can play two important roles in near-threshold fatigue crack growth:(1)increasing crack tip plasticity which accelerates the crack growth and(2)intro- ducing crack surface contact and rubbing to reduce the crack propagation rate.By means of crack closure,the quantity of shear resistance was easily solved in this paper.The friction shear stress strength factor range of mode Ⅱ,K_,is still much higher than the closure stress strength factor range of mode Ⅰ,K_(Ⅰ,cl).This illustrated that the roughness enlarged the second role and played a role of shielding crack tip from mode Ⅱ crack.
文摘Determination was carried out of fatigue crack propagation rate of steel 65Cr5Mo3W2VSiTi (LM2)with various bainite contents and M/B duplex structure tempered at various tempera- tures.The threshold value of fatigue for each processing was estimated by experimental data. The mechanism for fatigue crack propagation of M/B duplex structure in steel LM2 seems to be non-continuous.The calculated fatigue crack micro-propagation rates are found to agree with the experimental data.