Experimental investigation of the effects of oil asphaltene content on CO_(2) foam stability in the presence of nanoparticles and sodium dodecyl sulfate

Foam stability tests were performed using sodium dodecyl sulfate(SDS)surfactant and SiO2 nanoparticles as foaming system at different asphaltene concentrations,and the half-life of CO_(2) foam was measured.The mechanism of foam stability reduction in the presence of asphaltene was analyzed by scanning electron microscope(SEM),UV adsorption spectrophotometric concentration measurement and Zeta potential measurement.When the mass ratio of synthetic oil to foam-formation suspension was 1:9 and the asphaltene mass fraction increased from 0 to 15%,the half-life of SDS-stabilized foams decreased from 751 s to 239 s,and the half-life of SDS/silica-stabilized foams decreased from 912 s to 298 s.When the mass ratio of synthetic oil to foam-formation suspension was 2:8 and the asphaltene mass fraction increased from 0 to 15%,the half-life of SDS-stabilized foams decreased from 526 s to 171 s,and the half-life of SDS/silica-stabilized foams decreased from 660 s to 205 s.In addition,due to asphaltene-SDS/silica interaction in the aqueous phase,the absolute value of Zeta potential decreases,and the surface charges of particles reduce,leading to the reduction of repulsive forces between two interfaces of thin liquid film,which in turn,damages the foam stability.

Sodium dodecyl sulfate (SDS) as an effective corrosion inhibitor for Mg-8Li-3Al alloy in aqueous NaCl: A combined experimental and theoretical investigation

The corrosion inhibition behavior of Mg-8Li-3Al alloy in NaCl solution with sodium dodecyl sulfate(SDS)was investigated by hydrogen analysis,scanning electron microscopy(SEM),electrochemical test,scanning Kelvin probe force microscopy(SKPFM)and computational methods.Results showed that the corrosion resistance of Mg-8Li-3Al alloy in NaCl solution was effectively improved with SDS.The SEM and SKPFM results confirmed a dense,200 nm-thick SDS-adsorbed layer had formed on the alloy surface.The separation energy ΔE_(gap) and adsorption energy E_(ads) of SDS on the Mg surface were calculated by density functional theory and molecular dynamics simulations,respectively.And the corrosion inhibition mechanism was hypothesized and described.

Curing of the Bacillus subtilis Plasmid Using Sodium Dodecyl Sulfate

Curing of Bacillus subtilis plasmid using sodium dodecyl sulfate (SDS)was studied in order to obtain a host strain. An overnight culture of Bacillus subtilis 24/pMX45 was used to inoculate fresh LB containing SDS (0-0.008%). No growth of 24/pMX45 was observed when LB contained an SDS concentration of 0.006% or greater, and the sublethal concentration (w/v) of SDS was 0.005% with a killing rate of 99%. Samples were diluted and plated on LB agar, individual colonies were randomly picked to a selective agar medium by tooth to screen for loss of plasmid-encoded erythomycin resistance. CsCl-EtBr gradient centrifugation and plasmid DNA profile demonstrated that plasmid-cured derivative A7 has completely lost its plasmid. A7 had a shorter lag, and its cell concentration was consistently higher than that of the 24/pMX45. Elimination of the plasmid was first observed after 24/pMX45 had been treated with SDS for 8 h. The percent elimination then continued to increase until about 22 h, after which the fraction of cured cell in the population remained constant. Plasmid cured cell numbers were measured in a separate control culture of 24/pMX45 untreated by SDS. No spontaneous loss of pMX45 was observed after 24/pMX45 were incubated for 24 h and 48 h with shaking at 37 ℃.These results suggested that SDS can be used as curing agent to eliminate the plasmid of Bacillus subtilis.

Intermolecular Interactions in Self-Assembly Process of Sodium Dodecyl Sulfate by Vertically Polarized Raman Spectra

