Two Al2O3/Cu composites containing 0.24 wt.% Al2O3 and 0.60 wt.% Al2O3 separately are prepared by internal oxidation. Effects of sliding speed and pressure on the frictional characteristics of the composites and coppe...Two Al2O3/Cu composites containing 0.24 wt.% Al2O3 and 0.60 wt.% Al2O3 separately are prepared by internal oxidation. Effects of sliding speed and pressure on the frictional characteristics of the composites and copper against brass are investigated and compared. The changes in morphology of the sliding surface and subsurface are examined with scanning electron microscope （SEM） and energy dispersive X-ray spectrum （EDS）. The results show that the wear resistance of the Al2O3/Cu composites is superior to that of copper under the same conditions, Under a given electrical current, the wear rate of Al2O3/Cu composites decreases as the Al2O3-content increases, However, the wear rates of the Al2O3/Cu composites and copper increase as the sliding speed and pressure increase under dry sliding condition. The main wear mechanisms for Al2O3/Cu composites are of abrasion and adhesion; for copper, it is adhesion, although wear by oxidation and electrical erosion can also be observed as the speed and pressure rise.展开更多
Microstructure and interracial reactions of Al2O3 joints brazed with Al2O3-particulate-contained composite Ag-Cu-Ti filler material were researched by scanning electron microscopy （SEM）, electron probe microscopy an...Microstructure and interracial reactions of Al2O3 joints brazed with Al2O3-particulate-contained composite Ag-Cu-Ti filler material were researched by scanning electron microscopy （SEM）, electron probe microscopy analysis （EPMA）, energy dispersive spectroscopy （EDS） and X-ray diffraction （XRD）. The interracial reaction layer thickness of joints brazed with conventional active filler metal and active composite filler materials with different volume fraction of Al2O3 particulate was also studied. The experimental results indicated although there were Al2O3 particulates added into active filler metals, the time dependence of interracial layer growth of joints brazed with active composite filler material is t^1/2 as described by Fickian law as the joints brazed with conventional active filler metal.展开更多
Cs0.35V2O5 was successfully synthesized as cathode material for lithium secondary battery by the rheological phase reaction method from Cs2CO3 and NH4VO3. The Cs0.35V2O5/Cu composite material was prepared by the displ...Cs0.35V2O5 was successfully synthesized as cathode material for lithium secondary battery by the rheological phase reaction method from Cs2CO3 and NH4VO3. The Cs0.35V2O5/Cu composite material was prepared by the displacement reaction in CuSO4 solution using zinc powder as a reductant. The structure and electrochemical property of the so-prepared powders were characterized by means of XRD （powder X-ray diffraction） and the galvanostatic discharge-charge techniques. The results show that the electrochemical property of Cs0.35V2O5/Cu composite material is significantly improved compared to the bulk Cs0.35V2O5 material. The Cs0.35V2O5/Cu composite material exhibits the first discharge capacity as high as 164.3 mAh.g -1 in the range of 4.2-1.8V at a current rate of 10 mA.g-1 and remains at a stable discharge capacity of about 110 mAh.g-1 within 40 cycles.展开更多
The preferred internal oxidation of aluminum in Cu Al alloy was used to obtain in situ Al 2O 3/Cu composites. The reinforcement particles were mainly γ Al 2O 3, some θ Al 2O 3 and a little α Al 2O 3. Thermodynamics...The preferred internal oxidation of aluminum in Cu Al alloy was used to obtain in situ Al 2O 3/Cu composites. The reinforcement particles were mainly γ Al 2O 3, some θ Al 2O 3 and a little α Al 2O 3. Thermodynamics analyses show that the chemical reactions are 3Cu 2O+2Al=6Cu+Al 2O 3 or 3CuO+2Al=3Cu+Al 2O 3. A related equilibrium diagram was drawn. The experiments and investigation show that the formation rate of Al 2O 3 was controlled by the diffusion of oxygen in matrix.展开更多
Alumina dispersion strengthened copper composite （nano-Al2O3/Cu composite） was recently emerged as a kind of potentially viable and attractive engineering material for applications requiring high strength, high ther...Alumina dispersion strengthened copper composite （nano-Al2O3/Cu composite） was recently emerged as a kind of potentially viable and attractive engineering material for applications requiring high strength, high thermal and electrical conductivities and resistance to softening at elevated temperatures. The nano-Al2O3/Cu composite was produced by internal oxidation. The microstructures of the composite were analyzed by the TEM and its hot deformation behavior was investigated by means of continuous compression tests performed on a Gleeble 1500 thermo-simulator. Making use of the modified algorithm-Levenberg-Marquardt （L-M） algorithm BP neural network, a model for predicting the flow stresses during hot deformation was set up on the base of the experimental data. Results show that the microstructures of the composite are characterized by uniform distribution of nano-Al2O3 particles in Cu-matrix. The sliding of dislocations is the main deformation mechanism. The dynamic recovery is the main softening mode with the flow stress decreasing gently from 500℃ to 850 ~C. The recrystallization of Cu-matrix can be retarded late into as high as 850 ℃, when it happens only partially. The well-trained BP neural network model can accurately describe the influence of the temperature, strain rate, and true strain on the flow stresses, therefore, it can precisely predict the flow stresses of the composite under given deforming conditions and provide a new way to optimize hot deforming process parameters.展开更多
Silver as a highly conductive metal is usually doped in YBa2Cu3O7-x superconductor bulks to improve critical current density of YBa2Cu3O7-x superconductor.The valuable metal elements silver,yttrium,barium and copper i...Silver as a highly conductive metal is usually doped in YBa2Cu3O7-x superconductor bulks to improve critical current density of YBa2Cu3O7-x superconductor.The valuable metal elements silver,yttrium,barium and copper in waste YBa2Cu3O7-x/Ag composite superconductor bulks were recovered,respectively.Silver was recovered with process at first,the waste was dissolved by nitric acid and silver chloride was precipitated by adding chloride acid,then silver pig was obtained by melting silver chloride together with sodium carbonate at 1 000℃.The effective factors on recovery ratio and purity of silver were studied.The chemical analysis proves that the purity of silver ingot is 95.86%.The recovery ratio of silver is calculated to be 92.56%.The loss of silver may be due to the loss of silver chloride during filtering and the volatilization of silver when silver chloride and sodium carbonate are smelted at high temperature.For other three metal elements,Y3 +,Ba 2+and Cu 2+,in the surplus waste liquid after recovering silver, they were separated with the sequence of barium,copper and then yttrium step by step.First,sulfate acid was used to precipitate barium sulfate.Then,sodium sulfide was added to the surplus solution so that copper could be separated as copper sulfide.During this separation procedure,it was important to control the pH value to be 1-2.After that,oxalic acid was added into the surplus solution to obtain yttrium oxalate.Finally,yttrium oxide was formed by burning yttrium oxalate.The XRD results indicate that the final products are all single-phase compounds as BaSO4,CuS and Y2O3,respectively.展开更多
This work concerns with the high temperature deformation of internally oxidized Al2O3/Cu composites. The investigation revealed that dispersive alumina can obstruct dislocation sliding and define the subgrain size the...This work concerns with the high temperature deformation of internally oxidized Al2O3/Cu composites. The investigation revealed that dispersive alumina can obstruct dislocation sliding and define the subgrain size thereby improve significantly the strength of the materials at high temperature. The sliding of dislocations is a main deformation mechanism in the given temperature range. The sliding of grain boundary and diffusive creep play important roles at high temperature and low strain rate. The dispersoids can raise the recrystallization temperature to higher than 1223 K. Dynamic recovery is a main softening way under the experimental conditions. Higher deformation rate and lower deformation temperature imply a higher flow stress.展开更多
ZA22/Al2O3 composites were prepared by means of squeeze casting process. The effects of Ce on the ultimate tensile strength (UTS), impact toughness, and hardness of the composites were studied. The results show that b...ZA22/Al2O3 composites were prepared by means of squeeze casting process. The effects of Ce on the ultimate tensile strength (UTS), impact toughness, and hardness of the composites were studied. The results show that both the UTS and the hardness are improved and the impact toughness is decreased with the increase of the volume fraction of fibers (Vf). After Ce is added ,UTS (Vf>15%) and the hardness are improved at room temperature because of the modification of Ce, but the impact toughness and UTS at elevated temperature are lowered.The filtered action of the fiber preform results in that the influence of the amount of Ce added from 0. 1 wt% to 0. 5 wt% on the mechanical properties of the composites can be ignored.展开更多
