Quasi-static and high strain rate compressive experiments on vinyl ester casting were carried out by means of MTS (Material Test System) and Hopkinson bar. The behaviors of the compressed unstable and fracture of the ...Quasi-static and high strain rate compressive experiments on vinyl ester casting were carried out by means of MTS (Material Test System) and Hopkinson bar. The behaviors of the compressed unstable and fracture of the resin casting at different strain rates were investigated.The results indicate that the response behavior of the resin casting is controlled by different mechanisms at different strain rate, and some mechanical properties of vinyl ester casting are rate-dependent: the casting are destroyed in toughness model under strain rate 3.3×10 -4～6.6×10 -3/s, while the casting are destroyed in brittleness model under strain rate 950～5800/s. The yield stress, yield strain energy density are all increased with the increasing strain rates at quasi-static as well as at high strain rates. What is interesting is that the yield strain decreased with the strain rates increasing at quasi-static while increased at high strain rates. It is considered that the casting occurred forcing high elastic deformation at high strain rates. The damage of the specimens is mainly controlled by axial stress before unstable deformation, while mainly controlled by shear stress after unstable deformation, and then developed to fracture finally. This progress is rate-dependent: the development of the cracks inside the castings increased with the strain rate increasing.展开更多
文摘Quasi-static and high strain rate compressive experiments on vinyl ester casting were carried out by means of MTS (Material Test System) and Hopkinson bar. The behaviors of the compressed unstable and fracture of the resin casting at different strain rates were investigated.The results indicate that the response behavior of the resin casting is controlled by different mechanisms at different strain rate, and some mechanical properties of vinyl ester casting are rate-dependent: the casting are destroyed in toughness model under strain rate 3.3×10 -4～6.6×10 -3/s, while the casting are destroyed in brittleness model under strain rate 950～5800/s. The yield stress, yield strain energy density are all increased with the increasing strain rates at quasi-static as well as at high strain rates. What is interesting is that the yield strain decreased with the strain rates increasing at quasi-static while increased at high strain rates. It is considered that the casting occurred forcing high elastic deformation at high strain rates. The damage of the specimens is mainly controlled by axial stress before unstable deformation, while mainly controlled by shear stress after unstable deformation, and then developed to fracture finally. This progress is rate-dependent: the development of the cracks inside the castings increased with the strain rate increasing.