Double slag process was adopted to produce low-phosphorus steel from middle-phosphorus hot metal.To achieve a stable dephosphorization operation,conventional process was modified as follows：the blowing time was exten...Double slag process was adopted to produce low-phosphorus steel from middle-phosphorus hot metal.To achieve a stable dephosphorization operation,conventional process was modified as follows：the blowing time was extended by approximately 1min by reducing the oxygen supply flow rate;calcium ferrite pellets were added to adjust the slag composition and viscosity;the dumping temperature was lowered by 30-50°C by the addition of calcium ferrite pellets during the double slag process to prevent phosphorus in the slag from returning to the molten steel;and the bottom-blown gas flow was increased during the blowing process.For 40 heats of comparative experiments,the rate of dephosphorization reached 91% and ranged between 87% and 95%;the phosphorus,sulfur,manganese,and oxygen contents calculated according to the compositions of molten steel and slag as well as the temperature of molten steel at the end-point of the basic oxygen furnace process were similar to the equilibrium values for the reaction between the slag and the steel.Less free calcium oxide and metallic iron were present in the final slag,and the surface of the slag mineral phase was smooth,clear,and well developed,which showed that the slag exhibited better melting effects than that produced using the conventional slag process.A steady phosphorus capacity in the slag and stable dephosphorization effects were achieved.展开更多
The pre-reduced Bayan Obo ferroniobium（FeNb）ore concentrate block was taken as raw materials for studying the physical properties of niobium-enriched slag and changes in niobium recovery rate.In addition,the dephosp...The pre-reduced Bayan Obo ferroniobium（FeNb）ore concentrate block was taken as raw materials for studying the physical properties of niobium-enriched slag and changes in niobium recovery rate.In addition,the dephosphorization rate of the slag under different melting-separation conditions was investigated using the melting-separation test.The research results demonstrate that（i）the niobium recovery rate and dephosphorization rate of the slag decrease with the increase in melting-separation temperature;（ii）the niobium recovery rate of the slag initially increases and then decreases with increase in basicity and time;and（iii）the dephosphorization rate of the slag increases with the increase in basicity and time.When the test was performed under the conditions of basicity of 0.6-0.7,time of 7-10min,and temperature of 1400-1450°C,the niobium recovery rate and dephosphorization rate are over 96%and 95%,respectively.By scanning electron microscopy,it is observed that niobium mainly exists in the form of calcium and titanium silicate within the slag phase,with uneven distribution.展开更多
基金financially supported by the Beijing Natural Science Foundation of China(No.2172057)
文摘Double slag process was adopted to produce low-phosphorus steel from middle-phosphorus hot metal.To achieve a stable dephosphorization operation,conventional process was modified as follows：the blowing time was extended by approximately 1min by reducing the oxygen supply flow rate;calcium ferrite pellets were added to adjust the slag composition and viscosity;the dumping temperature was lowered by 30-50°C by the addition of calcium ferrite pellets during the double slag process to prevent phosphorus in the slag from returning to the molten steel;and the bottom-blown gas flow was increased during the blowing process.For 40 heats of comparative experiments,the rate of dephosphorization reached 91% and ranged between 87% and 95%;the phosphorus,sulfur,manganese,and oxygen contents calculated according to the compositions of molten steel and slag as well as the temperature of molten steel at the end-point of the basic oxygen furnace process were similar to the equilibrium values for the reaction between the slag and the steel.Less free calcium oxide and metallic iron were present in the final slag,and the surface of the slag mineral phase was smooth,clear,and well developed,which showed that the slag exhibited better melting effects than that produced using the conventional slag process.A steady phosphorus capacity in the slag and stable dephosphorization effects were achieved.
基金financially supported by the National Science and Technology Support Program (2008BAB32087)
文摘The pre-reduced Bayan Obo ferroniobium（FeNb）ore concentrate block was taken as raw materials for studying the physical properties of niobium-enriched slag and changes in niobium recovery rate.In addition,the dephosphorization rate of the slag under different melting-separation conditions was investigated using the melting-separation test.The research results demonstrate that（i）the niobium recovery rate and dephosphorization rate of the slag decrease with the increase in melting-separation temperature;（ii）the niobium recovery rate of the slag initially increases and then decreases with increase in basicity and time;and（iii）the dephosphorization rate of the slag increases with the increase in basicity and time.When the test was performed under the conditions of basicity of 0.6-0.7,time of 7-10min,and temperature of 1400-1450°C,the niobium recovery rate and dephosphorization rate are over 96%and 95%,respectively.By scanning electron microscopy,it is observed that niobium mainly exists in the form of calcium and titanium silicate within the slag phase,with uneven distribution.