Effect of Zr on microstructure and mechanical properties of 304 stainless steel joints brazed by Ag-Cu-Sn-In filler metal

The effect of Zr on the microstructure and mechanical properties of 304 stainless steel joints brazed with Ag-Cu fillers was studied.The incorporation of Zr had little effect on the solid-liquid phase line of the fillers,and the melting temperature range of the fillers was narrowed,which enhanced their fluidity and wettability.The presence of Zr in the form of heterogeneous particles augmented the nucleation rate during solidification,transforming the intermittently distributed gray-black coarse dendrites into cellular crystals.This structural transformation led to fragmentation and refinement of the microstructure.The dissolution of Zr into Ag and Cu promoted the transformation of low-angle grain boundaries to high-angle grain boundaries(HAGBs),hindering crack propagation.Zr element in the brazing seam led to grain refinement and increased density of grain boundaries.The grain refinement could disperse the stress,and HAGBs could resist the dislocation movement,improving the joint strength.The results display that when Zr content was 0.75 wt.%,the maximum strength was 221.1 MPa.The fracture occurred primarily at the brazing seam,exhibiting a ductile fracture.

Effect of brazing temperature on microstructure and tensile strength ofγ-TiAl joint vacuum brazed with micro-nano Ti−Cu−Ni−Nb−Al−Hf filler

A novel micro-nano Ti−10Cu−10Ni−8Al−8Nb−4Zr−1.5Hf filler was used to vacuum braze Ti−47Al−2Nb−2Cr−0.15B alloy at 1160−1220℃ for 30 min.The interfacial microstructure and formation mechanism of TiAl joints and the relationships among brazing temperature,interfacial microstructure and joint strength were emphatically investigated.Results show that the TiAl joints brazed at 1160 and 1180℃ possess three interfacial layers and mainly consist of α_(2)-Ti_(3)Al,τ_(3)-Al_(3)NiTi_(2) and Ti_(2)Ni,but the brazing seams are no longer layered and Ti_(2)Ni is completely replaced by the uniformly distributed τ_(3)-Al_(3)NiTi_(2) at 1200 and 1220℃ due to the destruction of α_(2)-Ti_(3)Al barrier layer.This transformation at 1200℃ obviously improves the tensile strength of the joint and obtains a maximum of 343 MPa.Notably,the outward diffusion of Al atoms from the dissolution of TiAl substrate dominates the microstructure evolution and tensile strength of the TiAl joint at different brazing temperatures.

Microstructure and properties of Cu/Al joints brazed with Zn-Al filler metals

The mechanical properties and microstructural distribution of the Cu/A1 brazing joints formed by torch-brazing with different Zn-A1 filler metals were investigated. The microstructure of the Zn-A1 alloys was studied by optical microscopy and scanning electron microscopy, and the phase constitution of the Cu/A1 joints was analyzed by energy dispersion spectrometry. The results show that the spreading area of the Zn-A1 filler metals on the Cu and A1 substrates increases as the A1 content increases. The mechanical results indicate that the shear strength reaches a peak value of 88 MPa when A1 and Cu are brazed with Zn-15AI filler metal. Microhardness levels from HV122 to HV515 were produced in the three brazing seam regions corresponding to various microstructure features. The Zn- and Al-rich phases exist in the middle brazing seam regions. However, two interface layers, CuZn3 and A12Cu are formed on the Cu side when the A1 content in the filler metals is 2% and more than 15%, respectively. The relationship between intermetallic compounds on Cu side and Zn-xA1 filler metals was investigated.

