A novel coprecipitation-reduction process has been proposed for preparing highly selective Cu/ZnO/Al 2O 3 catalysts for methanol synthesis from CO 2 hydrogenation. Compared to the catalysts prepared by the conventiona...A novel coprecipitation-reduction process has been proposed for preparing highly selective Cu/ZnO/Al 2O 3 catalysts for methanol synthesis from CO 2 hydrogenation. Compared to the catalysts prepared by the conventional method, the new catalysts prepared via the new method exhibit much higher BET surface area and pore size, much smaller crystallite size and higher catalytic activity and selectivity in CO 2 hydrogenation to methanol. It is also found that the molar ratio of Cu + to Cu 0 on the surface of the catalyst obtained by coprecipitation-reduction is much higher than that on the reduced catalyst obtained by the conventional method, which could be crucial for its high activity and selectivity for catalytic hydrogenation of CO 2 to methanol.展开更多
Two Al2O3/Cu composites containing 0.24 wt.% Al2O3 and 0.60 wt.% Al2O3 separately are prepared by internal oxidation. Effects of sliding speed and pressure on the frictional characteristics of the composites and coppe...Two Al2O3/Cu composites containing 0.24 wt.% Al2O3 and 0.60 wt.% Al2O3 separately are prepared by internal oxidation. Effects of sliding speed and pressure on the frictional characteristics of the composites and copper against brass are investigated and compared. The changes in morphology of the sliding surface and subsurface are examined with scanning electron microscope （SEM） and energy dispersive X-ray spectrum （EDS）. The results show that the wear resistance of the Al2O3/Cu composites is superior to that of copper under the same conditions, Under a given electrical current, the wear rate of Al2O3/Cu composites decreases as the Al2O3-content increases, However, the wear rates of the Al2O3/Cu composites and copper increase as the sliding speed and pressure increase under dry sliding condition. The main wear mechanisms for Al2O3/Cu composites are of abrasion and adhesion; for copper, it is adhesion, although wear by oxidation and electrical erosion can also be observed as the speed and pressure rise.展开更多
Hydrogen production by catalytic steam reforming of methanol over a series of coprecipitated Cu/ZnO/Al2O3 catalysts under atmospheric pressure in a microreactor has been studied Effects of catalyst composition...Hydrogen production by catalytic steam reforming of methanol over a series of coprecipitated Cu/ZnO/Al2O3 catalysts under atmospheric pressure in a microreactor has been studied Effects of catalyst composition, reaction temperature and activation conditions on the catalytic activity have been investigated Crystal phases of catalysts were analyzed by XRD The results showed that Cu/ZnO/Al2O3 catalysts displayed high activity and selectivity for hydrogen and stability The optimized molar ratio is Cu/Zn=10, a maximum methanol conversion of 994?mol%, hydrogen selectivity of 999?mol% and CO molar fraction of 0007% were obtained in the steam reforming reaction with the catalyst containing 45?mol% copper XRD results showed that the diffraction peaks of CuO in the catalyst were clearly lower and broaden It indicated that high dispersion of small copper crystallites on the catalyst surface was formed under the calcination conditions It is suggested that the good performance of Cu/ZnO/Al2O3 catalysts partly resulted from well dispersed展开更多
文摘A novel coprecipitation-reduction process has been proposed for preparing highly selective Cu/ZnO/Al 2O 3 catalysts for methanol synthesis from CO 2 hydrogenation. Compared to the catalysts prepared by the conventional method, the new catalysts prepared via the new method exhibit much higher BET surface area and pore size, much smaller crystallite size and higher catalytic activity and selectivity in CO 2 hydrogenation to methanol. It is also found that the molar ratio of Cu + to Cu 0 on the surface of the catalyst obtained by coprecipitation-reduction is much higher than that on the reduced catalyst obtained by the conventional method, which could be crucial for its high activity and selectivity for catalytic hydrogenation of CO 2 to methanol.
基金National Natural Science Foundation of China (50432020)Henan Innovation Project for University Prominent Re- search Talents (2007KYCX008)+3 种基金Henan Education Department Science and Technology Project (2007430004)Henan Plan Project for College Youth Backbone TeacherHenan University of Science and Technology Major Pre-research Foundation (2005ZD003)Henan University of Science and Technology Personnel Scientific Research Foundation (of023)
文摘Two Al2O3/Cu composites containing 0.24 wt.% Al2O3 and 0.60 wt.% Al2O3 separately are prepared by internal oxidation. Effects of sliding speed and pressure on the frictional characteristics of the composites and copper against brass are investigated and compared. The changes in morphology of the sliding surface and subsurface are examined with scanning electron microscope （SEM） and energy dispersive X-ray spectrum （EDS）. The results show that the wear resistance of the Al2O3/Cu composites is superior to that of copper under the same conditions, Under a given electrical current, the wear rate of Al2O3/Cu composites decreases as the Al2O3-content increases, However, the wear rates of the Al2O3/Cu composites and copper increase as the sliding speed and pressure increase under dry sliding condition. The main wear mechanisms for Al2O3/Cu composites are of abrasion and adhesion; for copper, it is adhesion, although wear by oxidation and electrical erosion can also be observed as the speed and pressure rise.
文摘Hydrogen production by catalytic steam reforming of methanol over a series of coprecipitated Cu/ZnO/Al2O3 catalysts under atmospheric pressure in a microreactor has been studied Effects of catalyst composition, reaction temperature and activation conditions on the catalytic activity have been investigated Crystal phases of catalysts were analyzed by XRD The results showed that Cu/ZnO/Al2O3 catalysts displayed high activity and selectivity for hydrogen and stability The optimized molar ratio is Cu/Zn=10, a maximum methanol conversion of 994?mol%, hydrogen selectivity of 999?mol% and CO molar fraction of 0007% were obtained in the steam reforming reaction with the catalyst containing 45?mol% copper XRD results showed that the diffraction peaks of CuO in the catalyst were clearly lower and broaden It indicated that high dispersion of small copper crystallites on the catalyst surface was formed under the calcination conditions It is suggested that the good performance of Cu/ZnO/Al2O3 catalysts partly resulted from well dispersed