Fatigue test was carried out on AZ31B magnesium alloy. Under 2×10 6 cycle times, the fatigue strengths of base metal （BM）, butt joint （BJ）, transverse cross joint （TJ）, lateral connection joint （LJ） are 6...Fatigue test was carried out on AZ31B magnesium alloy. Under 2×10 6 cycle times, the fatigue strengths of base metal （BM）, butt joint （BJ）, transverse cross joint （TJ）, lateral connection joint （LJ） are 66.72, 39.00, 24.38 and 24.40 MPa, respectively. The crack propagation behavior of the alloy was analyzed by optical microscopy. The AZ31B magnesium alloy base metal has a smooth crack propagation macroscopic path. However, the microscopic path is twisted and some cracks have two forks, and the crack propagation is transgranular. The crack initiates in the weld toe and the crack propagates along the HAZ for the BJ and TJ; for the LJ crack initiates in the fillet weld leg. The fatigue fracture mechanisms were analyzed by SEM. The fatigue fracture surface consists of quasi-cleavage patterns or cleavage step and a brittle fracture occurs. Numerous secondary cracks are observed; some fatigue striations exist in butt joint and its size is about 5 μm.展开更多
The fatigue crack propagation rate of as-extruded AZ31B magnesium alloy was studied. Compact tension [C（T）] of the notch direction parallel （T-L）, vertical （L-T）, and inclined at 45o to the extrusion direction w...The fatigue crack propagation rate of as-extruded AZ31B magnesium alloy was studied. Compact tension [C（T）] of the notch direction parallel （T-L）, vertical （L-T）, and inclined at 45o to the extrusion direction was investigated. The experimental results indicate that the crack propagation direction is parallel to the extrusion direction for T-L and L-T specimens, whereas the specimen inclined at 45o has an angular deflection of 9° to 11° toward the extrusion direction. The T-L specimen has the fastest fatigue crack propagation rate, and the L-T specimen has the slowest rate, the fatigue crack propagation rate of the specimen inclined at 45o is between the two directions. The crack tip propagates by both transgranular and intergranular fractures. Fatigue fractures consist of cleavage plane or quasi-cleavage and are brittle fractures. The fatigue striation occurs for specimens inclined at 45o and its size is 3-15 μm.展开更多
The effect of addition of different concentrations of Ce on high-cycle fatigue behavior of die-cast magnesium alloy AZ91D was investigated. Mechanical fatigue tests were conducted at the stress ratio of R = 0.1, and f...The effect of addition of different concentrations of Ce on high-cycle fatigue behavior of die-cast magnesium alloy AZ91D was investigated. Mechanical fatigue tests were conducted at the stress ratio of R = 0.1, and fatigue strength was evaluated using up-and-down loading method. The results show that the grain size of AZ91D alloy is remarkably refined, and the amount of porosity decreases and evenly distributes with the addition of Ce. The fatigue strength of AZ91D alloy at room temperature increases from 96.7 up to 116.3 MPa （ 1% Ce） and 105.5 MPa （2 % Ce）, respectively, at the number of cycles to failure, Nf = 1 × 10^7. The fatigue crack of AZ91D alloy initiates at porosities and inclusions, and propagates along grain boundaries. The fatigue striations on fractured surface appear with Ce addition. The fatigue fracture surface of test specimens shows mixed-fracture characteristics of quasi-cleavage and dimple.展开更多
基金Project(50675148)supported by the National Natural Science Foundation of China
文摘Fatigue test was carried out on AZ31B magnesium alloy. Under 2×10 6 cycle times, the fatigue strengths of base metal （BM）, butt joint （BJ）, transverse cross joint （TJ）, lateral connection joint （LJ） are 66.72, 39.00, 24.38 and 24.40 MPa, respectively. The crack propagation behavior of the alloy was analyzed by optical microscopy. The AZ31B magnesium alloy base metal has a smooth crack propagation macroscopic path. However, the microscopic path is twisted and some cracks have two forks, and the crack propagation is transgranular. The crack initiates in the weld toe and the crack propagates along the HAZ for the BJ and TJ; for the LJ crack initiates in the fillet weld leg. The fatigue fracture mechanisms were analyzed by SEM. The fatigue fracture surface consists of quasi-cleavage patterns or cleavage step and a brittle fracture occurs. Numerous secondary cracks are observed; some fatigue striations exist in butt joint and its size is about 5 μm.
基金Funded by the National Natural Science Foundation of China(No. 50675148)
文摘The fatigue crack propagation rate of as-extruded AZ31B magnesium alloy was studied. Compact tension [C（T）] of the notch direction parallel （T-L）, vertical （L-T）, and inclined at 45o to the extrusion direction was investigated. The experimental results indicate that the crack propagation direction is parallel to the extrusion direction for T-L and L-T specimens, whereas the specimen inclined at 45o has an angular deflection of 9° to 11° toward the extrusion direction. The T-L specimen has the fastest fatigue crack propagation rate, and the L-T specimen has the slowest rate, the fatigue crack propagation rate of the specimen inclined at 45o is between the two directions. The crack tip propagates by both transgranular and intergranular fractures. Fatigue fractures consist of cleavage plane or quasi-cleavage and are brittle fractures. The fatigue striation occurs for specimens inclined at 45o and its size is 3-15 μm.
基金Project supported bythe Key Technologies Fifteen R &D Programme (2001BA311A07-2) 985-Automotive Engineering ofJilin University
文摘The effect of addition of different concentrations of Ce on high-cycle fatigue behavior of die-cast magnesium alloy AZ91D was investigated. Mechanical fatigue tests were conducted at the stress ratio of R = 0.1, and fatigue strength was evaluated using up-and-down loading method. The results show that the grain size of AZ91D alloy is remarkably refined, and the amount of porosity decreases and evenly distributes with the addition of Ce. The fatigue strength of AZ91D alloy at room temperature increases from 96.7 up to 116.3 MPa （ 1% Ce） and 105.5 MPa （2 % Ce）, respectively, at the number of cycles to failure, Nf = 1 × 10^7. The fatigue crack of AZ91D alloy initiates at porosities and inclusions, and propagates along grain boundaries. The fatigue striations on fractured surface appear with Ce addition. The fatigue fracture surface of test specimens shows mixed-fracture characteristics of quasi-cleavage and dimple.