高固溶Al-7Mg合金高温拉伸行为及本构方程研究

光学显微镜(OM)及透射电子显微镜(TEM)研究发现热挤压制备的高固溶Al-7Mg合金由均匀粗晶粒组成,平均尺寸约为16μm,基体中没有检测到第二相。通过设计不同变形参数的高温拉伸实验,探索了Al-7Mg合金高温拉伸变形行为。其中,断裂延伸率随温度的升高而提高。较粗的晶粒导致该合金在400℃拉伸时的断裂延伸率约为200%。应变速率敏感系数(0.16~0.31)及变形激活能(124 kJ/mol)计算结果表明随拉伸温度由200℃提高至400℃,Al-7Mg合金的变形机制由位错滑移/蠕变转变为溶质拖拽蠕变,该过程由晶格扩散控制。通过峰值应变处应力值的系统分析,构建了用于预测Al-7Mg合金高温拉伸峰值应力的本构方程。

Effect of characteristics and distribution of Mg_(17)Al_(12)precipitates on tensile and bending properties of high-Al-containing Mg alloys

This study investigates the effect of characteristics and distribution of Mg_(17)Al_(12)precipitates on the uniaxial tensile and three-point bending properties of extruded Mg alloys containing high Al contents.The extruded Mg–9Al–1Zn–0.3Mn(AZ91)alloy contains lamellar-structured Mg_(17)Al_(12)discontinuous precipitates along the grain boundaries,which are formed via static precipitation during natural air cooling.The extruded Mg–11Al–1Zn–0.3Mn(AZ111)alloy contains spherical Mg_(17)Al_(12)precipitates at the grain boundaries and inside the grains,which are formed via dynamic precipitation during extrusion.Due to inhomogeneous distribution of precipitates,the AZ111 alloy consists of two different precipitate regions:precipitate-rich region with numerous precipitates and finer grains and precipitate-scarce region with a few precipitates and coarser grains.The AZ111 alloy exhibits a higher tensile strength than the AZ91 alloy because its smaller grain size and more abundant precipitates result in stronger grain-boundary hardening and precipitation hardening effects,respectively.However,the tensile elongation of the AZ111 alloy is lower than that of the AZ91 alloy because the weak cohesion between the dynamic precipitates and the matrix facilitates the crack initiation and propagation.During bending,a macrocrack initiates on the outer surface of bending specimen in both alloys.The AZ111 alloy exhibits higher bending yield strength and lower failure bending strain than the AZ91 alloy.The bending specimens of the AZ91 alloy have similar bending formability,whereas those of the AZ111 alloy exhibit considerable differences in bending formability and crack propagation behavior,depending on the distribution and number density of precipitates in the specimen.In bending specimens of the AZ111 alloy,it is found that the failure bending strain(ε_(f,bending))is inversely proportional to the area fraction of precipitates in the outer zone of bending specimen(A_(ppt)),with a relationship ofε_(f,bending)=–0.1A_(ppt)+5.86.

Synergistic effect of gradient Zn content and multiscale particles on the mechanical properties of Al-Zn-Mg-Cu alloys with coupling distribution of coarse-fine grains

This study investigated the influence of graded Zn content on the evolution of precipitated and iron-rich phases and grain struc-ture of the alloys,designed and developed the Al–8.0Zn–1.5Mg–1.5Cu–0.2Fe(wt%)alloy with high strength and formability.With the increase of Zn content,forming the coupling distribution of multiscale precipitates and iron-rich phases with a reasonable matching ratio and dispersion distribution characteristics is easy.This phenomenon induces the formation of cell-like structures with alternate distribu-tion of coarse and fine grains,and the average plasticity–strain ratio(characterizing the formability)of the pre-aged alloy with a high strength is up to 0.708.Results reveal the evolution and influence mechanisms of multiscale second-phase particles and the corresponding high formability mechanism of the alloys.The developed coupling control process exhibits considerable potential,revealing remarkable improvements in the room temperature formability of high-strength Al–Zn–Mg–Cu alloys.

