In this work,flexible photothermal PVA/Ti_(2)O_(3) composite films with different amount(0 wt%,5 wt%,10 wt%,15 wt%)of Ti_(2)O_(3) particles modified by steric acid were prepared by a simple solution casting method.The...In this work,flexible photothermal PVA/Ti_(2)O_(3) composite films with different amount(0 wt%,5 wt%,10 wt%,15 wt%)of Ti_(2)O_(3) particles modified by steric acid were prepared by a simple solution casting method.The microstructures,XRD patterns,FTIR spectra,UV-Vis-NIR spectra thermo-conductivity,thermo-stability and photothermal effects of these composite films were all characterized.These results indicated that Ti_(2)O_(3) particles were well dispersed throughout the polyvinyl alcohol(PVA)matrix in the PVA/Ti_(2)O_(3) composite films.And Ti_(2)O_(3) particles could also effectively improve the photothermal properties of the composite films which exhibited high light absorption and generated a high temperature(about 57.4℃for film with 15 wt%Ti_(2)O_(3) amount)on the surface when it was irradiated by a simulated sunlight source(1 kW/m^(2)).展开更多
Satellited CoNiCrAlY–Al_(2)O_(3)feedstocks with 2wt%, 4wt%, and 6wt% oxide nanoparticles and pure CoNiCrAlY powder were deposited by the high-velocity oxy fuel process on an Inconel738 superalloy substrate. The oxida...Satellited CoNiCrAlY–Al_(2)O_(3)feedstocks with 2wt%, 4wt%, and 6wt% oxide nanoparticles and pure CoNiCrAlY powder were deposited by the high-velocity oxy fuel process on an Inconel738 superalloy substrate. The oxidation test was performed at 1050℃ for 5, 50, 100,150, 200, and 400 h. The microstructure and phase composition of powders and coatings were characterized by scanning electron microscopy and X-ray diffraction, respectively. The bonding strength of the coatings was also evaluated. The results proved that with the increase in the percentage of nanoparticles(from 2wt% to 6wt%), the amount of porosity(from 1vol% to 4.7vol%), unmelted particles, and roughness of the coatings(from 4.8 to 8.8 μm) increased, and the bonding strength decreased from 71 to 48 MPa. The thicknesses of the thermally grown oxide layer of pure and composite coatings(2wt%, 4wt%, and 6wt%) after 400 h oxidation were measured as 6.5, 5.5, 7.6, and 8.1 μm, respectively.The CoNiCrAlY–2wt% Al_(2)O_(3)coating showed the highest oxidation resistance due to the diffusion barrier effect of well-dispersed nanoparticles. The CoNiCrAlY–6wt% Al_(2)O_(3)coating had the lowest oxidation resistance due to its rough surface morphology and porous microstructure.展开更多
SiC composite ceramics for solar absorber and storage integration are new concentrating solar power materials.SiC composite ceramics for solar absorber and storage integration were fabricated using SiC,black corundum ...SiC composite ceramics for solar absorber and storage integration are new concentrating solar power materials.SiC composite ceramics for solar absorber and storage integration were fabricated using SiC,black corundum and kaolin as the raw materials,Co_(2)O_(3)as the additive via pressureless graphite-buried sintering method in this study.Influences of Co_(2)O_(3)on the microstructure and properties of SiC composite ceramics for solar absorber and storage integration were studied.The results indicate that sample D2(5wt%Co_(2)O_(3))sintered at 1480℃exhibits optimal performances for 119.91 MPa bending strength,93%solar absorption,981.5 kJ/kg(25-800℃)thermal storage density.The weight gain ratio is 12.58 mg/cm2after 100 h oxidation at 1000℃.The Co_(2)O_(3)can decrease the liquid phase formation temperature and reduce the viscosity of liquid phase during sintering.The liquid with low viscosity not only promotes the elimination of pores to achieve densification,but also increases bending strength,solar absorption,thermal storage density and oxidation resistance.A dense SiO_(2) layer was formed on the surface of SiC after 100 h oxidation at 1000℃,which protects the sample from further oxidation.However,excessive Co_(2)O_(3)will make the microstructure loose,which is disadvantageous to the performances of samples.展开更多
The potential difference between positive and negative ions was utilized to improve the homogenized dispersion of nanoscale Al_(2)O_(3) whiskers in Mg matrix composites.The Mg powders were decorated with sodium dodecy...The potential difference between positive and negative ions was utilized to improve the homogenized dispersion of nanoscale Al_(2)O_(3) whiskers in Mg matrix composites.The Mg powders were decorated with sodium dodecylbenzene sulfonate(C_(18)H_(29)NaO_(3)S,SDBS)and were introduced to the cathode group on their surface.The Al_(2)O_(3) whiskers were modified by the cetyl trimethyl ammonium bromide(C_(19)H_(42)BrN,CTAB)and were featured in the anode group.The suitable contents of CTAB and SDBS,the application atmosphere,and the type of solvents were investigated.Dispersion results showed that adding 2wt%SDBS into Mg powders and adding 2wt%CTAB into Al_(2)O_(3) whiskers pro-moted the formation of more uniformly mixed composite powders,compared to those of conventional ball milling via scanning electron micro-scopy(SEM)analysis.Meanwhile,the calculated results derived from first-principle calculations also demonstrated the stronger cohesion between Al_(2)O_(3) whisker reinforcements and Mg matrix than undecorated composite powders.After preparation by powder metallurgy,the mor-phology,grain size,hardness,and standard deviation coefficient of composites were analyzed to evaluate the dispersed efficiency.The results indicated that the modification of homogenized dispersed Al_(2)O_(3) whiskers in composites contributed to the refinement of 26%in grain size and the improvement of 20%in hardness compared with pure Mg,and the reduction of 32.5%in the standard deviation coefficient of hardness compared with the ball-milling sample.展开更多
基金Funded by the Youth Backbone Teacher Training Plan in University of Henan Province(No.21220028)Science and Technology Research Project of Henan Province(No.242102321066)+2 种基金Natural Science Foundation of Henan Province(No.232300420312)Henan University of Technology Young Backbone Teacher Training Plan(No.21421260)the Innovation Training Program for College Students in Henan Province(No.202310463046)。
文摘In this work,flexible photothermal PVA/Ti_(2)O_(3) composite films with different amount(0 wt%,5 wt%,10 wt%,15 wt%)of Ti_(2)O_(3) particles modified by steric acid were prepared by a simple solution casting method.The microstructures,XRD patterns,FTIR spectra,UV-Vis-NIR spectra thermo-conductivity,thermo-stability and photothermal effects of these composite films were all characterized.These results indicated that Ti_(2)O_(3) particles were well dispersed throughout the polyvinyl alcohol(PVA)matrix in the PVA/Ti_(2)O_(3) composite films.And Ti_(2)O_(3) particles could also effectively improve the photothermal properties of the composite films which exhibited high light absorption and generated a high temperature(about 57.4℃for film with 15 wt%Ti_(2)O_(3) amount)on the surface when it was irradiated by a simulated sunlight source(1 kW/m^(2)).
