Cu based composites reinforced by 0%~25% (volume fraction) carbon nanotubes were prepared.The fracture behaviors and the rolling properties of the composites and the effects of the volume fraction of the carbon nanot...Cu based composites reinforced by 0%~25% (volume fraction) carbon nanotubes were prepared.The fracture behaviors and the rolling properties of the composites and the effects of the volume fraction of the carbon nanotubes were studied.The experimental results show that the fracture toughness of the composites is related to the pulling out and bridging of the carbon nanotubes in the fracture process.With the volume fraction of the carbon nanotubes increasing, the Vicker’s hardness and the compactness of the composites increase first and then decrease. The peaks of the hardness and the compactness occur at 12%~15% of volume fraction of carbon nanotubes.Some proper ratio of rolling reduction benefits to the comprehensive mechanical properties of the composites.展开更多
Layered composites have attracted considerable interest in the recent literature on metal composites. Their mechanical properties depend on the quality of the bonding provided by the intermediate layers. In this study...Layered composites have attracted considerable interest in the recent literature on metal composites. Their mechanical properties depend on the quality of the bonding provided by the intermediate layers. In this study, we analyzed the mechanical properties and bond strengths provided by the nickel layer with respect to its thickness and nature(either powder or coating). The results suggest that bond strength decreases with an increase in the content of nickel powder. At 0.3 vol% of nickel coating, we found the nature of nickel to be less efficient in terms of bond strength. A different picture arose when the content of nickel was increased and the bond strength increased in nickel coated samples. In addition, the results demonstrate that mechanical properties such as bend strength are strongly dependent on bond strength.展开更多
TiC-TiB2-Cu composites were produced by self-propagating high-temperature synthesis combined with pseudo hot isostatic pressing using Ti, B4C and Cu powders. The microstructure and mechanical properties of the composi...TiC-TiB2-Cu composites were produced by self-propagating high-temperature synthesis combined with pseudo hot isostatic pressing using Ti, B4C and Cu powders. The microstructure and mechanical properties of the composites were investigated. The X-ray diffraction (XRD) and scanning electron microscopy (SEM) results showed that the final products were only TiC, TiB2 and Cu phases. The clubbed TiB2 grains and spheroidal or irregular TiC grains were found in the microstructure of synthesized products. The reaction temperature and grain size of TiB2 and TiC particles decreased with increasing Cu content. The introduction of Cu into the composites resulted in a drastic increase in the relative density and flexual strength, and the maximum values were obtained with the addition of 20 wt pct, while the fracture toughness was the best when Cu content was 40 wt pct.展开更多
High reinforcement content SiCp/Cu composites (φp=50%, 55% and 60%) for electronic packaging applications were fabricated by patent cost-effective squeeze-casting technology. The composites appear to be free of pores...High reinforcement content SiCp/Cu composites (φp=50%, 55% and 60%) for electronic packaging applications were fabricated by patent cost-effective squeeze-casting technology. The composites appear to be free of pores, and the SiC particles are distribute uniformly in the composites. The mean linear coefficients of thermal expansion (CTEs, 20-100 ℃ ) of as-cast SiCp/Cu composites range from 8.8×10-6 ℃-1 to 9.9×10-6 ℃-1 and decrease with the increase of SiC content. The experimental CTEs of as-cast SiCp/Cu composites agree well with the predicted values based on Kerner model. The CTEs of composites reduce after annealing treatment due to the fact that the internal stress of the composite is released. The Brinell hardness increases from 272.3 to 313.2, and the modulus increases from 186 GPa to 210 GPa for the corresponding composites. The bending strength is larger than 374 MPa, but no obvious trend between bending strength and SiCp content is observed.展开更多
The preferred internal oxidation of aluminum in Cu Al alloy was used to obtain in situ Al 2O 3/Cu composites. The reinforcement particles were mainly γ Al 2O 3, some θ Al 2O 3 and a little α Al 2O 3. Thermodynamics...The preferred internal oxidation of aluminum in Cu Al alloy was used to obtain in situ Al 2O 3/Cu composites. The reinforcement particles were mainly γ Al 2O 3, some θ Al 2O 3 and a little α Al 2O 3. Thermodynamics analyses show that the chemical reactions are 3Cu 2O+2Al=6Cu+Al 2O 3 or 3CuO+2Al=3Cu+Al 2O 3. A related equilibrium diagram was drawn. The experiments and investigation show that the formation rate of Al 2O 3 was controlled by the diffusion of oxygen in matrix.展开更多
