以氧化镁粉末为载体,N2H4·H2O为还原剂,采用浸渍还原法制备Cu2O/MgO催化剂。考察制备条件对催化剂活性的影响,最佳原料配比为n(Cu2+)∶n(NaOH)∶n(N2H4·H2O)=5∶11∶5,对筛选出最佳条件下制备的催化剂进行正己醇脱氢制备正己...以氧化镁粉末为载体,N2H4·H2O为还原剂,采用浸渍还原法制备Cu2O/MgO催化剂。考察制备条件对催化剂活性的影响,最佳原料配比为n(Cu2+)∶n(NaOH)∶n(N2H4·H2O)=5∶11∶5,对筛选出最佳条件下制备的催化剂进行正己醇脱氢制备正己醛工艺条件考察,采用SEM、XRD和BET对催化剂进行表征。结果表明,在反应温度250℃、空速1.25 m L·(h·g)-1、催化剂用量12 g和N2流速0.05 L·min-1条件下,正己醇转化率为59.33%,正己醛选择性为93.81%。展开更多
A novel coprecipitation-reduction process has been proposed for preparing highly selective Cu/ZnO/Al 2O 3 catalysts for methanol synthesis from CO 2 hydrogenation. Compared to the catalysts prepared by the conventiona...A novel coprecipitation-reduction process has been proposed for preparing highly selective Cu/ZnO/Al 2O 3 catalysts for methanol synthesis from CO 2 hydrogenation. Compared to the catalysts prepared by the conventional method, the new catalysts prepared via the new method exhibit much higher BET surface area and pore size, much smaller crystallite size and higher catalytic activity and selectivity in CO 2 hydrogenation to methanol. It is also found that the molar ratio of Cu + to Cu 0 on the surface of the catalyst obtained by coprecipitation-reduction is much higher than that on the reduced catalyst obtained by the conventional method, which could be crucial for its high activity and selectivity for catalytic hydrogenation of CO 2 to methanol.展开更多
Hydrogen production by catalytic steam reforming of methanol over a series of coprecipitated Cu/ZnO/Al2O3 catalysts under atmospheric pressure in a microreactor has been studied Effects of catalyst composition...Hydrogen production by catalytic steam reforming of methanol over a series of coprecipitated Cu/ZnO/Al2O3 catalysts under atmospheric pressure in a microreactor has been studied Effects of catalyst composition, reaction temperature and activation conditions on the catalytic activity have been investigated Crystal phases of catalysts were analyzed by XRD The results showed that Cu/ZnO/Al2O3 catalysts displayed high activity and selectivity for hydrogen and stability The optimized molar ratio is Cu/Zn=10, a maximum methanol conversion of 994?mol%, hydrogen selectivity of 999?mol% and CO molar fraction of 0007% were obtained in the steam reforming reaction with the catalyst containing 45?mol% copper XRD results showed that the diffraction peaks of CuO in the catalyst were clearly lower and broaden It indicated that high dispersion of small copper crystallites on the catalyst surface was formed under the calcination conditions It is suggested that the good performance of Cu/ZnO/Al2O3 catalysts partly resulted from well dispersed展开更多
We demonstrate for the first time that a short time of microwave irradiation on the oxide precursor of a Cu/ZnO/Al2O3 catalyst can provide unique opportunity for tailoring the microstructure and activity of the cataly...We demonstrate for the first time that a short time of microwave irradiation on the oxide precursor of a Cu/ZnO/Al2O3 catalyst can provide unique opportunity for tailoring the microstructure and activity of the catalyst for methanol steam reforming. It is shown by in situ XRD that a considerable increase in the microstrain of Cu nanocrystals could be achieved in the catalysts processed by microwave irradiation for 310 min, which correlates well with the enhanced CH3OH conversion as observed on the corresponding samples. The present work also confirms that although the high specific surface area of Cu is a prerequisite for catalytic activity, it does not account for the observed changes in activity and selectivity alone without taking bulk microstructural changes into account.展开更多
文摘以氧化镁粉末为载体,N2H4·H2O为还原剂,采用浸渍还原法制备Cu2O/MgO催化剂。考察制备条件对催化剂活性的影响,最佳原料配比为n(Cu2+)∶n(NaOH)∶n(N2H4·H2O)=5∶11∶5,对筛选出最佳条件下制备的催化剂进行正己醇脱氢制备正己醛工艺条件考察,采用SEM、XRD和BET对催化剂进行表征。结果表明,在反应温度250℃、空速1.25 m L·(h·g)-1、催化剂用量12 g和N2流速0.05 L·min-1条件下,正己醇转化率为59.33%,正己醛选择性为93.81%。
文摘A novel coprecipitation-reduction process has been proposed for preparing highly selective Cu/ZnO/Al 2O 3 catalysts for methanol synthesis from CO 2 hydrogenation. Compared to the catalysts prepared by the conventional method, the new catalysts prepared via the new method exhibit much higher BET surface area and pore size, much smaller crystallite size and higher catalytic activity and selectivity in CO 2 hydrogenation to methanol. It is also found that the molar ratio of Cu + to Cu 0 on the surface of the catalyst obtained by coprecipitation-reduction is much higher than that on the reduced catalyst obtained by the conventional method, which could be crucial for its high activity and selectivity for catalytic hydrogenation of CO 2 to methanol.
文摘Hydrogen production by catalytic steam reforming of methanol over a series of coprecipitated Cu/ZnO/Al2O3 catalysts under atmospheric pressure in a microreactor has been studied Effects of catalyst composition, reaction temperature and activation conditions on the catalytic activity have been investigated Crystal phases of catalysts were analyzed by XRD The results showed that Cu/ZnO/Al2O3 catalysts displayed high activity and selectivity for hydrogen and stability The optimized molar ratio is Cu/Zn=10, a maximum methanol conversion of 994?mol%, hydrogen selectivity of 999?mol% and CO molar fraction of 0007% were obtained in the steam reforming reaction with the catalyst containing 45?mol% copper XRD results showed that the diffraction peaks of CuO in the catalyst were clearly lower and broaden It indicated that high dispersion of small copper crystallites on the catalyst surface was formed under the calcination conditions It is suggested that the good performance of Cu/ZnO/Al2O3 catalysts partly resulted from well dispersed
文摘We demonstrate for the first time that a short time of microwave irradiation on the oxide precursor of a Cu/ZnO/Al2O3 catalyst can provide unique opportunity for tailoring the microstructure and activity of the catalyst for methanol steam reforming. It is shown by in situ XRD that a considerable increase in the microstrain of Cu nanocrystals could be achieved in the catalysts processed by microwave irradiation for 310 min, which correlates well with the enhanced CH3OH conversion as observed on the corresponding samples. The present work also confirms that although the high specific surface area of Cu is a prerequisite for catalytic activity, it does not account for the observed changes in activity and selectivity alone without taking bulk microstructural changes into account.