Due to the complex structure and dense weld of the orthotropic steel bridge deck(OSBD),fatigue cracks are prone to occur in the typical welding details.Welding residual stress(WRS)will cause a plastic zone at the crac...Due to the complex structure and dense weld of the orthotropic steel bridge deck(OSBD),fatigue cracks are prone to occur in the typical welding details.Welding residual stress(WRS)will cause a plastic zone at the crack tip.In this paper,an elastoplastic constitutive model based on the Chaboche kinematic hardening model was introduced,and the extended finite element method(XFEM)was used to study the influence of material elastoplasticity and crack tip plastic zone on the law of fatigue crack propagation.By judging the stress state of the residual stress field at the crack tip and selecting different crack propagation rate models to investigate the crack propagation law when plastic deformation was considered,the propagation path and propagation rate of fatigue crack of the OSBD were obtained.The results show that,whether the residual stress field is considered or not,the plastic deformation at the crack tip will not cause the obvious closure of the fatigue crack at the U-rib toe during the crack propagation process,but will significantly affect the crack propagation path.When material plasticity is considered,the propagation angle of fatigue crack at the U-rib toe basically remains unchanged along the short-axis direction of the initial crack,but is going up along the long-axis direction,and the crack tip plastic zone inhibits the propagation of the crack tip on one side.Compared with linear elastic materials,the crack propagation law considering material plasticity is more consistent with that in actual bridge engineering.In terms of the propagation rate,if the residual stress field is not considered,the fatigue crack propagation rate at U-rib toe with plasticity considered is slightly higher than that without plasticity considered,because plastic deformation will affect the amplitude of energy release rate.When considering the WRS field,the fatigue crack propagation rate at U-rib toe is increased due to the combined actions of plastic deformation and stress ratio R.展开更多
A discontinuous deformation and displacement(DDD) analysis method is proposed for modelling the rock failure process. This method combines the rock failure process analysis(RFPA) method(based on finite element method)...A discontinuous deformation and displacement(DDD) analysis method is proposed for modelling the rock failure process. This method combines the rock failure process analysis(RFPA) method(based on finite element method) and discontinuous deformation analysis(DDA) method. RFPA is used to simulate crack initiation, propagation and coalescence processes of rock during the small deformation state. The DDA method is used to simulate the movement of blocks created by the multiple cracks modelled by the RFPA. The newly developed DDD method is particularly suitable for modelling both crack propagation and block movement during the rock failure process because of the natural and convenient coupling of continuous and discontinuous deformation analyses. The proposed method has been used to simulate crack initiation, propagation and coalescence within a slope as well as the block movement during the landslide process. Numerical modelling results indicate that the proposed DDD method can automatically simulate crack propagation and block movement during the rock failure process without degrading accuracy.展开更多
基金The works described in this paper are substantially supported by the grant from the National Natural Science Foundation of China(Grant No.51678135)the Natural Science Foundation of Jiangsu Province(No.BK20171350)Six Talent Peak Projects in Jiangsu Province(JNHB-007),which are gratefully acknowledged.
文摘Due to the complex structure and dense weld of the orthotropic steel bridge deck(OSBD),fatigue cracks are prone to occur in the typical welding details.Welding residual stress(WRS)will cause a plastic zone at the crack tip.In this paper,an elastoplastic constitutive model based on the Chaboche kinematic hardening model was introduced,and the extended finite element method(XFEM)was used to study the influence of material elastoplasticity and crack tip plastic zone on the law of fatigue crack propagation.By judging the stress state of the residual stress field at the crack tip and selecting different crack propagation rate models to investigate the crack propagation law when plastic deformation was considered,the propagation path and propagation rate of fatigue crack of the OSBD were obtained.The results show that,whether the residual stress field is considered or not,the plastic deformation at the crack tip will not cause the obvious closure of the fatigue crack at the U-rib toe during the crack propagation process,but will significantly affect the crack propagation path.When material plasticity is considered,the propagation angle of fatigue crack at the U-rib toe basically remains unchanged along the short-axis direction of the initial crack,but is going up along the long-axis direction,and the crack tip plastic zone inhibits the propagation of the crack tip on one side.Compared with linear elastic materials,the crack propagation law considering material plasticity is more consistent with that in actual bridge engineering.In terms of the propagation rate,if the residual stress field is not considered,the fatigue crack propagation rate at U-rib toe with plasticity considered is slightly higher than that without plasticity considered,because plastic deformation will affect the amplitude of energy release rate.When considering the WRS field,the fatigue crack propagation rate at U-rib toe is increased due to the combined actions of plastic deformation and stress ratio R.
基金supported by the National Basic Research Program of China("973"Project)(Grant No.2014CB047100)the National Natural Science Foundation of China(Grant Nos.51421064,51474046 & 51174039)the Fundamental Research Funds for the Central Universities(Grant No.DUT14LK21)
文摘A discontinuous deformation and displacement(DDD) analysis method is proposed for modelling the rock failure process. This method combines the rock failure process analysis(RFPA) method(based on finite element method) and discontinuous deformation analysis(DDA) method. RFPA is used to simulate crack initiation, propagation and coalescence processes of rock during the small deformation state. The DDA method is used to simulate the movement of blocks created by the multiple cracks modelled by the RFPA. The newly developed DDD method is particularly suitable for modelling both crack propagation and block movement during the rock failure process because of the natural and convenient coupling of continuous and discontinuous deformation analyses. The proposed method has been used to simulate crack initiation, propagation and coalescence within a slope as well as the block movement during the landslide process. Numerical modelling results indicate that the proposed DDD method can automatically simulate crack propagation and block movement during the rock failure process without degrading accuracy.