Cr_(2)O_(3)-bearing castables bonded with reactive MgO(RM)or calcium aluminate cement(CAC)were studied to evaluate the binder effect on their performance in corrosive environments.The properties of the as-prepared cas...Cr_(2)O_(3)-bearing castables bonded with reactive MgO(RM)or calcium aluminate cement(CAC)were studied to evaluate the binder effect on their performance in corrosive environments.The properties of the as-prepared castables were compared with respect to the differences in phase composition and microstructure.The corrosion behavior of the as-prepared castables by CaO-Al_(2)O_(3)-Fe_(2)O_(3)-SiO_(2)-based slag was systematically compared viarefractory cup testing at 1600℃with respect to the differences in phase composition and microstructure.The analysis indicates that RM bonded castables show higher apparent porosity,lower bulk density and strengths after drying at 110℃and firing at 1300℃,and higher permanent linear change after firing at 1300℃,but better slag corrosion and infiltration resistance compared with CAC bonded castables.展开更多
基金the Joint Founds of R&D Program of Henan Province (222301420034)National Natural Science Foundation of China (51802287)Collaborative Innovation Major Special Project of Zhengzhou (No. 20XTZX12025) for the financial support
文摘Cr_(2)O_(3)-bearing castables bonded with reactive MgO(RM)or calcium aluminate cement(CAC)were studied to evaluate the binder effect on their performance in corrosive environments.The properties of the as-prepared castables were compared with respect to the differences in phase composition and microstructure.The corrosion behavior of the as-prepared castables by CaO-Al_(2)O_(3)-Fe_(2)O_(3)-SiO_(2)-based slag was systematically compared viarefractory cup testing at 1600℃with respect to the differences in phase composition and microstructure.The analysis indicates that RM bonded castables show higher apparent porosity,lower bulk density and strengths after drying at 110℃and firing at 1300℃,and higher permanent linear change after firing at 1300℃,but better slag corrosion and infiltration resistance compared with CAC bonded castables.
基金supported by the Natural Science Foundation of Zhejiang Province,China(Y4100001)Science Technology Planning Project ofZhejiang Province,China(2009F70004,2009R50020-6)~~
基金This work was supported by the National Natural Science Foundation of China(No.92045303)the China Postdoctoral Science Foundation(No.2020M681444).The computational resources from Sinopec Geophysical Research Institute are acknowledged.