A novel technique for preparing functionally gradient electrically conductive polymeric composites was developed by using of solution casting technique on the principle of Stokes' law. Acrylonitrile- butadiene-styren...A novel technique for preparing functionally gradient electrically conductive polymeric composites was developed by using of solution casting technique on the principle of Stokes' law. Acrylonitrile- butadiene-styrene/Cu (ABS/Cu) gradient polymeric composites were prepared successfully using this technique. The gradient structures, electrically conductive performance and mechanical properties of the ABS/Cu composites were investigated. Optical microscope observation shows that the gradient distribution of Cu particles in ABS matrix was formed along their thickness-direction. The electrically conductive testing results indicate that the order of magnitude of surface resistivity was kept in 10^15 Ω at ABS rich side, while that declined to 10^5 Ω at Cu particles rich side, and the percolation threshold was in the range of 2.82 vo1%- 4.74 vol% Cu content at Cu particles rich side. Mechanical test shows that the tensile strength reduced insignificantly as the content of Cu increases owing to the gradient distribution.展开更多
We conducted molecular dynamics (MD) simulations of tension and compression along the <112> direction and MD simulations of compression along the <110> and <111> directions on nanolaminated graphene/...We conducted molecular dynamics (MD) simulations of tension and compression along the <112> direction and MD simulations of compression along the <110> and <111> directions on nanolaminated graphene/Cu (NGCu) composites to investigate the effects of the incorporated graphene and the deformation mechanisms related to the loading direction. The deformation behavior and the defect structures were found to be strongly dependent on the loading conditions. An asymmetric tension-compression deformation behavior was thus found in graphene/Cu nanolaminates under the <112> loading, which was dominated by stacking faults and deformation twins formed by dislocation slide under tension and compression, respectively. High density and ordered nanotwins were formed at the graphene/Cu interfaces. Two different formation mechanisms of the twins were found under the <112> compression, and the nucleated twins were easy to be thickened with the assistance of the graphene wrinkles. Multiple twins were formed under the <110> compression by the dislocation cross-slip. This study provides a way to introduce graphene reinforcement and twin boundary to Cu matrix composites and design nanotwinned graphene/Cu composites with excellent mechanical performance.展开更多
In order to improve wear resistance and decrease the cost, carbon and carbon nanotubes reinforced copper matrix composites were fabricated by the power metallurgy method. The effects of carbon (carbon and carbon nano...In order to improve wear resistance and decrease the cost, carbon and carbon nanotubes reinforced copper matrix composites were fabricated by the power metallurgy method. The effects of carbon (carbon and carbon nanotubes) volume fraction and applied load on the friction coefficient and wear rate under dry sliding of the composites were investigated at room temperature. By scanning electron microscopy (SEM), the worn surfaces and debris were observed, and wear mechanism was also analyzed and discussed. The experimental wear process consists of the run-in, steady wear and severe wear process with the increasing of sliding distance. Both the friction coefficient and wear rate of the composites first decrease and then increase with the increasing of carbon volume fraction. The minimum friction coefficient and wear rate are obtained when carbon is 4.0vo1%. The wear mechanisms of the composites change from the adhesive wear and delamination wear to abrasive wear with the increasing of carbon volume fraction.展开更多
The WC-10%Co particulate reinforced Cu matrix composite material with a WC-Co∶Cu mass ratio of 20∶80 was successfully fabricated by selective laser sintering(SLS) process. The following optimal processing parameters...The WC-10%Co particulate reinforced Cu matrix composite material with a WC-Co∶Cu mass ratio of 20∶80 was successfully fabricated by selective laser sintering(SLS) process. The following optimal processing parameters were used: laser power of 700 W, scan speed of 0.06 m/s, scan line spacing of 0.15 mm, and powder layer thickness of 0.3 mm. The microstructure, composition, and phase of the laser processed material were investigated by scanning electron microscopy(SEM), X-ray diffraction(XRD), and energy dispersive X-ray(EDX) spectroscopy. The results show that the bonding mechanism of this process is liquid phase sintering. The Cu and Co act as the binder phase, while the WC acts as the reinforcing phase. The non-equilibrium effects induced by laser melting, such