文摘Satellited CoNiCrAlY–Al_(2)O_(3)feedstocks with 2wt%, 4wt%, and 6wt% oxide nanoparticles and pure CoNiCrAlY powder were deposited by the high-velocity oxy fuel process on an Inconel738 superalloy substrate. The oxidation test was performed at 1050℃ for 5, 50, 100,150, 200, and 400 h. The microstructure and phase composition of powders and coatings were characterized by scanning electron microscopy and X-ray diffraction, respectively. The bonding strength of the coatings was also evaluated. The results proved that with the increase in the percentage of nanoparticles(from 2wt% to 6wt%), the amount of porosity(from 1vol% to 4.7vol%), unmelted particles, and roughness of the coatings(from 4.8 to 8.8 μm) increased, and the bonding strength decreased from 71 to 48 MPa. The thicknesses of the thermally grown oxide layer of pure and composite coatings(2wt%, 4wt%, and 6wt%) after 400 h oxidation were measured as 6.5, 5.5, 7.6, and 8.1 μm, respectively.The CoNiCrAlY–2wt% Al_(2)O_(3)coating showed the highest oxidation resistance due to the diffusion barrier effect of well-dispersed nanoparticles. The CoNiCrAlY–6wt% Al_(2)O_(3)coating had the lowest oxidation resistance due to its rough surface morphology and porous microstructure.
基金Funded by the National Key R&D Program of China(No.2018YFB1501002)。
文摘SiC composite ceramics for solar absorber and storage integration are new concentrating solar power materials.SiC composite ceramics for solar absorber and storage integration were fabricated using SiC,black corundum and kaolin as the raw materials,Co_(2)O_(3)as the additive via pressureless graphite-buried sintering method in this study.Influences of Co_(2)O_(3)on the microstructure and properties of SiC composite ceramics for solar absorber and storage integration were studied.The results indicate that sample D2(5wt%Co_(2)O_(3))sintered at 1480℃exhibits optimal performances for 119.91 MPa bending strength,93%solar absorption,981.5 kJ/kg(25-800℃)thermal storage density.The weight gain ratio is 12.58 mg/cm2after 100 h oxidation at 1000℃.The Co_(2)O_(3)can decrease the liquid phase formation temperature and reduce the viscosity of liquid phase during sintering.The liquid with low viscosity not only promotes the elimination of pores to achieve densification,but also increases bending strength,solar absorption,thermal storage density and oxidation resistance.A dense SiO_(2) layer was formed on the surface of SiC after 100 h oxidation at 1000℃,which protects the sample from further oxidation.However,excessive Co_(2)O_(3)will make the microstructure loose,which is disadvantageous to the performances of samples.
基金the Fundamental Research Funds for the National Natural Science Foundation of China (Nos. 52101123 and 52004227)the Fundamental Research Funds for the Central Universities-Interdisciplinary Research (No. 2682021ZTPY001)the Dongguan Scitech Commissioner (No. 20211800500102)
文摘The potential difference between positive and negative ions was utilized to improve the homogenized dispersion of nanoscale Al_(2)O_(3) whiskers in Mg matrix composites.The Mg powders were decorated with sodium dodecylbenzene sulfonate(C_(18)H_(29)NaO_(3)S,SDBS)and were introduced to the cathode group on their surface.The Al_(2)O_(3) whiskers were modified by the cetyl trimethyl ammonium bromide(C_(19)H_(42)BrN,CTAB)and were featured in the anode group.The suitable contents of CTAB and SDBS,the application atmosphere,and the type of solvents were investigated.Dispersion results showed that adding 2wt%SDBS into Mg powders and adding 2wt%CTAB into Al_(2)O_(3) whiskers pro-moted the formation of more uniformly mixed composite powders,compared to those of conventional ball milling via scanning electron micro-scopy(SEM)analysis.Meanwhile,the calculated results derived from first-principle calculations also demonstrated the stronger cohesion between Al_(2)O_(3) whisker reinforcements and Mg matrix than undecorated composite powders.After preparation by powder metallurgy,the mor-phology,grain size,hardness,and standard deviation coefficient of composites were analyzed to evaluate the dispersed efficiency.The results indicated that the modification of homogenized dispersed Al_(2)O_(3) whiskers in composites contributed to the refinement of 26%in grain size and the improvement of 20%in hardness compared with pure Mg,and the reduction of 32.5%in the standard deviation coefficient of hardness compared with the ball-milling sample.