Ultrahigh strength Al-12Zn-2.4Mg-1.1Cu-0.20Zr-0.30Sc-0.30Ni alloy billets were fabricated by spray deposition method(the Osprey process). The effect of homogenization treatment on the microstructures and tensile prope...Ultrahigh strength Al-12Zn-2.4Mg-1.1Cu-0.20Zr-0.30Sc-0.30Ni alloy billets were fabricated by spray deposition method(the Osprey process). The effect of homogenization treatment on the microstructures and tensile properties were investigated by OM, SEM and EDS. The results show that adding small amount of Sc and Zr can greatly refine the grain size of the billet, with the average grain size of 10 μm. Grain-boundary becomes coarser firstly and then thinner under different homogenizing condition and grain coarsening were observed. The solute elements content of Zn inside grains has a peak at 490 ℃ /2 h, and Cu element, which was solved into matrix, can enhance the matrix hardness obviously during homogenization. The suitable homogenizing treatment is 460～490 °C/2 h for the hot extrusion of the studied alloy; after the optimized solid solution and T6 aging, the highest ultimate tensile strength (UTS) is 858 MPa with a ductility of 4.8%.展开更多
The effect of adding 0.03wt%Ni on the microstructure and mechanical properties of Al–Mg–Si–Cu–Zn alloys was systematically studied.The results reveal that the number density of spherical Fe-rich phases within grai...The effect of adding 0.03wt%Ni on the microstructure and mechanical properties of Al–Mg–Si–Cu–Zn alloys was systematically studied.The results reveal that the number density of spherical Fe-rich phases within grains increases with the addition of Ni,accompanied by the formation of Q(Al3Mg9Si7Cu2)precipitates around the spherical Fe-rich phases.Additionally,Ni addition is beneficial to reducing the grain size in the as-cast state.During the homogenization process,Q phases could be completely dissolved and the grain size could remain basically unchanged.However,compared with the Ni-free alloy,the Fe-rich phase in the Ni-containing alloy is more likely to undergo the phase transformation and further form more spherical particles during homogenization treatment.After thermomechanical processing,the distribution of Fe-rich phases in the Ni-containing alloy was further greatly improved and directly resulted in a greater formability than that of the Ni-free alloy.Accordingly,a reasonable Ni addition positively affected the microstructure and formability of the alloys.展开更多
The electrochemical behavior of Cu-Zn-Al shape memory alloy (SMA) with andwithout electroless plated Ni-P was investigated by electrochemical methods, in artificial Tyrode'ssolution. The results showed that Cu-Zn-...The electrochemical behavior of Cu-Zn-Al shape memory alloy (SMA) with andwithout electroless plated Ni-P was investigated by electrochemical methods, in artificial Tyrode'ssolution. The results showed that Cu-Zn-Al SMA engendered dezincification corrosion in Tyrode'ssolution. The anodic active current densities as well as electrochemical dissolution sensitivity ofthe electroless plated Ni-P Cu-Zn-Al SMA increased with NaCl concentration rising, pH of solutiondecreasing and environmental temperature uprising. X-ray diffraction analysis indicated that aftersurface modification by electroless plated Ni-P, an amorphous plated film formed on the surface ofCu-Zn-Al SMA. This film can effectively isolate matrix metal from corrosion media and significantlyimprove the electrochemical property of Cu-Zn-Al SMA in artificial Tyrode's solution.展开更多
目的建立微波消解-电感耦合等离子体质谱（ICP-MS）直接稀释测定脉络宁注射液中25种矿物质元素（Mg、Ca、Fe、Cu、Zn、Mn、Al、B、Ba、Co、Cr、K、Li、Mo、Na、Ni、P、Pb、Sr、Th、Ti、V、As、Cd和Hg）的方法。方法分别对微波消解条件...目的建立微波消解-电感耦合等离子体质谱（ICP-MS）直接稀释测定脉络宁注射液中25种矿物质元素（Mg、Ca、Fe、Cu、Zn、Mn、Al、B、Ba、Co、Cr、K、Li、Mo、Na、Ni、P、Pb、Sr、Th、Ti、V、As、Cd和Hg）的方法。方法分别对微波消解条件和测试条件进行考察;样品经微波消解后,采用电感耦合质谱仪测定25种矿物质元素,并对测定方法学进行考察。结果确定最佳消解条件为3步缓慢升温：400 W 80℃升温10 min,保留5 min;600 W 120℃升温10 min,保留5 min;900 W 200℃升温20 min,保留20 min;25种矿物质元素在各自的线性范围内线性关系良好,r≥0.999 6,精密度、稳定性和重复性试验的RSD均符合定量分析要求;加标回收率为94.7%~106.1%,RSD在0.34%~2.79%。脉络宁注射液中检测出Mg、Ca、Fe、Cu、Zn、Mn、Al、B、Ba、Co、Cr、K、Li、Mo、Na、Ni、P、Pb、Sr、Th、Ti、V,未检出As、Cd和Hg。结论该方法简便、迅速、准确,适用于脉络宁注射液中25种矿物质元素的同时测定。展开更多
基金Colleges and Universities Scientific Research Fund of Inner Mongolia (NJ06083)
文摘Ultrahigh strength Al-12Zn-2.4Mg-1.1Cu-0.20Zr-0.30Sc-0.30Ni alloy billets were fabricated by spray deposition method(the Osprey process). The effect of homogenization treatment on the microstructures and tensile properties were investigated by OM, SEM and EDS. The results show that adding small amount of Sc and Zr can greatly refine the grain size of the billet, with the average grain size of 10 μm. Grain-boundary becomes coarser firstly and then thinner under different homogenizing condition and grain coarsening were observed. The solute elements content of Zn inside grains has a peak at 490 ℃ /2 h, and Cu element, which was solved into matrix, can enhance the matrix hardness obviously during homogenization. The suitable homogenizing treatment is 460～490 °C/2 h for the hot extrusion of the studied alloy; after the optimized solid solution and T6 aging, the highest ultimate tensile strength (UTS) is 858 MPa with a ductility of 4.8%.