Molecular self-assembly is extremely important in many fields, but the characterization of their corresponding intermolecular interactions is still lacking. The C-H stretching Raman band can reflect the hydrophobic interactions during the self-assembly process of sodium dodecyl sulfate （SDS） in aqueous solutions. However, the Raman spectra in this region are seriously overlapped by the OH stretching band of water. In this work, vertically polarized Raman spectra were used to improve the detection sensitivity of spectra of C-H region for the first time. The spectral results showed that the first critical micelle concentration and the second critical micelle concentration of SDS in water were 8.5 and 69 mmol/L, respectively, which were consistent with the results given by surface tension measurements. Because of the high sensitivity of vertically polarized Raman spectra, the critical micelle concentration of SDS in a relatively high concentration of salt solution could be obtained in our experiment. The two critical concentrations of SDS in 100 mmol/L NaCl solution were recorded to be 1.8 and 16.5 mmol/L, respectively. Through comparing the spectra and surface tension of SDS in water and in NaCl solution, the self-assembly process in bulk phase and at interface were discussed. The interactions among salt ions, SDS and water molecules were also analyzed. These results demonstrated the vertically polarized Raman spectra could be employed to study the self-assembly process of SDS in water.

Enhancing the leaching effect of an ion-absorbed rare earth ore by ameliorating the seepage effect with sodium dodecyl sulfate surfactant

Ameliorating the problem of low leaching efficiency,long leaching period,and high agent consumption should be studied to efficiently exploit ion-absorbed rare earth ore resources.In this study,the surfactant sodium dodecyl sulfate(SDS) is used to enhance the leaching effect of an ion-absorbed rare earth ore by ameliorating the seepage effect for the first time.The effects of surfactant concentration,leaching agent dosage,solution flow velocity,and solution pH on the leaching rate were explored,and the mechanism of SDS was discussed.Under the optimum conditions,the addition of a small amount of SDS(mass fraction0.04%) can increase the leaching rate by about 5%,shorten the leaching period,and reduce the consumption of the leaching agent.SDS significantly ameliorates the seepage effect of the ore body by reducing the surface tension of the leaching agent and ameliorating the wettability of the mineral surface.This effect is the main factor that improves the leaching efficiency.DFT(density functional theory) calculation results show that SDS can react with rare earth ions,which reduces the adsorption strength on clay mineral surfaces.Hence,rare earth ions are easily exchanged by ammonium ions,and mass transfer is enhanced.

Effects of BaCl_2 on K-feldspar flotation using dodecyl amine chloride under natural pH

The effects of BaCl2 on the flotation of K-feldspar using dodecyl amine chloride as the collector under natural pH wereinvestigated by flotation tests, absorption measurements, Fourier transform infrared spectroscopy （FTIR） and X-ray photoelectronspectroscopy （XPS）. The results indicated that lower BaCl2 concentration can increase the floatability of K-feldspar, whereas higherBaCl2 concentration can significantly inhibit the flotation of K-feldspar. Peaks at 3548.18, 3475.56 and 3414.35 cm？1in the FTIRspectra of K-feldspar adsorbed by dodecyl amine chloride revealed three forms of -OH. XPS analyses of K-feldspar adsorbed byBa2＋ showed that the concentration of K atom was reduced by nearly twice as those of Si, Al, and O. The activation of BaCl2 at a lowconcentration was mainly caused by Ba2＋ in the form of the ion exchange between K＋ and Ba2＋. The inhibitory action of BaCl2 at ahigh concentration is mainly attributed to the physical absorption of Ba2＋ on the surface of K-feldspar and the fact that a highconcentration of Cl？ causes the chemical equilibrium of dodecyl amine chloride to be changed, and the dodecyl amine chloride in theform of RNH2H＋ is reduced.

Synthesis and Kinetics of Hydrogenated Rosin Dodecyl Ester as an Environmentally Friendly Plasticizer

The plasticizer is an important polymer material additive.Non-toxic and environmentally friendly plasticizers are developed recently in order to decrease fossil fuel reserves,serious environmental pollution and the toxicity of phthalate esters.In this study,a new,efficient and environmentally friendly plasticizer of hydrogenated rosin dodecyl ester was prepared by an esterification reaction of hydrogenated rosin and dodecanol.The influences of different reaction conditions(including different catalysts,the catalyst concentration,the ratio of the reactants,reaction temperature,and reaction time)on the esterification yield are examined and discussed.Hydrogenated rosin dodecyl ester with 71.8%yield was synthesized under the optimized reaction conditions(1:0.8 molar ratio of rosin to dodecanol,1 mol%tetrabutyl titanate concentration,and 210℃for 6 h).The esterification reaction is a second-order reaction,and kinetic calculations showed that the activation energy is 39.77 KJ·mol^(−1).The structure of the hydrogenated rosin dodecyl ester was confirmed by FT-IR spectroscopy and^(13)C NMR spectrum.Besides,the thermal stability of target product(hydrogenated rosin dodecyl ester)was also tested by thermal gravimetric analysis(TGA),which showed a good thermal stability.

