Date palm pit(DPP)-filled poly(-hydroxybutyrate)(PHB)composites were prepared,evaluated,and characterized to determine their thermal insulation ability.Thermal conductivity values ranged between 0.086 and 0.100 W/(m&#...Date palm pit(DPP)-filled poly(-hydroxybutyrate)(PHB)composites were prepared,evaluated,and characterized to determine their thermal insulation ability.Thermal conductivity values ranged between 0.086 and 0.100 W/(m·K).At a maximum filler concentration(50%(w)),the specific heat capacity and thermal diffusivity were 1183 J/(kg·K)and 0.0689 mm^(2)/s,respec-tively.The DPP increased the thermal stability,and the highest compressive strength obtained was 80 MPa at 30%filler content.The PHB-DPP composites exhibited promising water absorption(less than 6%)and tensile strength(6-14 MPa).Date-pit-based PHB composites could be used in sustainable building engineering and cleaner production.展开更多
Date pits for feed preparation or oil extraction are soaked in water to soften before milling or extrusion. Knowledge of water absorption by the date pits helps in better managing the soaking duration. In this researc...Date pits for feed preparation or oil extraction are soaked in water to soften before milling or extrusion. Knowledge of water absorption by the date pits helps in better managing the soaking duration. In this research, the process of water absorption by date pits was modeled and analyzed using Fick's second law of diffusion, finite element approach, and Peleg model. The moisture content of the pits reached to its saturation level of 41.5% (wet basis) after 10 d. The estimated coefficient of diffusion was 9.89×10-12 m2/s. The finite element model with a proposed ellipsoid geometry for a single date pit and the analytical model fitted better to the experimental data with R2 of 0.98. The former model slightly overestimated the moisture content of the pits during the initial stages of the soaking and the latter model generally underestimated this variable through the entire stages of soaking process.展开更多
基金financially supported by UAE University (SURE+2022 Grant#G00003848).
文摘Date palm pit(DPP)-filled poly(-hydroxybutyrate)(PHB)composites were prepared,evaluated,and characterized to determine their thermal insulation ability.Thermal conductivity values ranged between 0.086 and 0.100 W/(m·K).At a maximum filler concentration(50%(w)),the specific heat capacity and thermal diffusivity were 1183 J/(kg·K)and 0.0689 mm^(2)/s,respec-tively.The DPP increased the thermal stability,and the highest compressive strength obtained was 80 MPa at 30%filler content.The PHB-DPP composites exhibited promising water absorption(less than 6%)and tensile strength(6-14 MPa).Date-pit-based PHB composites could be used in sustainable building engineering and cleaner production.
文摘Date pits for feed preparation or oil extraction are soaked in water to soften before milling or extrusion. Knowledge of water absorption by the date pits helps in better managing the soaking duration. In this research, the process of water absorption by date pits was modeled and analyzed using Fick's second law of diffusion, finite element approach, and Peleg model. The moisture content of the pits reached to its saturation level of 41.5% (wet basis) after 10 d. The estimated coefficient of diffusion was 9.89×10-12 m2/s. The finite element model with a proposed ellipsoid geometry for a single date pit and the analytical model fitted better to the experimental data with R2 of 0.98. The former model slightly overestimated the moisture content of the pits during the initial stages of the soaking and the latter model generally underestimated this variable through the entire stages of soaking process.