The corrosion behavior of a CuCrNiAl alloy with NaCl deposit at 700 and 900℃ was studied by means of metalloscope, XRD, SEM/EDX, and thermogravimetric analysis. The results indicated that the corrosion of the CuCrNiA...The corrosion behavior of a CuCrNiAl alloy with NaCl deposit at 700 and 900℃ was studied by means of metalloscope, XRD, SEM/EDX, and thermogravimetric analysis. The results indicated that the corrosion of the CuCrNiAl alloy beneath the NaCl deposit is severe; the corrosion production is loose and easy to scale off; the Cr phase is easier to erode than the Cu phase, and the contents of Cu and Cr decrease when the content of Ni increases in the matrix of the alloy beneath the corrosion region. The effects of distortion on the corrosion of the CuCrNiAl alloy were discussed, and the acceleration mechanisms of NaCl on the corrosion were also discussed.展开更多
文摘The corrosion behavior of a CuCrNiAl alloy with NaCl deposit at 700 and 900℃ was studied by means of metalloscope, XRD, SEM/EDX, and thermogravimetric analysis. The results indicated that the corrosion of the CuCrNiAl alloy beneath the NaCl deposit is severe; the corrosion production is loose and easy to scale off; the Cr phase is easier to erode than the Cu phase, and the contents of Cu and Cr decrease when the content of Ni increases in the matrix of the alloy beneath the corrosion region. The effects of distortion on the corrosion of the CuCrNiAl alloy were discussed, and the acceleration mechanisms of NaCl on the corrosion were also discussed.