Interaction of ciprofloxacin hydrochloride with sodium dodecyl sulfate in aqueous/electrolytes solution at different temperatures and compositions

Interactions of ciprofloxacin hydrochloride(CPFH)with sodium dodecyl sulfate(SDS)were investigated by conductivity measurement in H2O/electrolyte solutions(NaCl,Na2SO4&Na3PO4)over 298.15–318.15 K temperature range(with 5 K interval)considering the human body temperature.In all cases,two critical micelle concentrations(c*)were observed which are increased in the presence of drug and decreased in the presence of salts enunciating the presence of interaction amongst the studied components.For(CPFH+SDS)system in the presence of salt,the c*values at 303.15 K and I=0.50 mmol·kg^-1 followed the order:CNaCl>CNa2SO4>CNa3PO4.TheΔG1,m0 andΔG2,m0values are found to be negative for all systems that show that the micellization process is thermodynamically spontaneous.For(CPFH+SDS)system in water,theΔHm0&ΔSm0 values reveal that the micellization processes is both entropy dominated in almost all cases.In the occurrence of electrolytes,ΔHm0 andΔSm0 values indicate that micellization processes are both entropy&enthalpy restricted at upper temperature but it becomes totally entropy dependent at higher temperature.The higher positiveΔSm0 values indicate the enhanced hydrophobic interaction in presence of salts.The enthalpy-entropy compensation was determined from the linear relationship betweenΔHm0 andΔSm0 values in every state.Different transfer energies as well as compensation temperature and intrinsic enthalpy were also evaluated and the behaviors were comparable to other biological system.

Phase Behavior of Sodium Dodecyl Sulfate-n-Butanol-Kerosene-Water Microemulsion System

Experiments were carried out to investigate the influences of cation from electrolytes and acidity/alkalinity on the phase behavior of sodium dodecyl sulfate-n-butanol-organics-water （with electrolytes） microemulsion sys-tem. The organics used is commercial kerosene. The volume ratio of water to organics is 1︰1. The results show that the type and valence of electrolyte cations are important factors influencing the microemulsion behavior. Biva-lent Ca2＋is more effective than monovalent K＋and Na＋for the formation of Winsor type III and II microemulsion. For electrolytes with the same monovalent cation Na＋, i.e. NaCl and Na2CO3, anions in the electrolyte have some effect. Bivalent anion 23CO - leads to a lower activity of cation Na＋than monovalent anion Cl-. NaOH （or KOH） behaves similar with NaCl （or KCl）. When HCl is used as electrolyte, its acidity plays an important role. Phase in-version of microemulsion from type III （or II） to type I is observed through precipitation of Ca2＋using Na2CO3, neutralization of HCl by NaOH, and addition of water to the system, which releases the oil from the microemulsion.

Determination of Trace Amounts of Zinc, Iron and Copper by Flame Atomic Absorption after Their Preconcentration Using Sodium Dodecyl Sulfate (SDS) Coated Alumina Nanoparticles Modified with 3-Mercapto-D-Valin from Environmental Samples

A sensitive and simple solid phase extraction method for the simultaneous determination of trace and toxic metals in environmental samples has been reported. The method is based on the adsorption of Zinc, Iron and Copper on SDS-coated alumina nanoparticles, which is also modified with 3-mercapto-D-valine. The retained analyte ions on modified solid phase were eluted using 5 mL of 4 mol·L﹣1 HNO3. The analyte determination was carried out by flame atomic absorption spectrometry. The influences of some metal ion and anions on the recoveries of understudy analyte ion were investigated. The influences of the analytical parameters including pH, ligand and SDS amount, eluting solution (type and concentrations) and sample volume on metal ions recoveries were investigated. The extraction efficiency was > 98% with relative standard deviation lower than 3% the method has been successfully applied for the extraction and determination of these ions content in some real samples. Prepared adsorbent was characterized by SEM and FT-IR measurements.