A series of polymer- supported Pd -Fe2O3 composite catalysts were prepared and their hydrogenation property mas investigated. It was found that the above catalysts have good catalytic hydrogenation activity for carbon...A series of polymer- supported Pd -Fe2O3 composite catalysts were prepared and their hydrogenation property mas investigated. It was found that the above catalysts have good catalytic hydrogenation activity for carbon - carbon double bonds systems and reusability. Furthermore, XPS and IR spectra shouted that active component in the composite catalysts is atomic Pd(0). An addition of a small amount of Fe2O3 has a promotive action upon hydrogenation activity of the catalysts, which indicated that there are some strong interactions (electron transfer) between Pd(0) and Fe(Ⅲ) species. Based on these results, a possible catalytic hydrogenation mechanism was also suggested.展开更多
YBaCuO(YBCO) is one of thesuperconducting oxides with transition tem-perature above 90K.It has a orthorhombic crystal structrure ofa layered-perovskite-type with oxygen defi-ciency.This kind of material shows differen...YBaCuO(YBCO) is one of thesuperconducting oxides with transition tem-perature above 90K.It has a orthorhombic crystal structrure ofa layered-perovskite-type with oxygen defi-ciency.This kind of material shows differentdegree of preferred orientation after the展开更多
基金National Natural Science Foundation of China (50432020)Henan Innovation Project for University Prominent Re- search Talents (2007KYCX008)+3 种基金Henan Education Department Science and Technology Project (2007430004)Henan Plan Project for College Youth Backbone TeacherHenan University of Science and Technology Major Pre-research Foundation (2005ZD003)Henan University of Science and Technology Personnel Scientific Research Foundation (of023)
文摘Two Al2O3/Cu composites containing 0.24 wt.% Al2O3 and 0.60 wt.% Al2O3 separately are prepared by internal oxidation. Effects of sliding speed and pressure on the frictional characteristics of the composites and copper against brass are investigated and compared. The changes in morphology of the sliding surface and subsurface are examined with scanning electron microscope （SEM） and energy dispersive X-ray spectrum （EDS）. The results show that the wear resistance of the Al2O3/Cu composites is superior to that of copper under the same conditions, Under a given electrical current, the wear rate of Al2O3/Cu composites decreases as the Al2O3-content increases, However, the wear rates of the Al2O3/Cu composites and copper increase as the sliding speed and pressure increase under dry sliding condition. The main wear mechanisms for Al2O3/Cu composites are of abrasion and adhesion; for copper, it is adhesion, although wear by oxidation and electrical erosion can also be observed as the speed and pressure rise.
基金the National Natural Science Foundation of China(Grant No.50075019) the Visiting Scholar Foundation of Key Lab.in University of China
文摘Microstructure and interracial reactions of Al2O3 joints brazed with Al2O3-particulate-contained composite Ag-Cu-Ti filler material were researched by scanning electron microscopy （SEM）, electron probe microscopy analysis （EPMA）, energy dispersive spectroscopy （EDS） and X-ray diffraction （XRD）. The interracial reaction layer thickness of joints brazed with conventional active filler metal and active composite filler materials with different volume fraction of Al2O3 particulate was also studied. The experimental results indicated although there were Al2O3 particulates added into active filler metals, the time dependence of interracial layer growth of joints brazed with active composite filler material is t^1/2 as described by Fickian law as the joints brazed with conventional active filler metal.
文摘Cs0.35V2O5 was successfully synthesized as cathode material for lithium secondary battery by the rheological phase reaction method from Cs2CO3 and NH4VO3. The Cs0.35V2O5/Cu composite material was prepared by the displacement reaction in CuSO4 solution using zinc powder as a reductant. The structure and electrochemical property of the so-prepared powders were characterized by means of XRD （powder X-ray diffraction） and the galvanostatic discharge-charge techniques. The results show that the electrochemical property of Cs0.35V2O5/Cu composite material is significantly improved compared to the bulk Cs0.35V2O5 material. The Cs0.35V2O5/Cu composite material exhibits the first discharge capacity as high as 164.3 mAh.g -1 in the range of 4.2-1.8V at a current rate of 10 mA.g-1 and remains at a stable discharge capacity of about 110 mAh.g-1 within 40 cycles.
文摘The preferred internal oxidation of aluminum in Cu Al alloy was used to obtain in situ Al 2O 3/Cu composites. The reinforcement particles were mainly γ Al 2O 3, some θ Al 2O 3 and a little α Al 2O 3. Thermodynamics analyses show that the chemical reactions are 3Cu 2O+2Al=6Cu+Al 2O 3 or 3CuO+2Al=3Cu+Al 2O 3. A related equilibrium diagram was drawn. The experiments and investigation show that the formation rate of Al 2O 3 was controlled by the diffusion of oxygen in matrix.