Microstructure and properties of the joints of ZrO2 ceramic/ stainless steel brazed in vacuum with AgCuTi active filler metal

The ZrO2 ceranfic was successfully jointed to stainless steel by vacuum brazing with active filler metal. The AgCuTi active filler metal was used and the joining was performed at a temperature of 850 ℃ for 10 rain. The microstructures of the joints were characterized by metallographic microscopy, scanning electron microscopy （SEM）, and energy dispersive spectroscopy （EDS）. Metallographic microscopy analysis shows that the morphology of the cross section was a sandwich structure and the TiO is observed in the surface of ZrO2/ stainless steel. The diffusion and enrichment of the elements are the key roles in the brazing of ZrO2 ceramic and stainless steel. The formation of TiCu compounds inhibited the further diffusion of titanium into stainless steel or the ZrO2 ceramic to form TiO compound. In the experimental conditions, the average tensile strength is 80MPa for the joint of ZrO2 ceramic / AgCuTi/ stainless steel systems. A complete joint is formed between the ZrO2 ceramic and stainless steel with the leakage rate at the degree of 10 ^-12 Pa · m^3/s.

Microstructure and shear strength ofγ-TiAl/GH536 joints brazed with Ti-Zr-Cu-Ni-Fe-Co-Mo filler alloy

The influence of brazing temperature and brazing time on the microstructure and shear strength ofγ-TiAl/GH536 joints brazed with Ti-Zr-Cu-Ni-Fe-Co-Mo filler was investigated using SEM,EDS,XRD and universal testing machine.Results show that all the brazed joints mainly consist of four reaction layers regardless of the brazing temperature and brazing time.The thickness of the brazed seam and the average shear strength of the joint increase firstly and then decrease with brazing temperature in the range of 1090-1170℃and brazing time varying from 0 to 20 min.The maximum shear strength of 262 MPa is obtained at 1150℃for 10 min.The brittle Al3NiTi2 and TiNi3 intermetallics are the main controlling factors for the crack generation and deterioration of joint strength.The fracture surface is characterized as typical cleavage fracture and it mainly consists of massive brittle Al3NiTi2 intermetallics.

Interfacial microstructure and mechanical properties of tungsten carbide brazed joints using Ag-Cu-Zn + Ni/Mn filler alloy

WC-Co hard metal was furnace brazed by Ag-Cu-Zn+Ni/Mn filler alloy using a tube furnace under high-purity argon at730°C.The influence of brazing time and gap size of joints was studied.The results revealed the maximum shear strength of(156±7)MPa for samples with150μm gap size at a holding time15min.The characterization and microstructure of the brazed joints were characterized by SEM,EDS and XRD.The results showed that increasing the time from5to15min could provide a better chance for the liquid interlayer to flow towards the base metal.However,the formation of some metallic phases such as Mn3W3C at brazing time longer than15min resulted in decreased shear strength of the joint.

Theoretical study and numerical simulation of the stress fields of the Al_2O_3 joints brazed with composite filler materials

Non-linear finite element code MSC. Marc was utilized to analysis the field of stress of the Al2O3 joints brazed with composite filler materials. The properties of the filler materials were defined by using the mixing law, method of Mori-Tanaka and theory of Eshelby to ensure the accuracy and reliability of results of finite element method （FEM）. The results show stress in brazed beam is higher than that in base material. The maximal stress can be found in the interface of joint. And the experimental results show that the shear strength of joints increases from 93.75 MPa （ Al2O3p Ovol. % ） to 135.32 MPa （ Al2O3p 15vol. % ） when composition of titanium is 3wt% in the filler metal.

Interfacial features of TiAl alloy/316L stainless steel joint brazed with Zr−Cu−Ni−Al amorphous filler metal

TiAl alloy and 316L stainless steel were vacuum-brazed with Zr−50.0Cu−7.1Ni−7.1Al(at.%)amorphous filler metal.The influence of brazing time and temperature on the interfacial microstructure and shear strength of the resultant joints was investigated.The brazed seam consisted of three layers,including two diffusion layers and one residual filler metal layer.The typical microstructure of brazed TiAl alloy/316L stainless steel joint was TiAl alloy substrate/α2-(Ti3Al)/AlCuTi/residual filler metal/Cu9Zr11+Fe23Zr6/Laves-Fe2Zr/α-(Fe,Cr)/316L stainless steel substrate.Discontinuous brittle Fe2Zr layer formed near the interface between the residual filler metal layer andα-(Fe,Cr)layer.The maximum shear strength of brazed joints reached 129 MPa when brazed at 1020℃ for 10 min.The diffusion activation energies ofα2-(Ti3Al)andα-(Fe,Cr)phases were−195.769 and−112.420 kJ/mol,respectively,the diffusion constants for these two phases were 3.639×10^(−6) and 7.502×10^(−10)μm^(2)/s,respectively.Cracks initiated at Fe2Zr layer and propagated into the residual filler metal layer during the shear test.The Laves-Fe2Zr phase existing on the fracture surface suggested the brittle fracture mode of the brazed joints.