Phase Behavior and Structural Transitions in Sodium Dodecyl Sulfonate Microemulsions

The forming mechanism of microemulsion of sodium dodecyl sulfonate, alcohols,water and isooctane was studied, with particular emphasis on the effect of molecular weight andconcentration of alcohols. Phase diagram of the four components, alcohol, sodium dodecyl sulfonate,water and isooctane, was used as a means of study, through which the microemulsion regions weredetermined. Phase diagram of sodium dodecyl sulfonate/n-pentanol/isooctane/water system at κ_m = 2(κ_m = W_(n-pentanol)/W_(SDS)) is presented. The variation of conductivities of differentmicroemulsion samples with water was measured. From the conductivities we investigated a change instructure from water droplets in oil (W/O) at low water content to liquid crystal at intermediatewater content and a stricture of oil droplets in water (O/W) at high water content.

Effect of Addition of Sodium Dodecyl Sulfite on Physical Properties of Wheat Gluten Films

Films were made from the wheat glutens treated with 5%,10%,15%,20%,25% and 30%(wt% of gluten) of sodium dodecyl sulfite (SDS) in order to improve the properties of the films. Glycerol was used as a plasticizer.An addition of SDS in wheat glutens prior to forming films significantly increased the elongation at break(E) (P<0.05) and reduced notably the water vapor permeability(WVP) (P<0.05). In contrast,a decrease in the tensile strength(TS) of the films from gluten containing-SDS was found.Moreover,a significant decrease in P_(O_2) and P_(CO_2) of films from gluten treated with SDS was noticed. Although SDS-treated gluten film was slightly more yellow and darker than control one, it was not visually detrimental. It is indicated that the treatment with SDS prior to forming films greatly enhances the mechanical properties of wheat gluten films.The obivous improvement in water vapor permeability and extensibility of gluten films means that the use of SDS is a potential choice for improving properties of gluten films. The edible film was used to preserve tomatoes. The experimental results show that the shelf life of tomatoes coated with the edible film is extended, and the nutritional quality is kept well.

Molecular Dynamics Simulation of Effect of Salt on the Compromise of Hydrophilic and Hydrophobic Interactions in Sodium Dodecyl Sulfate Micelle Solutions

The presence of salt has a profound effect on the size,shape and structure of sodium dodecyl sulfate(SDS)micelles.There have been a great number of experiments on SDS micelles in the presence and absence of salt to study this complex problem.Unfortunately,it is not clear yet how electrolyte ions influence the structure of micelles.By describing the compromise between dominant mechanisms,a simplified atomic model of SDS in presence of salt has been developed and the molecular dynamics(MD)simulations of two series of systems with different concentrations of salt and charges of ion have been performed.Polydispersity of micelle size is founded at relatively high concentration of SDS and low charge of cation.Although the counter-ion pairs with head groups are formed,the transition of micelle shape is not observed because the charge of cation is not enough to neutralize the polar of micelle surface.

Molecular dynamics simulations of the effects of sodium dodecyl sulfate on lipid bilayer

Molecular dynamics simulations have been performed on the fully hydrated lipid bilayer with different concentrations of sodium dodecyl sulfate （SDS）. SDS can readily penetrate into the membrane. The insertion of SDS causes a decrease in the bilayer area and increases in the bilayer thickness and lipid tail order, when the fraction of SDS is less than 28%. Through calculating the binding energy, we confirm that the presence of SDS strengthens the interactions among the DPPC lipids, while SDS molecules act as intermedia. Both the strong hydrophilic interactions between sulfate and phosphocholine groups and the hydrophobic interactions between SDS and DPPC hydrocarbon chains contribute to the tight packing and ordered alignment of the lipids. These results are in good agreement with the experimental observations and provide atomic level information that complements the experiments.

The Electrooxidation of Tetracycline at Acetylene Black Electrode in the Presence of Sodium Dodecyl Sulfate

The electrooxidation of tetracycline (TC) at acetylene black electrode has been studied in the presence of sodium dodecyl sulfate (SDS). Tetracycline (TC) exhibited very sensitive oxidation peak in this system. The peak current was proportional to TC concentration, and the detection limit was 1.2×10-8 mol/L. The system was used to the determination of TC in Pharmaceuticals.

MICELLIZATION STUDIES OF DODECYL BENZENESULFONIC ACID AND ITS INTERACTION WITH POLYVINYLPYRROLIDONE

Dodecyl benzenesulfonic acid(DBSA)surfactant was used in the present study to find the effect of concentrationon its electrical conductance in solution from 293-323 K above and below the critical micelle concentration(CMC).Themicellization parameters i.e.degree of counter ion binding(β),aggregation number(n)and number of counter ion micelle(m)were measured.The interaction of DBSA with polyvinylpyrrolidone(PVP)was also studied at 293 K throughconductance and surface tension measure ments.A number of important parameters i.e.critical aggregation concentration(CAC),Gibb's free energy(△G)and binding ratio(R)were determined and the effect of NaCl on the CAC and polymersaturation point(PSP)was also investigated.

