The ESR signal of lithium intercalated MCMB can be well simulated by combination of a Lorentz curve and a Gauss curve. The ESR intensity of the Lorentz component is essentially independent of temperature while the Gau...The ESR signal of lithium intercalated MCMB can be well simulated by combination of a Lorentz curve and a Gauss curve. The ESR intensity of the Lorentz component is essentially independent of temperature while the Gauss component shows a linear change with the reciprocal of temperature, indicative of Pauli spin and Curie spin, respectively. The former is probably associated with the ordered (graphitized) structures while the latter with the disordered structures in the sample.展开更多
NdMn_(6-x)CoxSn_6(x=0,0.2,0.4,0.6,0.8,1,1.5) were found to crystallize in the YCoeGe6 type structure.The magnetic ordering temperature(Curie temperature) and the saturation magnetization at room temperature decreases ...NdMn_(6-x)CoxSn_6(x=0,0.2,0.4,0.6,0.8,1,1.5) were found to crystallize in the YCoeGe6 type structure.The magnetic ordering temperature(Curie temperature) and the saturation magnetization at room temperature decreases with increasing Co content in NdMn_(6-x)Co_xSn_6 compounds.The spin reorientation process appears in all compounds.The spin orientation temperature increases with increasing Co content for NdMn_(3-x)Co_xSn_6.展开更多
基金the National Natural Science Foundation of China (No. 29873034) is gratefully acknowledged. We thank Professor Han Xi YANG and
文摘The ESR signal of lithium intercalated MCMB can be well simulated by combination of a Lorentz curve and a Gauss curve. The ESR intensity of the Lorentz component is essentially independent of temperature while the Gauss component shows a linear change with the reciprocal of temperature, indicative of Pauli spin and Curie spin, respectively. The former is probably associated with the ordered (graphitized) structures while the latter with the disordered structures in the sample.
文摘NdMn_(6-x)CoxSn_6(x=0,0.2,0.4,0.6,0.8,1,1.5) were found to crystallize in the YCoeGe6 type structure.The magnetic ordering temperature(Curie temperature) and the saturation magnetization at room temperature decreases with increasing Co content in NdMn_(6-x)Co_xSn_6 compounds.The spin reorientation process appears in all compounds.The spin orientation temperature increases with increasing Co content for NdMn_(3-x)Co_xSn_6.