Al2_3/Al2O3 Joint Brazed with Al2O3-particulate-contained Composite Ag-Cu-Ti Filler Material

Microstructure and interracial reactions of Al2O3 joints brazed with Al2O3-particulate-contained composite Ag-Cu-Ti filler material were researched by scanning electron microscopy （SEM）, electron probe microscopy analysis （EPMA）, energy dispersive spectroscopy （EDS） and X-ray diffraction （XRD）. The interracial reaction layer thickness of joints brazed with conventional active filler metal and active composite filler materials with different volume fraction of Al2O3 particulate was also studied. The experimental results indicated although there were Al2O3 particulates added into active filler metals, the time dependence of interracial layer growth of joints brazed with active composite filler material is t^1/2 as described by Fickian law as the joints brazed with conventional active filler metal.

Interfacial microstructure and mechanical properties of GH99 superalloy and Nb brazed joint using Cu75Pt25 filler

Cu75Pt25 brazing filler was applied to brazing GH99 superalloy to Nb,and the sound joints were obtained by adjusting brazing parameters.The typical interfacial microstructure of the brazed joint was Nb/Nb7Ni6+NbNi3/Ni(s,s)+Cr-rich NbNi3+(NbCr2+NbNi3)/GH99.The effects of brazing temperature and holding time on the interfacial microstructure of GH99/Cu75Pt25/Nb joints were studied.The results showed that the solution and diffusion of Ni atoms from GH99 substrate into brazing seam played a critical role in the interfacial microstructure evolution.As the brazing temperature rose,the Nb−Ni reaction layer was formed instead of the initial Nb3Pt layer,and the thickness increased firstly and then remained constant.The highest shear strength of the joint reached 152 MPa when brazed at 1150℃ for 15 min.All of the joints presented a brittle fracture mode during shear test,and the fracture location changed from Nb3Pt layer to Nb−Ni compounds layer.

Brazeability evaluation of Ti-Zr-Cu-Ni-Co-Mo filler for vacuum brazing TiAl-based alloy

Ti-47Al-2Nb-2Cr-0.15B(mole fraction,%)alloy was vacuum brazed with amorphous and crystalline Ti.25Zr-12.5Cu-12.5Ni-3.0Co-2.0Mo(mass fraction,%)filler alloys,and the melting,spreading and gap filling behaviors of the amorphous and crystalline filler alloys as well as the joints brazed with them were investigated in details.Results showed that the amorphous filler alloy possessed narrower melting temperature interval,lower liquidus temperature and melting active energy compared with the crystalline filler alloy,and it also exhibited better brazeability on the surface of the Ti.47Al.2Nb.2Cr.0.15B alloy.The TiAl joints brazed with crystalline and amorphous filler alloys were composed of two interfacial reaction layers and a central brazed layer.Under the same conditions,the tensile strength of the joint brazed with the amorphous filler alloy was always higher than that with the crystalline filler alloy.The maxmium tensile strength of the joint brazed at 1273 K with the amorphous filler alloy reached 254 MPa.

Brazed joints of CBN grains and AISI 1045 steel with AgCuTi-TiC mixed powder as filler materials

The brazing process of cubic boron nitride （CBN） grains and AISI 1045 steel with AgCuTi-TiC mixed powder as a filler material was carried out.The joining strength and the interfacial microstructure were investigated.The experimental results indicate that the spreading of the molten filler material on AISI 1045 steel is decreased with the increase of TiC content.A good interface is formed between the TiC particulates and AgCuTi alloy through the wetting behavior.In the case of AgCuTi＋16wt% TiC,the strength of the brazed steel-to-steel joints reached the highest value of 95MPa dependent upon the reinforcement effect of TiC particles within the filler layer.Brazing resultants of TiB2,TiB,and TiN are produced at the interface of the CBN grains and the AgCuTi-TiC filler layer by virtue of the interdiffusion of B,N,and Ti atoms.