Effect of β-Cyclodextrin Upon the Sol-gel Transition of Methylcellulose Solutions in the Presence of Sodium Dodecyl Sulfate

The sol-gel transition temperature of methylcellulose （MC） solution in the presence of sodium dodecyl sulfate （SDS） as well as the mixtures of SDS and β-cyclodextrin （β-CD） was mea- sured, and the effect of the two competing interactions, the hydrophobic interaction between SDS and MC and the inclusion interaction between SDS and β-CD, upon the sol-gel transition of MC solution was studied. It has been found that the inclusion interaction between SDS and β-CD is much greater than the hydrophobic interaction between SDS and MC. As a result, in the coexistence of SDS and β-CD, the sol-gel transition temperature of MC solution keeps the same value, independent of the concentration of SDS in solution on con- dition that the concentration of SDS is less than β-CD. Our experimental results not only suggest that the effect of SDS upon the sol-gel transition of MC solution can be screened by β-CD completely but also indicate the inclusion ratio of SDS to β-CD can be determined quantitatively by using rheological measurement. The inclusion ratio of SDS to β-CD is 1：1, which is in good agreement with the inclusion ratio of SDS to β-CD in the presence of poly（vincyl pyrrolidone） determined by the viscosity measurement but is critically different from the inclusion ratio of SDS to β-CD in the presence of the oppositely charged polyelec-trolyte by using the rheological measurement, mainly due to the reason that the mechanism of the interaction between SDS and MC is critically different from the mechanism of the interaction between SDS and the oppositely charged polyelectrolyte.

STUDIES ON DERIVATIVE FLUORIMETRY Ⅲ. DETERMINATION OF TRACE AMOUNT OF TERBIUM IN THE PRESENCE OF SODIUM DODECYL SULFONATE

The derivative fluorimetric characteristics of Tb—SDS and Tb—SDS—phenanthroline systems have been studied. The optimum conditions were obtained. The 2nd—derivative spectrofluorimetric method in the systems has been applied to the determination of trace amounts of terbium, in rare earth ore and their oxides. The results are satisfactory.

Effects of Sodium Dodecyl Sulfate on a Single Cavitation Bubble

Dynamics of a single cavitation bubble in sodium dodecyl sulfate（SDS） aqueous solutions is investigated experimentally and theoretically. The bubble pulsation is measured by a phase-locked integrated imaging technique,and the ambient radius is obtained by fitting the numerical calculation based on the Rayleigh–Plesset bubble dynamics model to the experimental data. The results show that, under the same driving condition, the ambient radius of the cavitation bubble decreases correspondingly with the increase of SDS concentration within the critical micelle concentration, while the compression ratio of the radius increases, which indicates that the addition of SDS decreases the internal molecular number of the cavitation bubble and increases the power capability of the cavitation bubble. In addition, bubble oscillation increases the concentration of the surfactant molecules on the bubble wall, so that the effect of SDS on a single cavitation bubble is reduced when the SDS concentration is greater than 0.8 m M.

Experimental and Quantum Chemical Studies of the Inhibition of Copper with Sodium Dodecyl Sulphate (SDS) in Acidic Medium

This work investigates the inhibitive properties of sodium dodecyl sulphate (SDS) on the corrosion of copper (Cu) in nitric acid using gasometric methods. The inhibition efficiency increases with time and concentration of SDS. The corrosion rate of copper decreases as concentration of SDS increases. Adsorption of the SDS on the surface obeyed the Langmuir adsorption isotherm. The high negative values of the kinetic parameter B suggest that the inhibitor’s effectiveness increases with temperature. The equilibrium constant and the free energy of adsorption of SDS to copper are negative and large. This observation implies that the adsorption mechanism maybe chemisorption. The quantum chemical calculation of copper dodecyl sulphate shows that the energy change in the HOMO-LUMO energy of the moiety is positive and small. This observation implies that the SDS is an efficient inhibitor. The high dipole moment obtained implies that corrosion inhibition of Cu is enhanced by adsorption of SDS and this observation correlates with the observed experimental inhibition efficiency.