Effect of cold rolling deformation on microstructure evolution and mechanical properties of spray formed Al−Zn−Mg−Cu−Cr alloys

The impact of cold rolling deformation,which was introduced after solid solution and before aging treatment,on microstructure evolution and mechanical properties of the as-extruded spray formed Al−9.8Zn−2.3Mg−1.73Cu−0.13Cr(wt.%)alloy,was investigated.SEM,TEM,and EBSD were used to analyze the microstructures,and tensile tests were conducted to assess mechanical properties.The results indicate that the D1-T6 sample,subjected to 25%cold rolling deformation,exhibits finer grains(3.35μm)compared to the D0-T6 sample(grain size of 4.23μm)without cold rolling.Cold rolling refines the grains that grow in solution treatment.Due to the combined effects of finer and more dispersed precipitates,higher dislocation density and smaller grains,the yield strength and ultimate tensile strength of the D1-T6 sample can reach 663 and 737 MPa,respectively.In comparison to the as-extruded and D0-T6 samples,the yield strength of the D1-T6 sample increases by 415 and 92 MPa,respectively.

Improvement of microstructure and mechanical properties of Al−Cu−Li−Mg−Zn alloys through water-cooling centrifugal casting technique

The microstructure and mechanical properties of as-cast Al−Cu−Li−Mg−Zn alloys fabricated by conventional gravity casting and centrifugal casting techniques combined with rapid solidification were investigated.Experimental results demonstrated that compared with the gravity casting technique,the water-cooling centrifugal casting technique significantly reduces porosity,refinesα(Al)grains and secondary phases,modifies the morphology of secondary phases,and mitigates both macro-and micro-segregation.These improvements arise from the synergistic effects of the vigorous backflow,centrifugal field,vibration and rapid solidification.Porosity and coarse plate-like Al13Fe4/Al7Cu2Fe phase result in the fracture before the gravity-cast alloy reaches the yield point.The centrifugal-cast alloy,however,exhibits an ultra-high yield strength of 292.0 MPa and a moderate elongation of 6.1%.This high yield strength is attributed to solid solution strengthening(SSS)of 225.3 MPa,and grain boundary strengthening(GBS)of 35.7 MPa.Li contributes the most to SSS with a scaling factor of 7.9 MPa·wt.%^(-1).The elongation of the centrifugal-cast alloy can be effectively enhanced by reducing the porosity and segregation behavior,refining the microstructure and changing the morphology of secondary phases.

Dissimilar Al/Mg alloys friction stir lap welding with Zn foil assisted by ultrasonic

The Zn-added ultrasonic assisted friction stir lap welding(UaFSLW) was carried out to improve the quality of dissimilar Al/Mg alloys joint. The effects of ultrasonic power on the joint quality were also investigated.The results indicated that the larger effective lap width and mixing region between Mg and Al(Mg/Al MR) were attained by Zn foil addition and external ultrasonic assistance. Compared with the conventional joint, the finer and better-distributed Mg-Zn IMCs placing the continuous Al-Mg IMCs were formed in the Mg/Al MR of the Zn-added UaFSLW joint. The Zn foil addition and external ultrasonic assistance significantly improved the tensile shear load of the joint, and the load was increased with the increase of the ultrasonic power. The maximum tensile shear load of 7.95 kN was attained, which was 52.6% larger than that of the conventional joint.

Numerical simulation and experimental study of hybrid laser-electric arc welding between dissimilar Mg alloys

This work aims to establish a suitable numerical simulation model for hybrid laser-electric arc heat source welding of dissimilar Mg alloys between AZ31 and AZ80. Based on the energy conservation law and Fourier’s law of heat conduction, the differential equations of the three-dimensional temperature field for nonlinear transient heat conduction are built. According to the analysis of nonlinear transient heat transfer, the equations representing initial conditions and boundary conditions are obtained. The “double ellipsoidal heat source + 3D Gaussian heat source”combination was chosen to construct the laser-electric arc hybrid heat source. The weld bead morphologies and the distribution of temperature, stress, displacement and plastic strains are numerically simulated. The actual welding experiments were performed by a hybrid laser-electric arc welding machine. The interaction mechanism between laser and electric arc in the hybrid welding of Mg alloys is discussed in detail. The hybrid heat source can promote the absorption of laser energy and electric arc in the molten pool, resulting in more uniform energy distribution in the molten pool and the corresponding improvement of welding parameters. This work can provide theoretical guidance and data supports for the optimization of the hybrid laser-electric arc welding processes for Mg alloys.