as high degrees of undercooling and high solidification rate, result in the formation of a metastable phase CoC0.25. The WC reinforcing particulates typically have three kinds of morphology. They are agglomerated and undissolved, incompletely separated and partially dissolved, separated and dissolved, which indicates that particle rearrangement acts as the dominant sintering mechanism for the larger WC, while dissolution-precipitation prevails for the smaller WC particles. Microhardness tester was used to determine the Vickers hardness across the cross-section of the laser sintered sample, with the average value being HV0.1268.5. However, the hardness varied considerably, which might be attributed to the WC segregation and the high solidification rate experienced by the molten pool.展开更多
Diamond-copper composites were prepared by powder metallurgy,in which the diamond particles were pre-coated by magnetic sputtering with copper alloy containing a small amount of carbide forming elements(including B,Cr...Diamond-copper composites were prepared by powder metallurgy,in which the diamond particles were pre-coated by magnetic sputtering with copper alloy containing a small amount of carbide forming elements(including B,Cr,Ti,and Si).The influence of the carbide forming element additives on the microstructure and thermal conductivity of diamond composites was investigated.It is found that the composites fabricated with Cu-0.5B coated diamond particles has a relatively higher density and its thermal conductivity approaches 300 W/(m·K).Addition of 0.5%B improves the interfacial bonding and decreases thermal boundary resistance between diamond and Cu,while addition of 1%Cr makes the interfacial layer break away from diamond surface.The actual interfacial thermal conductivity of the composites with Cu-0.5B alloy coated on diamond is much higher than that of the Cu-1Cr layer,which suggests that the intrinsic thermal conductivity of the interfacial layer is an important factor for improving the thermal conductivity of the diamond composites.展开更多
The effects of alloying elements on the mechanical properties as well as electrical conductivity in Cu-15%Cr(mass fraction) in-situ composites were systematically studied and high strength and high electrical conducti...The effects of alloying elements on the mechanical properties as well as electrical conductivity in Cu-15%Cr(mass fraction) in-situ composites were systematically studied and high strength and high electrical conductive Cu base in-situ composites have been developed. The best combination is the addition of 0.1% to 0.2% Zr, Ti, or Sn in Cu-15%Cr in-situ composite, thermomechanical treatment to refine the microstructure and optimizing the precipitation of second phase. The strength is controlled by high density of dislocations in the Cu matrix, the lamellar spacing of the second phase, and the fine Cr precipitates. The aging treatment to reduce solute atoms has a beneficial effect on the increase of electrical conductivity. The addition of Zr, or Ti of about 0.15% to 0.2% promotes the precipitation of Cr particles.展开更多
Sessile drop technique was used to investigate the influence of Ti on the wetting behaviour of copper alloy on SiC substrate. A low contact angle of 15- for Cu alloy on SiC substrate is obtained at the temperature of ...Sessile drop technique was used to investigate the influence of Ti on the wetting behaviour of copper alloy on SiC substrate. A low contact angle of 15- for Cu alloy on SiC substrate is obtained at the temperature of 1 100 ℃. The interfacial energy is lowered by the segregation of Ti and the formation of reaction product TiC, resulting in the significant enhancement of wettability. Ti is found to almost completely segregate to Cu/SiC interface. This agrees well with a coverage of 99.8%Ti at the Cu/SiC interface predicted from a simple model based on Gibbs adsorption isotherm. SiCp/Cu composites are produced by pressureless infiltration of copper alloy into Ti-activated SiC preform. The volume fraction of SiC reaches 57%. The densification achieves 97.5%. The bending strength varies from 150 MPa to 250 MPa and increases with decreasing particle size.展开更多
文摘Cu based composites reinforced by 0%~25% (volume fraction) carbon nanotubes were prepared.The fracture behaviors and the rolling properties of the composites and the effects of the volume fraction of the carbon nanotubes were studied.The experimental results show that the fracture toughness of the composites is related to the pulling out and bridging of the carbon nanotubes in the fracture process.With the volume fraction of the carbon nanotubes increasing, the Vicker’s hardness and the compactness of the composites increase first and then decrease. The peaks of the hardness and the compactness occur at 12%~15% of volume fraction of carbon nanotubes.Some proper ratio of rolling reduction benefits to the comprehensive mechanical properties of the composites.