基金financially supported by the National Key Research and Development Program of China(No.2016YFB0300801)the National Natural Science Foundation of China(Nos.51871029,51571023,and 51301016)+2 种基金Beijing Natural Science Foundation(No.2172038)Beijing Laboratory of Metallic Materials and Processing for Modern Transportation(No.FRF-SD-B-005B)The China Scholarship Council for financial support to M.X.Guo
文摘The effect of adding 0.03wt%Ni on the microstructure and mechanical properties of Al–Mg–Si–Cu–Zn alloys was systematically studied.The results reveal that the number density of spherical Fe-rich phases within grains increases with the addition of Ni,accompanied by the formation of Q(Al3Mg9Si7Cu2)precipitates around the spherical Fe-rich phases.Additionally,Ni addition is beneficial to reducing the grain size in the as-cast state.During the homogenization process,Q phases could be completely dissolved and the grain size could remain basically unchanged.However,compared with the Ni-free alloy,the Fe-rich phase in the Ni-containing alloy is more likely to undergo the phase transformation and further form more spherical particles during homogenization treatment.After thermomechanical processing,the distribution of Fe-rich phases in the Ni-containing alloy was further greatly improved and directly resulted in a greater formability than that of the Ni-free alloy.Accordingly,a reasonable Ni addition positively affected the microstructure and formability of the alloys.
文摘The electrochemical behavior of Cu-Zn-Al shape memory alloy (SMA) with andwithout electroless plated Ni-P was investigated by electrochemical methods, in artificial Tyrode'ssolution. The results showed that Cu-Zn-Al SMA engendered dezincification corrosion in Tyrode'ssolution. The anodic active current densities as well as electrochemical dissolution sensitivity ofthe electroless plated Ni-P Cu-Zn-Al SMA increased with NaCl concentration rising, pH of solutiondecreasing and environmental temperature uprising. X-ray diffraction analysis indicated that aftersurface modification by electroless plated Ni-P, an amorphous plated film formed on the surface ofCu-Zn-Al SMA. This film can effectively isolate matrix metal from corrosion media and significantlyimprove the electrochemical property of Cu-Zn-Al SMA in artificial Tyrode's solution.
文摘目的建立微波消解-电感耦合等离子体质谱（ICP-MS）直接稀释测定脉络宁注射液中25种矿物质元素（Mg、Ca、Fe、Cu、Zn、Mn、Al、B、Ba、Co、Cr、K、Li、Mo、Na、Ni、P、Pb、Sr、Th、Ti、V、As、Cd和Hg）的方法。方法分别对微波消解条件和测试条件进行考察;样品经微波消解后,采用电感耦合质谱仪测定25种矿物质元素,并对测定方法学进行考察。结果确定最佳消解条件为3步缓慢升温：400 W 80℃升温10 min,保留5 min;600 W 120℃升温10 min,保留5 min;900 W 200℃升温20 min,保留20 min;25种矿物质元素在各自的线性范围内线性关系良好,r≥0.999 6,精密度、稳定性和重复性试验的RSD均符合定量分析要求;加标回收率为94.7%~106.1%,RSD在0.34%~2.79%。脉络宁注射液中检测出Mg、Ca、Fe、Cu、Zn、Mn、Al、B、Ba、Co、Cr、K、Li、Mo、Na、Ni、P、Pb、Sr、Th、Ti、V,未检出As、Cd和Hg。结论该方法简便、迅速、准确,适用于脉络宁注射液中25种矿物质元素的同时测定。