Microstructure and properties of the joints of Cu/Cu and metallized Cu / kovar brazed with a low-silver vacuum brazing filler metal

In an attempt to develop low-silver brazing filler metals used for hermetic sealing materials in the vacuum interrupter industry,the ternary Ag-50Cu-5Ga low-silver vacuum brazing filler metal was investigated.The melting temperature was measured by differential scanning calorimetry(DSC),and the brazability of Ag-50Cu-5Ga alloy on copper and metallized copper/kovar were ascertained at 850℃under 1×10-4 Pa in this article.The microstructures of the filler metal and the joints have been analyzed by using scanning electron microscopy(SEM),equipped with an energy dispersive spectroscopy.The results show that vacuum brazing was success to join with copper or metallized copper/kovar using Ag-50Cu-5Ga filler and reliable joints were obtained.There were Ag-rich phase,Cu-rich phase and a fine eutectic structure of Ag-based solid solution and Cu-based solid solution in the copper joints and the width of brazing seam is about 60μm.The joints of kovar alloy to copper after surface nickel plating was composed of AgCu eutectic phase,Ag,Cu,Cu2Ga and CuNi2 phase.The tensile strength was 167 MPa and 150 MPa,respectively.The tensile results of joints show that the joint strengths were equivalent to the traditional brazing filler metals.

Microstructure and mechanical properties of Cu/Al joints brazed using(Cu,Ni,Zr,Er)-modified Al−Si filler alloys

To design a promising Al−Si filler alloy with a relatively low melting-point,good strength and plasticity for the Cu/Al joint,the Cu,Ni,Zr and Er elements were innovatively added to modify the traditional Al−Si eutectic filler.The microstructure and mechanical properties of filler alloys and Cu/Al joints were investigated.The result indicated that the Al−Si−Ni−Cu filler alloys mainly consisted of Al(s,s),Al_(2)(Cu,Ni)and Si(s,s).The Al−10Si−2Ni−6Cu filler alloy exhibited relatively low solidus(521℃)and liquidus(577℃)temperature,good tensile strength(305.8 MPa)and fracture elongation(8.5%).The corresponding Cu/Al joint brazed using Al−10Si−2Ni−6Cu filler was mainly composed of Al_(8)(Mn,Fe)_(2)Si,Al_(2)(Cu,Ni)3,Al(Cu,Ni),Al_(2)(Cu,Ni)and Al(s,s),yielding a shear strength of(90.3±10.7)MPa.The joint strength was further improved to(94.6±2.5)MPa when the joint was brazed using the Al−10Si−2Ni−6Cu−0.2Er−0.2Zr filler alloy.Consequently,the(Cu,Ni,Zr,Er)-modified Al−Si filler alloy was suitable for obtaining high-quality Cu/Al brazed joints.

Effects of Al2O3 Particulates on the Thickness of Reaction Layer of Al2O3 Joints Brazed with Al2O3-Particulate-Contained Composite Filler Materials

In order to understand the rate-controlling process for the interfacial layer growth of brazing joints brazed with active composite filler materials, the thickness of brazing joints brazed with conventional active filler metal and active composite filler materials with different volume fraction of AI2O3 participate was studied. The experimental results indicate although there are Al2O3 particulates added into active filler metals, the time dependence of interfacial layer growth is t2 as described by Fickian law for the joints brazed with conventional active filler metal. It also shows that the key factor affecting the interfacial layer growth is the volume fraction of alumina in the composite filler material compared with the titanium weight fraction in the filler material.

