Hierachically porous （HP） CuO/α-Fe2O3/SiO2 composite material was fabricated by sol-gel method and multi-hydrothermal processes using HP-SiO2 as support.The resulting material was characterized by N2 adsorption-des...Hierachically porous （HP） CuO/α-Fe2O3/SiO2 composite material was fabricated by sol-gel method and multi-hydrothermal processes using HP-SiO2 as support.The resulting material was characterized by N2 adsorption-desorption,X-ray diffraction and scanning electron microscopy.The as-prepared CuO/Fe2O3/HP-SiO2 sample,with α-Fe2O3 and CuO nanocrystals,possessed a co-continuous skeleton,through-macroporous and mesoporous structure.Its catalytic behavior for CO and o-DCB oxidation was investigated.The result showed that CuO/Fe2O3/HP-SiO2 catalyst exhibited high catalytic activity for both CO and o-DCB oxidation,indicating its potential application in combined abatement of CO and chlorinated volatile organic compounds.展开更多
The ferrites of Cuo-ZnO-Fe2o3 solid solution series near the molar ratio of ZnxCu1-x were prepared by direct heating of their coprecipitated hydroxides using NH4OH as precipitating agent where x=0.0, 0.2, 0.5, 0.8 and...The ferrites of Cuo-ZnO-Fe2o3 solid solution series near the molar ratio of ZnxCu1-x were prepared by direct heating of their coprecipitated hydroxides using NH4OH as precipitating agent where x=0.0, 0.2, 0.5, 0.8 and 1.0. Additional amounts of Cu and Zn sulphates were added to compensate the loss during the coprecipitation of the hydroxides. The ferritized samples were characterized by chemical analysis, XRD. DTA, TGA and SEM. XRD of both Zn0.2Cu0.8Fe2O4 and Zn0.5Cu0.5 Fe2O4 that indicates the formation of a heterogeneous ferrite material of ZnFe2O4 and CuFe2O4 mixed with variable amounts of α-Fe2O3. Zn and Cu ferrites were observed only in Zn0.8Cu0.2Fe2O4.From TGA-time relation, the activation energy of the different transformation phases were calculated. It is found that, the activation energy of ZnFe2O4 is slightly equal to 3/2 of that for CuFe2O4. Dielectric measurements show that the electrical behaviour depends on the ordering and disordering of the phases.展开更多
Nanocomposites of PAn-DBSA/γ-Fe 2O 3 with electrical and ferromagnetic behavior(σ= 2.18×10 -3-5.00×10 -5 S/cm, M s=3.7-16.6 m 2·A/kg, H c=8 805.2-9 133.1 A/m) were prepared by a chemical modification-...Nanocomposites of PAn-DBSA/γ-Fe 2O 3 with electrical and ferromagnetic behavior(σ= 2.18×10 -3-5.00×10 -5 S/cm, M s=3.7-16.6 m 2·A/kg, H c=8 805.2-9 133.1 A/m) were prepared by a chemical modification-redoping method in a neutral medium. The products were characterized by TEM, XRD, UV-Vis, four-probe method, and magnetometer. The results indicate that the electrical and magnetic properties of the nanocomposites strongly depend on γ-Fe 2O 3 content. With the increase of γ-Fe 2O 3 content, the electrical conductivity is decreased and saturation magnetization is increased.展开更多
Cubic and ellipsoide ultrafine monodispersed hematite colloidal particles wereprepared by hydrothermal reaction from Fe（OH）3 get in the presence of Sn4+ ions. Thenumbers of nuclei increase with the concentration of ...Cubic and ellipsoide ultrafine monodispersed hematite colloidal particles wereprepared by hydrothermal reaction from Fe（OH）3 get in the presence of Sn4+ ions. Thenumbers of nuclei increase with the concentration of Sn4+ ions. The initial concentrationof Fe（OH）3 gel might approach to 0.5 mol.L- 1. The products were characterized by TEMand XRD.展开更多
基金supported by the National Natural Science Foundation of China (No. 20977052 and 21177066)the Science and Technology Commission Foundation of Tianjin (No. 11JCYBJC05100)+1 种基金the Chinese Academy of Sciences(No. KZCX2-YW-420)the National 973 program (No. 2009CB421606)
文摘Hierachically porous （HP） CuO/α-Fe2O3/SiO2 composite material was fabricated by sol-gel method and multi-hydrothermal processes using HP-SiO2 as support.The resulting material was characterized by N2 adsorption-desorption,X-ray diffraction and scanning electron microscopy.The as-prepared CuO/Fe2O3/HP-SiO2 sample,with α-Fe2O3 and CuO nanocrystals,possessed a co-continuous skeleton,through-macroporous and mesoporous structure.Its catalytic behavior for CO and o-DCB oxidation was investigated.The result showed that CuO/Fe2O3/HP-SiO2 catalyst exhibited high catalytic activity for both CO and o-DCB oxidation,indicating its potential application in combined abatement of CO and chlorinated volatile organic compounds.
文摘The ferrites of Cuo-ZnO-Fe2o3 solid solution series near the molar ratio of ZnxCu1-x were prepared by direct heating of their coprecipitated hydroxides using NH4OH as precipitating agent where x=0.0, 0.2, 0.5, 0.8 and 1.0. Additional amounts of Cu and Zn sulphates were added to compensate the loss during the coprecipitation of the hydroxides. The ferritized samples were characterized by chemical analysis, XRD. DTA, TGA and SEM. XRD of both Zn0.2Cu0.8Fe2O4 and Zn0.5Cu0.5 Fe2O4 that indicates the formation of a heterogeneous ferrite material of ZnFe2O4 and CuFe2O4 mixed with variable amounts of α-Fe2O3. Zn and Cu ferrites were observed only in Zn0.8Cu0.2Fe2O4.From TGA-time relation, the activation energy of the different transformation phases were calculated. It is found that, the activation energy of ZnFe2O4 is slightly equal to 3/2 of that for CuFe2O4. Dielectric measurements show that the electrical behaviour depends on the ordering and disordering of the phases.
文摘Nanocomposites of PAn-DBSA/γ-Fe 2O 3 with electrical and ferromagnetic behavior(σ= 2.18×10 -3-5.00×10 -5 S/cm, M s=3.7-16.6 m 2·A/kg, H c=8 805.2-9 133.1 A/m) were prepared by a chemical modification-redoping method in a neutral medium. The products were characterized by TEM, XRD, UV-Vis, four-probe method, and magnetometer. The results indicate that the electrical and magnetic properties of the nanocomposites strongly depend on γ-Fe 2O 3 content. With the increase of γ-Fe 2O 3 content, the electrical conductivity is decreased and saturation magnetization is increased.
文摘Cubic and ellipsoide ultrafine monodispersed hematite colloidal particles wereprepared by hydrothermal reaction from Fe（OH）3 get in the presence of Sn4+ ions. Thenumbers of nuclei increase with the concentration of Sn4+ ions. The initial concentrationof Fe（OH）3 gel might approach to 0.5 mol.L- 1. The products were characterized by TEMand XRD.
基金supported by the National Natural Science Foundation of China(20976162,21103149,20906079)Natural Science Foundation of Zhejiang Province,China(R5100266)Significant Science and Technology Project of Zhejiang Province,China(2010C13001)~~