Al-Mg系合金中合金化元素作用及其对力学性能的影响

铝镁合金是轻量化材料应用领域中一种重要的金属材料,属于中高强度铝合金,具有较高的塑性、良好的耐蚀性以及优良的焊接性等优势,目前在航空航天、交通运输和军工制造等领域具有广阔的应用前景。笔者综述了铝镁合金力学性能特点以及用途,介绍了Al-Mg系合金中的强化机制,重点阐述了Al-Mg系合金中主合金化元素Mg及其含量对合金微观组织和力学性能的影响规律及机理,详细论述了Mn、Zr、Ti、Sc、Er、Y等微合金化元素的作用以及对Al-Mg系合金微观组织和力学性能的影响规律。最后,结合Al-Mg系合金当前研究现状,提出了今后值得研究的方向。

Mn微合金化Al-Si-Cu-Mg合金显微组织及耐蚀性能研究

Al-Si-Cu-Mg系列合金具有优异的强韧性,但其中的含Cu强化相极大地影响了该系合金的耐蚀性能。因此,本文通过对不同Mn含量的Al-7Si-2Cu-0.6Mg合金进行显微组织观察和电化学分析,探究Mn元素的添加对T6热处理状态下合金微观结构和耐蚀性的影响。结果表明,Mn添加量的提高对合金显微硬度几乎没有影响,但在合金基体中可以观察到弥散相。随着Mn含量升高,合金的耐蚀性呈现先升高后降低的趋势。添加0.360%Mn(质量分数)合金具有最佳耐蚀性,腐蚀电流密度比基础合金减少了54%。腐蚀形貌观察结果表明,Mn的添加可以显著减弱合金的点蚀趋势。

通过不同热挤压方式制备具有较优强塑性组合的新型Mg-5Sn-2Al-1Zn合金

制备新型Mg-5Sn-2Al-1Zn(TAZ521)合金。为提高合金的强度与塑性,采用正挤压(DE)和挤压-剪切(ES)两种工艺对该合金进行变形处理。通过XRD、SEM、TEM、EBSD和拉伸试验等方法研究均匀态和挤压态合金的显微组织演变、织构演变及强化机制。结果表明,正挤压态合金的力学性能得到改善;然而,合金表现出由粗晶和细小动态再结晶(DRXed)晶粒组成的双峰组织。经过挤压-剪切变形后的合金组织变得更加均匀,并且实现更好的强韧性结合,变形后合金的屈服强度(YS)、极限抗拉强度(UTS)和伸长率(EL)分别达到212 MPa、303 MPa和21.7%。晶粒细化和Mg2Sn析出物的钉扎效应对强度的提高起到重要作用,此外,延展性的提高归因于基面纤维织构的弱化和非基面滑移系的激活。

基于冷喷涂工艺的Mg-Zn-Al-Sn-Mn合金防腐Al涂层制备

采用冷喷涂技术在Mg-Zn-Al-Sn-Mn合金表面制备Al涂层,以提高其耐腐蚀性能。研究工作气体温度和压力对Al涂层显微组织和腐蚀行为的影响。结果表明,随着气体温度和压力的升高,Al涂层的致密度和厚度均明显增加。高的气体温度能降低颗粒沉积的临界速度,并提高沉积效率。高的气体压力不仅提升机械结合质量,而且对沉积的涂层具有较强的夯实作用。由于孔隙的减少,Al涂层的耐蚀性随着气体温度和压力的升高而提高。Al(OH)_(3)和Al_(2)O_(3)等腐蚀产物可以堵塞涂层中的孔隙,并作为阻碍腐蚀的物理屏障,从而有效保护Mg合金免受腐蚀。

均匀化退火对Al-8Zn-1.2Mg-1.5Cu合金显微组织和力学性能的影响

通过半固态电磁搅拌铸造法制备了Al-8Zn-1.2Mg-1.5Cu合金,并对其进行均匀化退火处理。采用光学显微镜、X射线衍射仪、扫描电镜、金属涡流电导仪和维氏硬度计等对合金组织和性能进行分析与测试。结果表明:铸态Al-8Zn-1.2Mg-1.5Cu合金的组织主要由α-Al基体和MgZn_(2)相组成,并存在严重的枝晶偏析;随着均匀化退火温度从400℃升高到460℃,粗大的网状枝晶组织逐渐消失,MgZn_(2)和非平衡共晶相逐渐溶入α-Al基体中,合金的硬度和电导率先增大后减小,在440℃退火保温12 h后硬度达到最大值,为134.8 HV0.3;在460℃均匀化退火时,随着保温时间从6 h增加到24 h,合金中的共晶组织不断溶解,硬度先增大后减小,在保温时间为18 h时达到最大值,为131.7 HV0.3,合金的电导率则是呈先下降再上升随后下降的趋势。