Influence of filler metal and processing on brazed joints of TiAl alloy and 42CrMo

The filler metals of AgAlTi and AgAlTiCo were selected for the vacuum brazing of TiAl alloy and 42CrMo under different processing parameters. The results show that for both filler metals, the highest tensile strength of joint can be achieved at 950℃, 15min, and with the addition of Co the joint strength becomes higher. By the comparison of the microstructure of joints, the joint interface is the main factor that influences the joint strength.

Evaluation of the Properties of Si3N4/Si3N4 Joint Brazed Using a Filler Alloy Containing Pd

Si3N4 ceramic was jointed to itself using a filler alloy of Cu76.5Pd8.5Ti15, and the mechanical properties of the jointwere measured and analyzed. By using a filler alloy of Cu76.5Pd8.5Ti15, the SisN4/SisN4 joints were obtained bybrazing at 1373～1473 K for 0.9～5.4 ks under a pressure of 2×10-3 MPa. The effect of brazing parameters on theshear strength of the joint was investigated. When the brazing temperature and holding time is 1423 K and 5.4 ksrespectively, the maximum shear strength of the Si3N4/Si3N4 joint is obtained to be 198 MPa.

Research progress of nanoparticles reinforced composite filler metal

Composite filler metal refers to the traditional filler metal by adding a certain proportion of various forms of superalloy,carbon fiber and ceramic particles as reinforcement phase.Due to the addition of the reinforcement phase,the filler metal can have a suitable thermal expansion coefficient,which can effectively reduce the residual stress at the brazing joint caused by the different thermal expansion coefficients of the base metal and improve the comprehensive performance of the brazing joint.In recent years,with the progress of science and technology,the research on nanomaterials has been deepening,and nanomaterials are widely used in the modification of composite filler metals because of their special surface effect,small size effect,quantum size effect and macroscopic quantum tunneling effect.The modification performance of different composite solders by nanoparticles in recent years is reviewed,the advantages and disadvantages of nano-reinforced composite solders are analyzed,and the future research direction of composite solders is prospected.

Development of Al-12Si-xTi system active ternary filler metals for Al metal matrix composites

To improve the wettability of Al metal matrix composites（Al-MMCs） by common filler metals,Al-12Si-xTi（x=0.1,0.5,1,3.0;mass fraction,%） system active ternary filler metals were prepared.It was demonstrated that although the added Ti existed within Ti（Al1-xSix）3（0≤x≤0.15） phase,the shear strength and shear fracture surface of the developed Al-12Si-xTi brazes were quite similar to those of traditional Al-12Si braze due to the presence of similar microstructure of Al-Si eutectic microstructure with large volume fraction.So,small Ti addition（～1%） did not make the active brazes brittle and hard compared with the conventional Al-12Si braze.The measured melting range of each Al-12Si-xTi foil was very similar,i.e.,580-590 ℃,because the composition was close to that of eutectic.For wettability improvement,with increasing Ti content,the interfacial gap between the Al2O3 reinforcement and filler metal（R/M） could be eliminated,and the amount of the remainder of the active fillers on the composite substrate decreased after sessile drop test at 610 ℃ for 30 min.So,the wettability improvement became easy to observe repeatedly with increasing Ti content.Additionally,the amount and size of Ti（AlSi）3 phase were sensitive to the Ti content（before brazing） and Si content（after brazing）.

Effects of germanium additions on microstructures and properties of Al-Si filler metals for brazing aluminum

A series of Al?Si?Ge filler metals were studied for brazing aluminum. The microstructures and properties of the filler metals were investigated systematically. The results show that the liquidus temperature of Al?Si?Ge filler metals drops from 592 to 519 °C as the content of Ge increases from 0 to 30% (mass fraction). As the content of Ge increases, bright eutectic Ge forms. However, as the Ge content exceeds 20%, the aggregation growth of the eutectic structure tends to happen and coarsened primary Si?Ge particle forms, which is detrimental to the properties of alloys. The Al?10.8Si?10Ge filler metal has good processability and wettability with the base metal Al. When this filler metal is used to braze 1060 aluminum, the complete joint can be achieved. Furthermore, the shear strength test results show that the fracture of brazed joint with Al?10.8Si?10Ge filler metal occurs in the base metal.