Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub&...Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> was determined by nano-particle size analyzer, and the effects of nano-α-Al<sub>2</sub>O<sub>3</sub> content, ethanol-aqueous solution ratio and KH560 dosage on the dispersion and particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> were investigated. The material structure before and after modification was determined by Fourier transform infrared spectroscopy (FTIR). Aqueous polyurethane resin and inorganic components are combined with modified nano-α-Al<sub>2</sub>O<sub>3</sub> dispersion to form chromium-free passivation solution. The solution is coated on the galvanized sheet, the adhesion and surface hardness are tested, the bonding strength of the coating and the surface hardness of the substrate are discussed. The corrosion resistance and surface morphology of the matrix were investigated by electrochemical test, neutral salt spray test and scanning electron microscope test. The chromium-free passivation film formed after the modification of nano-α-Al<sub>2</sub>O<sub>3</sub> increases the surface hardness of galvanized sheet by about 85%. The corrosion resistance of the film is better than that of a single polyurethane film. The results show that the surface hardness and corrosion resistance of polyurethane resin composite passivation film are significantly improved by the introduction of nano-α-Al<sub>2</sub>O<sub>3</sub>.展开更多
YBa2Cu3O7-x （YBCO） superconducting film was fabricated on {001} LaAlO3 （LAO） substrate by pulse laser deposition （PLD）, and its microstructure was examined by high resolution X-ray diffraction technology （HRXRD...YBa2Cu3O7-x （YBCO） superconducting film was fabricated on {001} LaAlO3 （LAO） substrate by pulse laser deposition （PLD）, and its microstructure was examined by high resolution X-ray diffraction technology （HRXRD）, such as pole figure, rocking curve, reciprocal space mapping. The results show that the YBCO crystalline alignment is almost {001}YBCO//{001}LAO, 100YBCO//100LAO besides 2% {001}YBCO//{001}LAO, 110YBCO//100LAO. The out-plane alignment of YBCO is some spreading （the breadth is 0.75°）. There are 90°±0.65°110 twin domains in the film, which is caused by the high local stress and stress difference between 100 and 010 during the tetragonal to orthorhombic phase transition.展开更多
文摘Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> was determined by nano-particle size analyzer, and the effects of nano-α-Al<sub>2</sub>O<sub>3</sub> content, ethanol-aqueous solution ratio and KH560 dosage on the dispersion and particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> were investigated. The material structure before and after modification was determined by Fourier transform infrared spectroscopy (FTIR). Aqueous polyurethane resin and inorganic components are combined with modified nano-α-Al<sub>2</sub>O<sub>3</sub> dispersion to form chromium-free passivation solution. The solution is coated on the galvanized sheet, the adhesion and surface hardness are tested, the bonding strength of the coating and the surface hardness of the substrate are discussed. The corrosion resistance and surface morphology of the matrix were investigated by electrochemical test, neutral salt spray test and scanning electron microscope test. The chromium-free passivation film formed after the modification of nano-α-Al<sub>2</sub>O<sub>3</sub> increases the surface hardness of galvanized sheet by about 85%. The corrosion resistance of the film is better than that of a single polyurethane film. The results show that the surface hardness and corrosion resistance of polyurethane resin composite passivation film are significantly improved by the introduction of nano-α-Al<sub>2</sub>O<sub>3</sub>.
基金Project (50972019) supported by the National Natural Science Foundation of ChinaProject (2011CBA00105) supported by the National Basic Research Program of China
文摘YBa2Cu3O7-x （YBCO） superconducting film was fabricated on {001} LaAlO3 （LAO） substrate by pulse laser deposition （PLD）, and its microstructure was examined by high resolution X-ray diffraction technology （HRXRD）, such as pole figure, rocking curve, reciprocal space mapping. The results show that the YBCO crystalline alignment is almost {001}YBCO//{001}LAO, 100YBCO//100LAO besides 2% {001}YBCO//{001}LAO, 110YBCO//100LAO. The out-plane alignment of YBCO is some spreading （the breadth is 0.75°）. There are 90°±0.65°110 twin domains in the film, which is caused by the high local stress and stress difference between 100 and 010 during the tetragonal to orthorhombic phase transition.