激光熔化沉积Al-Mg-Sc-Zr合金晶粒尺寸预测及成形工艺优化

通过激光熔化沉积试验分析了工艺条件(送粉速度、扫描速度和激光功率)对Al-Mg-Sc-Zr合金晶粒尺寸的影响,构建了晶粒尺寸预测模型,优化了成形工艺参数,给出了工艺参数最佳区间。结果表明,相较于激光功率和扫描速度,送粉速度对晶粒尺寸的影响最为显著;随着成形能量密度的增加,合金晶粒尺寸呈现出先减小后增大的演变趋势;采用回归方程构建的晶粒尺寸-工艺参数关系模型能准确预测不同工艺条件下激光熔化沉积Al-Mg-Sc-Zr合金的平均晶粒尺寸,相对误差小于2%;通过响应面分析得到工艺参数最佳区间为:送粉速度2.8~3 g·min^(-1)、激光功率1000~1050 W、扫描速度4~5 mm·s^(-1)。

碳纳米管增韧Al-Mg合金复合材料的制备与性能研究

选择碳纳米管为增强相,通过搅拌铸造法制备了碳纳米管增韧Al-Mg合金复合材料,研究了碳纳米管的添加量对复合材料力学性能、微观组织以及韧性的影响,并探究了碳纳米管对Al-Mg合金的增韧机理。结果表明,掺入适量的碳纳米管后细化了Al-Mg合金复合材料的晶粒,晶粒尺寸约为80μm,当碳纳米管的添加量为0.8%(质量分数)时,复合材料的断口形貌最均匀。随着碳纳米管添加量的增大,复合材料的抗拉强度、断裂伸长率、硬度均表现出先增大后降低的趋势,当碳纳米管的添加量为0.8%(质量分数)时,抗拉强度、断裂伸长率和硬度均达到了最大值,分别为208.6 MPa、15.8%和53.1 HB。适量碳纳米管的添加显著改善了Al-Mg合金的韧性,使断裂延伸率逐渐增大,屈服阶段延长,韧性得到提高,这是因为适量的碳纳米管添加后能够与合金发生较好的结合,并贯穿于合金的裂纹中,发挥出了桥联作用,阻碍了裂纹的萌生和扩展,从而改善了Al-Mg合金复合材料的韧性,延缓了合金的失效过程,延长了合金的屈服阶段。综上分析可知,碳纳米管的最佳添加量为0.8%(质量分数)。

热挤压对快速凝固Al-Si-Fe-Cu-Mg合金显微组织及性能的影响

采用单辊旋淬法制备了快速凝固Al-20Si-5Fe-Cu-Mg合金,采用了SEM对其进行观察分析。结果表明,快速凝固能够极大细化Al-20Si-5Fe-Cu-Mg合金组织,抑制Si相及β-Fe相的析出长大,且组织的细化程度呈梯度分布。对快速凝固Al-20Si-5Fe-Cu-Mg合金进行了不同工艺参数的热挤压实验。结果表明,粉末包套热挤压工艺能够使快速凝固Al-20Si-5Fe-Cu-Mg带材合金致密化,当挤压温度为400℃、挤压比为1∶16时,合金获得了较优异的力学性能,其屈服强度和抗拉强度分别达到了456 MPa和805 MPa,压缩率为9.3%。