文摘Layered composites have attracted considerable interest in the recent literature on metal composites. Their mechanical properties depend on the quality of the bonding provided by the intermediate layers. In this study, we analyzed the mechanical properties and bond strengths provided by the nickel layer with respect to its thickness and nature(either powder or coating). The results suggest that bond strength decreases with an increase in the content of nickel powder. At 0.3 vol% of nickel coating, we found the nature of nickel to be less efficient in terms of bond strength. A different picture arose when the content of nickel was increased and the bond strength increased in nickel coated samples. In addition, the results demonstrate that mechanical properties such as bend strength are strongly dependent on bond strength.
基金The work was supported by the Foundation of Aerospace Innovation Fund and the National Natural Science Foundation of China(No.90505015)the Foundation of National Key Laboratory for Remanufacturing.
文摘TiC-TiB2-Cu composites were produced by self-propagating high-temperature synthesis combined with pseudo hot isostatic pressing using Ti, B4C and Cu powders. The microstructure and mechanical properties of the composites were investigated. The X-ray diffraction (XRD) and scanning electron microscopy (SEM) results showed that the final products were only TiC, TiB2 and Cu phases. The clubbed TiB2 grains and spheroidal or irregular TiC grains were found in the microstructure of synthesized products. The reaction temperature and grain size of TiB2 and TiC particles decreased with increasing Cu content. The introduction of Cu into the composites resulted in a drastic increase in the relative density and flexual strength, and the maximum values were obtained with the addition of 20 wt pct, while the fracture toughness was the best when Cu content was 40 wt pct.
基金Foundation item: Project(20080430895) supported by China Postdoctoral Science FoundationProject(2003AA5CG041) supported by the High-tech Research and Development Program of Harbin City, China
文摘High reinforcement content SiCp/Cu composites (φp=50%, 55% and 60%) for electronic packaging applications were fabricated by patent cost-effective squeeze-casting technology. The composites appear to be free of pores, and the SiC particles are distribute uniformly in the composites. The mean linear coefficients of thermal expansion (CTEs, 20-100 ℃ ) of as-cast SiCp/Cu composites range from 8.8×10-6 ℃-1 to 9.9×10-6 ℃-1 and decrease with the increase of SiC content. The experimental CTEs of as-cast SiCp/Cu composites agree well with the predicted values based on Kerner model. The CTEs of composites reduce after annealing treatment due to the fact that the internal stress of the composite is released. The Brinell hardness increases from 272.3 to 313.2, and the modulus increases from 186 GPa to 210 GPa for the corresponding composites. The bending strength is larger than 374 MPa, but no obvious trend between bending strength and SiCp content is observed.
文摘The preferred internal oxidation of aluminum in Cu Al alloy was used to obtain in situ Al 2O 3/Cu composites. The reinforcement particles were mainly γ Al 2O 3, some θ Al 2O 3 and a little α Al 2O 3. Thermodynamics analyses show that the chemical reactions are 3Cu 2O+2Al=6Cu+Al 2O 3 or 3CuO+2Al=3Cu+Al 2O 3. A related equilibrium diagram was drawn. The experiments and investigation show that the formation rate of Al 2O 3 was controlled by the diffusion of oxygen in matrix.