基金Henan Innovation Project for University Prominent Research Talents (2007KYCX008)Henan Major Science and Technol-ogy Project (0523021500)+1 种基金Henan University of Science and Technology Major Pre-research Foundation (2005ZD003)Henan University of Science and Technology Personnel Scientific Research Foundation
文摘Alumina dispersion strengthened copper composite （nano-Al2O3/Cu composite） was recently emerged as a kind of potentially viable and attractive engineering material for applications requiring high strength, high thermal and electrical conductivities and resistance to softening at elevated temperatures. The nano-Al2O3/Cu composite was produced by internal oxidation. The microstructures of the composite were analyzed by the TEM and its hot deformation behavior was investigated by means of continuous compression tests performed on a Gleeble 1500 thermo-simulator. Making use of the modified algorithm-Levenberg-Marquardt （L-M） algorithm BP neural network, a model for predicting the flow stresses during hot deformation was set up on the base of the experimental data. Results show that the microstructures of the composite are characterized by uniform distribution of nano-Al2O3 particles in Cu-matrix. The sliding of dislocations is the main deformation mechanism. The dynamic recovery is the main softening mode with the flow stress decreasing gently from 500℃ to 850 ~C. The recrystallization of Cu-matrix can be retarded late into as high as 850 ℃, when it happens only partially. The well-trained BP neural network model can accurately describe the influence of the temperature, strain rate, and true strain on the flow stresses, therefore, it can precisely predict the flow stresses of the composite under given deforming conditions and provide a new way to optimize hot deforming process parameters.
基金Project(50702012)supported by the National Natural Science Foundation of ChinaProject(20060145030)supported by Doctoral Foundation of Chinese Education Ministry
文摘Silver as a highly conductive metal is usually doped in YBa2Cu3O7-x superconductor bulks to improve critical current density of YBa2Cu3O7-x superconductor.The valuable metal elements silver,yttrium,barium and copper in waste YBa2Cu3O7-x/Ag composite superconductor bulks were recovered,respectively.Silver was recovered with process at first,the waste was dissolved by nitric acid and silver chloride was precipitated by adding chloride acid,then silver pig was obtained by melting silver chloride together with sodium carbonate at 1 000℃.The effective factors on recovery ratio and purity of silver were studied.The chemical analysis proves that the purity of silver ingot is 95.86%.The recovery ratio of silver is calculated to be 92.56%.The loss of silver may be due to the loss of silver chloride during filtering and the volatilization of silver when silver chloride and sodium carbonate are smelted at high temperature.For other three metal elements,Y3 +,Ba 2+and Cu 2+,in the surplus waste liquid after recovering silver, they were separated with the sequence of barium,copper and then yttrium step by step.First,sulfate acid was used to precipitate barium sulfate.Then,sodium sulfide was added to the surplus solution so that copper could be separated as copper sulfide.During this separation procedure,it was important to control the pH value to be 1-2.After that,oxalic acid was added into the surplus solution to obtain yttrium oxalate.Finally,yttrium oxide was formed by burning yttrium oxalate.The XRD results indicate that the final products are all single-phase compounds as BaSO4,CuS and Y2O3,respectively.
基金The work was financiaIly supported hy the NaturalScience Foundation of Hebei Province (No.94087) alld Pd-ucation Conlmittee of
文摘This work concerns with the high temperature deformation of internally oxidized Al2O3/Cu composites. The investigation revealed that dispersive alumina can obstruct dislocation sliding and define the subgrain size thereby improve significantly the strength of the materials at high temperature. The sliding of dislocations is a main deformation mechanism in the given temperature range. The sliding of grain boundary and diffusive creep play important roles at high temperature and low strain rate. The dispersoids can raise the recrystallization temperature to higher than 1223 K. Dynamic recovery is a main softening way under the experimental conditions. Higher deformation rate and lower deformation temperature imply a higher flow stress.
文摘ZA22/Al2O3 composites were prepared by means of squeeze casting process. The effects of Ce on the ultimate tensile strength (UTS), impact toughness, and hardness of the composites were studied. The results show that both the UTS and the hardness are improved and the impact toughness is decreased with the increase of the volume fraction of fibers (Vf). After Ce is added ,UTS (Vf>15%) and the hardness are improved at room temperature because of the modification of Ce, but the impact toughness and UTS at elevated temperature are lowered.The filtered action of the fiber preform results in that the influence of the amount of Ce added from 0. 1 wt% to 0. 5 wt% on the mechanical properties of the composites can be ignored.
文摘A series of polymer- supported Pd -Fe2O3 composite catalysts were prepared and their hydrogenation property mas investigated. It was found that the above catalysts have good catalytic hydrogenation activity for carbon - carbon double bonds systems and reusability. Furthermore, XPS and IR spectra shouted that active component in the composite catalysts is atomic Pd(0). An addition of a small amount of Fe2O3 has a promotive action upon hydrogenation activity of the catalysts, which indicated that there are some strong interactions (electron transfer) between Pd(0) and Fe(Ⅲ) species. Based on these results, a possible catalytic hydrogenation mechanism was also suggested.
文摘YBaCuO(YBCO) is one of thesuperconducting oxides with transition tem-perature above 90K.It has a orthorhombic crystal structrure ofa layered-perovskite-type with oxygen defi-ciency.This kind of material shows differentdegree of preferred orientation after the