高强Al-Zn-Mg-Cu合金静态再结晶模型及组织演变

采用Gleeble 3800热模拟试验机对航空用Al-Zn-Mg-Cu合金的热变形行为进行了测试,对变形后的微观组织进行了表征,系统分析了静态软化行为,建立了静态再结晶动力学模型。结果表明:实验用航空Al-Zn-Mg-Cu合金的静态再结晶激活能为129162 J·mol^(-1),静态再结晶体积分数受变形温度、变形程度、变形速率的影响,且变形温度对静态再结晶影响最明显;变形速率一定时,变形温度越高,道次停留时间的影响越不明显;350℃低温变形后,α-Al基体晶粒内部仍存在大量的位错缠结;400℃中温变形后,位错运动能够充分进行,部分晶粒发生了再结晶;450℃高温变形后,基体晶粒基本全部完成了再结晶,基体晶粒内部发现5~25 nm尺寸范围的Al-Zn-Mg-Cu四元相粒子;对于不同热变形条件,模型预测值的误差在0.008~0.0625范围内,动力学模型的计算结果精确度较高。

T6态热挤压Al-5Cu-0.8Mg-0.15Zr-0.2Sc-0.5Ag合金的低周疲劳行为

为了揭示经过T6处理的热挤压Al-5Cu-0.8Mg-0.15Zr-0.2Sc-0.5Ag合金在不同温度下的低周疲劳变形与断裂行为,对T6态热挤压合金进行了室温和200℃条件下的低周疲劳实验。结果表明:在室温和200℃下合金塑性应变幅与载荷反向周次之间服从Coffin-Manson公式,而弹性应变幅与载荷反向周次之间服从Basquin公式;合金在室温和200℃下低周疲劳变形时,在较低外加总应变幅下疲劳变形机制主要为平面滑移,而在较高外加总应变幅下疲劳变形机制主要为波状滑移;室温和200℃下合金的疲劳裂纹均萌生于疲劳试样表面并以穿晶方式扩展。

Zr对Al-Si-Mg-Mn合金凝固过程、时效组织和性能的影响

通过模拟计算、组织观察以及力学性能测试,研究了不同Zr含量对铸造Al-Si-Mg-Mn合金凝固过程、时效组织及力学性能的影响。结果表明,随着Zr含量增加,合金凝固路径存在显著差异,晶粒由初期树枝晶逐步演变为等轴晶;175℃时效7 h条件下,Zr的加入显著提高合金硬度。Zr的加入促使析出相在更低时效温度析出,这可能是Zr细化了晶粒从而提高了扩散效率。峰值时效时合金主要析出相为β″相和Q′相。

激光选区熔化Al-Mg-Sc-Zr合金各向组织与损伤容限性能

研究激光选区熔化(selective laser melting,SLM)技术成形Al-Mg-Sc-Zr合金材料不同取向的显微组织特征、拉伸和损伤容限性能。结果表明:YZ截面为细小的等轴晶和粗大的柱状晶组成的双峰组织,XY截面由细小的等轴晶组成;0°和90°方向屈服强度、抗拉强度均超过500 MPa,各向异性较小,但堆积层间存在的未熔合缺陷使得90°方向断裂伸长率明显低于0°方向;0°和90°CT试样K_(IC)分别为21.41 MPa·m^(1/2)和20.89 MPa·m^(1/2),在柱状晶区域裂纹扩展阻抗低,导致90°CT试样K_(IC)稍小;显微组织和缺陷是影响裂纹扩展性能各向异性的主要因素,在近门槛区未熔合缺陷起主导作用,当裂纹面平行于水平方向时裂纹扩展速率更快;在稳态扩展区显微组织的影响起主导作用,当裂纹面平行于水平方向时为穿晶断裂,裂纹扩展阻抗较高,裂纹扩展速率较低。

基于机器学习的Al-Zn-Mg-Cu合金快速设计

提出一种基于机器学习的合金快速设计系统(ARDS),以定制所需性能的合金制备策略或预测制备策略所对应的合金性能。为此,分别对3种回归算法:线性回归(LR)、支持向量回归(SVR)和人工神经网络(BPNN)进行建模和比较以训练多性能预测模型。其中,应用SVR构建的机器学习模型被证明是最佳的。然后,基于生成对抗网络(GAN)模型原理,构建Al-Zn-Mg-Cu系铝合金快速设计系统(ARDS)。对ARDS的预测可靠性进行验证。结果表明,为了能够获得准确的制备策略,系统中极限抗拉强度(UTS)、屈服强度(YS)和伸长率(EL)的输入上限分别约为790 MPa、730 MPa和28%。此外,基于ARDS预测结果,制备了一种性能优异的新型铝合金材料,其UTS为764 MPa、YS为732 MPa、EL为10.1%,进一步验证了ARDS的可靠性。