基金Funded by the National Natural Science Foundation of China(No.21274007)the Beijing Natural Science Foundation+1 种基金the Key Scientific Project of Beijing Municipal Education Commission(No.KZ201110011014)the Science and Technology Innovation Platform of Beijing Municipal Education Commission(No.PXM2012-014213-000025)
文摘A novel technique for preparing functionally gradient electrically conductive polymeric composites was developed by using of solution casting technique on the principle of Stokes' law. Acrylonitrile- butadiene-styrene/Cu (ABS/Cu) gradient polymeric composites were prepared successfully using this technique. The gradient structures, electrically conductive performance and mechanical properties of the ABS/Cu composites were investigated. Optical microscope observation shows that the gradient distribution of Cu particles in ABS matrix was formed along their thickness-direction. The electrically conductive testing results indicate that the order of magnitude of surface resistivity was kept in 10^15 Ω at ABS rich side, while that declined to 10^5 Ω at Cu particles rich side, and the percolation threshold was in the range of 2.82 vo1%- 4.74 vol% Cu content at Cu particles rich side. Mechanical test shows that the tensile strength reduced insignificantly as the content of Cu increases owing to the gradient distribution.
基金financial support from National Natural Science Foundation of China (grant nos. U1864208, 51603022, 11632004, 11802045)Fundamental Research Funds for the Central Universities (grant no. 106112017CDJXSYY0001)+3 种基金the Key Program for International Science and Technology Cooperation Projects of Ministry of Science and Technology of China (grant no. 2016YFE0125900)State Key Laboratory of Advanced Design and Manufacturing for Vehicle Body (grant no. 31715007)the Postdoctoral Program for Innovative Talents of Chongqing (grant no. CQBX201804)the China Postdoctoral Science Foundation funded project (grant no. 2018M631058)
文摘We conducted molecular dynamics (MD) simulations of tension and compression along the <112> direction and MD simulations of compression along the <110> and <111> directions on nanolaminated graphene/Cu (NGCu) composites to investigate the effects of the incorporated graphene and the deformation mechanisms related to the loading direction. The deformation behavior and the defect structures were found to be strongly dependent on the loading conditions. An asymmetric tension-compression deformation behavior was thus found in graphene/Cu nanolaminates under the <112> loading, which was dominated by stacking faults and deformation twins formed by dislocation slide under tension and compression, respectively. High density and ordered nanotwins were formed at the graphene/Cu interfaces. Two different formation mechanisms of the twins were found under the <112> compression, and the nucleated twins were easy to be thickened with the assistance of the graphene wrinkles. Multiple twins were formed under the <110> compression by the dislocation cross-slip. This study provides a way to introduce graphene reinforcement and twin boundary to Cu matrix composites and design nanotwinned graphene/Cu composites with excellent mechanical performance.
基金Funded by the National Natural Science Foundation of China (50873047)the Natural Science Foundation of Gansu Province (3ZS061-A25-039)
文摘In order to improve wear resistance and decrease the cost, carbon and carbon nanotubes reinforced copper matrix composites were fabricated by the power metallurgy method. The effects of carbon (carbon and carbon nanotubes) volume fraction and applied load on the friction coefficient and wear rate under dry sliding of the composites were investigated at room temperature. By scanning electron microscopy (SEM), the worn surfaces and debris were observed, and wear mechanism was also analyzed and discussed. The experimental wear process consists of the run-in, steady wear and severe wear process with the increasing of sliding distance. Both the friction coefficient and wear rate of the composites first decrease and then increase with the increasing of carbon volume fraction. The minimum friction coefficient and wear rate are obtained when carbon is 4.0vo1%. The wear mechanisms of the composites change from the adhesive wear and delamination wear to abrasive wear with the increasing of carbon volume fraction.
