The influence of heating rate on double reversible transformation in CuZnAlMnNi shape memory alloy was investigated by differential scanning calorimetry. It was found that rapid heating inhibits X -->M transformati...The influence of heating rate on double reversible transformation in CuZnAlMnNi shape memory alloy was investigated by differential scanning calorimetry. It was found that rapid heating inhibits X -->M transformation but is favorable to the reverse martensite transformation, giving rise to the approach of the two transformation peaks. With the decrease of heating rate, the two transformation peaks separate gradually.展开更多
Microstructures of a CuZnAlMnNi shape memory alloy in the as-quenched andlong-term aged conditions were investigated by transmission electron microscopy. Aged for one yearin martensite phase, an equilibrium α-phase w...Microstructures of a CuZnAlMnNi shape memory alloy in the as-quenched andlong-term aged conditions were investigated by transmission electron microscopy. Aged for one yearin martensite phase, an equilibrium α-phase with fcc structure was observed in the M18R martensitematrix, accompanied by the appearance of a novel diffraction pattern. By analysis, it was suggestedthat the novel pattern results from the α-phase and the martensite matrix remaining in seven fineplates which produce intense secondary diffraction effect when the diffraction beams enter from onephase into another.展开更多
文摘The influence of heating rate on double reversible transformation in CuZnAlMnNi shape memory alloy was investigated by differential scanning calorimetry. It was found that rapid heating inhibits X -->M transformation but is favorable to the reverse martensite transformation, giving rise to the approach of the two transformation peaks. With the decrease of heating rate, the two transformation peaks separate gradually.
基金This project is financially supported by the Natural Science Foundation of Shandong Province ( Y2001F06) and the Fund for Outstanding Young Researcher of Shandong Province
文摘Microstructures of a CuZnAlMnNi shape memory alloy in the as-quenched andlong-term aged conditions were investigated by transmission electron microscopy. Aged for one yearin martensite phase, an equilibrium α-phase with fcc structure was observed in the M18R martensitematrix, accompanied by the appearance of a novel diffraction pattern. By analysis, it was suggestedthat the novel pattern results from the α-phase and the martensite matrix remaining in seven fineplates which produce intense secondary diffraction effect when the diffraction beams enter from onephase into another.