Several action regimes were employed, namely, those exposed to solutions containing single and/or composite chloride and sulfate salts, and under wet-dry cycles and/or flexural loading. The variations in dynamic modul...Several action regimes were employed, namely, those exposed to solutions containing single and/or composite chloride and sulfate salts, and under wet-dry cycles and/or flexural loading. The variations in dynamic modulus of elasticity（Erd values） were monitored, as well as the key factor impacting on the chloride ingress when concrete subjected to multiple action regimes was identified by the method of Grey Relation Analysis（GRA）. The changes in micro-structures and mineral products of interior concrete after different action regimes were investigated by means of X-ray diffraction（XRD）, mercury intrusion technique（MIP）, and scanning electron microscopy（SEM）. The test results showed that the cyclic wet-dry accelerated the deterioration of OPC concrete more than the action of 35% flexural loading based on the results of Erd values and the GEA. The analyses from micro-structures could give certain explanations to the change in Erd values under different action regimes.展开更多
Hardened cement paste was subjected to the flexural loading and wet-dry cycles in sea water. The degradation of microstructures was obtained using scanning electron microscope （SEM）, and the energy dispersive spectr...Hardened cement paste was subjected to the flexural loading and wet-dry cycles in sea water. The degradation of microstructures was obtained using scanning electron microscope （SEM）, and the energy dispersive spectrum （EDS） analysis was carried to analyze the local composition. Mercury intrusion porosimetry （Poremaster GT-60） was used to analyze the degradation of pore structures. The experimental results show that the synergistic action of the flexural loading, wet-dry cycles and sea water leads to significant deterioration of hardened cement paste. The degradation of microstructures in the tensile region is more serious than that in the compressive region. The flexural loading and wet-dry cycles accelerate the chemical attack of sea water.展开更多
Our research focused on the analy sis of concrete deterioration mechan ism under the coup ling effects of flexural load,cy clic wetting and dry ing, and sulfate. The relative dy namic modulus of elasticity of a corrod...Our research focused on the analy sis of concrete deterioration mechan ism under the coup ling effects of flexural load,cy clic wetting and dry ing, and sulfate. The relative dy namic modulus of elasticity of a corroded concrete samp le was tested, and scannin g electron microscop e was used to observe the microstructure of concrete under the coup ling effects of flexural load,cy clic wetting and dry ing, and sulf ate. Results manif ested that flexur al load and cy clic wetting and dry ing durin g the concrete service chan ged the corrosion p rocess of the sulfate mediu m in con crete and enh anced the deterioration of con crete p erforman ce.Furthermore, the influencin g p atterns of strength grade of concr ete, mass concentration of sulfate solution, and mineral admixtures on the degree of concrete deterioration were identified.展开更多
上海软X射线自由电子激光装置(Shanghai soft X-ray Free Electron Laser,SXFEL)与上海硬X射线自由电子激光装置(Shanghai High repetition rate XFEL and Extreme light facility,SHINE)需要使用许多大功率微波元件,例如行波加速管、...上海软X射线自由电子激光装置(Shanghai soft X-ray Free Electron Laser,SXFEL)与上海硬X射线自由电子激光装置(Shanghai High repetition rate XFEL and Extreme light facility,SHINE)需要使用许多大功率微波元件,例如行波加速管、偏转腔、脉冲压缩器等。为了满足这些元件的高功率测试与运行的需求,研发了两台高功率不锈钢吸收负载,在X波段两台负载的工作频率分别为11.424 GHz和11.988 GHz。通过模拟仿真的方法,设计了负载的初步模型,并优化了其微波参数。模拟结果显示两台负载在中心频率附近-20 dB以下的带宽达到百兆赫兹以上。通过理论计算的方法计算了水路中的对流换热系数,并基于此对负载的机械模型进行了热分析,计算了其工作状态下的温度分布。两台负载模型均具有周期性凹槽的类波导结构,在完成负载的加工制造后,使用矢量网络分析仪对两种负载在装夹状态和焊接完成后的射频参数进行了测量。实验测试的结果与模拟计算的结果吻合较好,达到了设计要求。展开更多
基金Funded by the National Natural Science Foundation of China(51578141)the Major State Basic Research Development Program of China(973 Program)(2015CB655102)+1 种基金the Program Most of China(2016YFE0118200)the support of China Scholarship Council
文摘Several action regimes were employed, namely, those exposed to solutions containing single and/or composite chloride and sulfate salts, and under wet-dry cycles and/or flexural loading. The variations in dynamic modulus of elasticity（Erd values） were monitored, as well as the key factor impacting on the chloride ingress when concrete subjected to multiple action regimes was identified by the method of Grey Relation Analysis（GRA）. The changes in micro-structures and mineral products of interior concrete after different action regimes were investigated by means of X-ray diffraction（XRD）, mercury intrusion technique（MIP）, and scanning electron microscopy（SEM）. The test results showed that the cyclic wet-dry accelerated the deterioration of OPC concrete more than the action of 35% flexural loading based on the results of Erd values and the GEA. The analyses from micro-structures could give certain explanations to the change in Erd values under different action regimes.
基金Founded by the Western traffic Project under the Ministry of Communications of China (No. 200631822302-03)the China National Natural Science Foundation (No. 50808045)
文摘Hardened cement paste was subjected to the flexural loading and wet-dry cycles in sea water. The degradation of microstructures was obtained using scanning electron microscope （SEM）, and the energy dispersive spectrum （EDS） analysis was carried to analyze the local composition. Mercury intrusion porosimetry （Poremaster GT-60） was used to analyze the degradation of pore structures. The experimental results show that the synergistic action of the flexural loading, wet-dry cycles and sea water leads to significant deterioration of hardened cement paste. The degradation of microstructures in the tensile region is more serious than that in the compressive region. The flexural loading and wet-dry cycles accelerate the chemical attack of sea water.
基金Funded by Fujian Education Department(Nos.JA11329 and JA12412)Quanzhou(Fujian)Techno logy Research and Development Program(Nos.2013Z158,2013Z47,and 2010G7)
文摘Our research focused on the analy sis of concrete deterioration mechan ism under the coup ling effects of flexural load,cy clic wetting and dry ing, and sulfate. The relative dy namic modulus of elasticity of a corroded concrete samp le was tested, and scannin g electron microscop e was used to observe the microstructure of concrete under the coup ling effects of flexural load,cy clic wetting and dry ing, and sulf ate. Results manif ested that flexur al load and cy clic wetting and dry ing durin g the concrete service chan ged the corrosion p rocess of the sulfate mediu m in con crete and enh anced the deterioration of con crete p erforman ce.Furthermore, the influencin g p atterns of strength grade of concr ete, mass concentration of sulfate solution, and mineral admixtures on the degree of concrete deterioration were identified.