基金Project(10276017) supported by the Joint Fund of National Natural Science Foundation of China and China Academy of Engineering Physics Project(04H52061) supported by the Aeronautical Science Foundation of China Project(S0403-061) supported by the Scientific Research Innovations Foundation of Nanjing University of Aeronautics and Astronautics
文摘The WC-10%Co particulate reinforced Cu matrix composite material with a WC-Co∶Cu mass ratio of 20∶80 was successfully fabricated by selective laser sintering(SLS) process. The following optimal processing parameters were used: laser power of 700 W, scan speed of 0.06 m/s, scan line spacing of 0.15 mm, and powder layer thickness of 0.3 mm. The microstructure, composition, and phase of the laser processed material were investigated by scanning electron microscopy(SEM), X-ray diffraction(XRD), and energy dispersive X-ray(EDX) spectroscopy. The results show that the bonding mechanism of this process is liquid phase sintering. The Cu and Co act as the binder phase, while the WC acts as the reinforcing phase. The non-equilibrium effects induced by laser melting, such as high degrees of undercooling and high solidification rate, result in the formation of a metastable phase CoC0.25. The WC reinforcing particulates typically have three kinds of morphology. They are agglomerated and undissolved, incompletely separated and partially dissolved, separated and dissolved, which indicates that particle rearrangement acts as the dominant sintering mechanism for the larger WC, while dissolution-precipitation prevails for the smaller WC particles. Microhardness tester was used to determine the Vickers hardness across the cross-section of the laser sintered sample, with the average value being HV0.1268.5. However, the hardness varied considerably, which might be attributed to the WC segregation and the high solidification rate experienced by the molten pool.
基金Project(82129)supported by the Innovative Foundation of Science and Technology of General Research Institute of Nonferrous Metals,China
文摘Diamond-copper composites were prepared by powder metallurgy,in which the diamond particles were pre-coated by magnetic sputtering with copper alloy containing a small amount of carbide forming elements(including B,Cr,Ti,and Si).The influence of the carbide forming element additives on the microstructure and thermal conductivity of diamond composites was investigated.It is found that the composites fabricated with Cu-0.5B coated diamond particles has a relatively higher density and its thermal conductivity approaches 300 W/(m·K).Addition of 0.5%B improves the interfacial bonding and decreases thermal boundary resistance between diamond and Cu,while addition of 1%Cr makes the interfacial layer break away from diamond surface.The actual interfacial thermal conductivity of the composites with Cu-0.5B alloy coated on diamond is much higher than that of the Cu-1Cr layer,which suggests that the intrinsic thermal conductivity of the interfacial layer is an important factor for improving the thermal conductivity of the diamond composites.
文摘The effects of alloying elements on the mechanical properties as well as electrical conductivity in Cu-15%Cr(mass fraction) in-situ composites were systematically studied and high strength and high electrical conductive Cu base in-situ composites have been developed. The best combination is the addition of 0.1% to 0.2% Zr, Ti, or Sn in Cu-15%Cr in-situ composite, thermomechanical treatment to refine the microstructure and optimizing the precipitation of second phase. The strength is controlled by high density of dislocations in the Cu matrix, the lamellar spacing of the second phase, and the fine Cr precipitates. The aging treatment to reduce solute atoms has a beneficial effect on the increase of electrical conductivity. The addition of Zr, or Ti of about 0.15% to 0.2% promotes the precipitation of Cr particles.
基金Project(2006AA03Z557) supported by The High-tech Research and Development Program of ChinaProject(2006CB605207) supported by the National Basic Research Program of ChinaProject(I2P407) supported by MOE Program For Changjiang Scholars and Innovative Research Team in University
文摘Sessile drop technique was used to investigate the influence of Ti on the wetting behaviour of copper alloy on SiC substrate. A low contact angle of 15- for Cu alloy on SiC substrate is obtained at the temperature of 1 100 ℃. The interfacial energy is lowered by the segregation of Ti and the formation of reaction product TiC, resulting in the significant enhancement of wettability. Ti is found to almost completely segregate to Cu/SiC interface. This agrees well with a coverage of 99.8%Ti at the Cu/SiC interface predicted from a simple model based on Gibbs adsorption isotherm. SiCp/Cu composites are produced by pressureless infiltration of copper alloy into Ti-activated SiC preform. The volume fraction of SiC reaches 57%. The densification achieves 97.5%. The bending strength varies from 150 MPa to 250 MPa and increases with decreasing particle size.