A Y2O3 particle enhanced Ni/TiC composite coating was fabricated in-situ on a TC4 Ti alloy by laser surface cladding. The phase component, microstructure, composition distribution and properties of the composite layer...A Y2O3 particle enhanced Ni/TiC composite coating was fabricated in-situ on a TC4 Ti alloy by laser surface cladding. The phase component, microstructure, composition distribution and properties of the composite layer were investigated. The composite layer has graded microstructures and compositions, due to the fast melting followed by rapid solidification and cooling during laser cladding. The TiC powders are completely dissolved into the melted layer during melting and segregated as fine dendrites when solidified. The size of TiC dendrites decreases with increasing depth. Y2O3 fine particles distribute in the whole clad layer. The Y2O3 particle enhanced Ni/TiC composite layer has a quite uniform hardness along depth with a maximum value of HV1380, which is 4 times higher than the initial hardness. The wear resistance of the Ti alloy is significantly improved after laser cladding due to the high hardness of the composite coating.展开更多
Cavitation erosion behavior of as-welded Cu12Mn8Al3Fe2Ni alloy in 3.5% NaCl aqueous solution was studied bymagnetostrictive vibratory device for cavitation erosion. The results show that the cavitation erosion resista...Cavitation erosion behavior of as-welded Cu12Mn8Al3Fe2Ni alloy in 3.5% NaCl aqueous solution was studied bymagnetostrictive vibratory device for cavitation erosion. The results show that the cavitation erosion resistance ofthe as-welded Cu12Mn8Al3Fe2Ni alloy is much more superior to that of the as-cast one. The cumulative mass lossand the mass loss rate of the as-welded Cu12Mn8Al3Fe2Ni alloy are almost 1/4 that of the as-cast one. SEM analysisof eroded specimens reveals that the as-cast Cu12Mn8Al3Fe2Ni alloy is attacked more severely than the as-weldedone. Microcracks causing cavitation damage initiate at the phase boundaries.展开更多
Mg-Al-Ni alloys were prepared by powder metallurgy, and their microstructure and elevated temperature mechanical properties were investigated. Results indicate that, in addition to α-Mg matrix, both coarse Al;Ni;part...Mg-Al-Ni alloys were prepared by powder metallurgy, and their microstructure and elevated temperature mechanical properties were investigated. Results indicate that, in addition to α-Mg matrix, both coarse Al;Ni;particles and fine Al Ni nano-particles exist in the Mg-Al-Ni alloys. The strength at 150?C is improved with the increase in Ni content. Mg-18.3Al-8Ni alloy possesses a compressive strength of234.7 MPa and a yield strength of 146.5 MPa. Plasticity is also improved with a low concentration of Ni. Mg-11.3Al-2Ni alloy possesses a compression ratio of 17.3%. The phases of Al;Ni;and Al Ni in the alloys block the movements of grain boundaries and dislocations during the deformation at elevated temperature. The existence of Al Ni phase provides a non-basal slip system, leading to the improvement in plasticity. Finally, the formation mechanism of Al-Ni phases in the process is discussed with thermodynamics and kinetics.展开更多
基金Projects (51101096, 51002093) supported by the National Natural Science Foundation of ChinaProject (1052nm05000) supported by Special Foundation of the Shanghai Science and Technology Commission for Nano-Materials ResearchProject (J51042) supported by Leading Academic Discipline Project of the Shanghai Education Commission, China
文摘A Y2O3 particle enhanced Ni/TiC composite coating was fabricated in-situ on a TC4 Ti alloy by laser surface cladding. The phase component, microstructure, composition distribution and properties of the composite layer were investigated. The composite layer has graded microstructures and compositions, due to the fast melting followed by rapid solidification and cooling during laser cladding. The TiC powders are completely dissolved into the melted layer during melting and segregated as fine dendrites when solidified. The size of TiC dendrites decreases with increasing depth. Y2O3 fine particles distribute in the whole clad layer. The Y2O3 particle enhanced Ni/TiC composite layer has a quite uniform hardness along depth with a maximum value of HV1380, which is 4 times higher than the initial hardness. The wear resistance of the Ti alloy is significantly improved after laser cladding due to the high hardness of the composite coating.
文摘Cavitation erosion behavior of as-welded Cu12Mn8Al3Fe2Ni alloy in 3.5% NaCl aqueous solution was studied bymagnetostrictive vibratory device for cavitation erosion. The results show that the cavitation erosion resistance ofthe as-welded Cu12Mn8Al3Fe2Ni alloy is much more superior to that of the as-cast one. The cumulative mass lossand the mass loss rate of the as-welded Cu12Mn8Al3Fe2Ni alloy are almost 1/4 that of the as-cast one. SEM analysisof eroded specimens reveals that the as-cast Cu12Mn8Al3Fe2Ni alloy is attacked more severely than the as-weldedone. Microcracks causing cavitation damage initiate at the phase boundaries.
基金supported by the National Natural Science Foundation of China (No. 51671063)the Research Fund for the Doctoral Program of Higher Education (No. 20132304110006)+1 种基金the Fundamental Research Funds for the Central Universities (No. HEUCF20161016)the Harbin City Application Technology Research and Development Project (Nos. 2015AE4AE005, 2015RQXXJ001, 2016AB2AG013)
文摘Mg-Al-Ni alloys were prepared by powder metallurgy, and their microstructure and elevated temperature mechanical properties were investigated. Results indicate that, in addition to α-Mg matrix, both coarse Al;Ni;particles and fine Al Ni nano-particles exist in the Mg-Al-Ni alloys. The strength at 150?C is improved with the increase in Ni content. Mg-18.3Al-8Ni alloy possesses a compressive strength of234.7 MPa and a yield strength of 146.5 MPa. Plasticity is also improved with a low concentration of Ni. Mg-11.3Al-2Ni alloy possesses a compression ratio of 17.3%. The phases of Al;Ni;and Al Ni in the alloys block the movements of grain boundaries and dislocations during the deformation at elevated temperature. The existence of Al Ni phase provides a non-basal slip system, leading to the improvement in plasticity. Finally, the formation mechanism of Al-Ni phases in the process is discussed with thermodynamics and kinetics.