In the present paper, the high velocity impact of 9 mm soft lead projectile on 10 mm and 30 mm thick Eglass/epoxy composites was studied using a 450 kV Flash X-ray radiography(FXR) system. The basic parameters of FXR ...In the present paper, the high velocity impact of 9 mm soft lead projectile on 10 mm and 30 mm thick Eglass/epoxy composites was studied using a 450 kV Flash X-ray radiography(FXR) system. The basic parameters of FXR imaging, such as effect of ratio of target to film(TF) and source to target(ST) distances and X-ray penetration thickness of the composite material were optimized based on clarity and the actual dimensions of the objects. The optimized parameters were used in the FXR imaging of the ballistic event of 9 mm soft projectile on E-glass/epoxy composite. The real time deformation patterns of both the projectile and composite target during the ballistic impact were captured and studied at different time intervals. The notable failure modes of the 10 mm thick target with time include fibre breakage, bulging on the back side, delamination, recovery of the bulging, reverse bulging and its recovery. However, with increase in thickness of the target to 30 mm the only failure mechanism observed is the breaking of fibres. The ballistic impact event was also numerically simulated using commercially available LS-DYNA software. The numerically simulated deformation patterns of the projectile and target at different time intervals are closely matching with the corresponding radiographic images.展开更多
Short jute fiber (2 - 3 mm) reinforced polypropylene PP-based composites (20% fiber by weight) were fabricated using compression molding and the mechanical properties were evaluated. Tensile strength (TS), tensile mod...Short jute fiber (2 - 3 mm) reinforced polypropylene PP-based composites (20% fiber by weight) were fabricated using compression molding and the mechanical properties were evaluated. Tensile strength (TS), tensile modulus (TM), elongation at break (Eb%), flexural strength (FS), flexural modulus (FM), impact strength (IS), and hardness of the composites were found to be 32 MPa, 850 MPa, 12%, 38 MPa, 1685 MPa, 18 kJ/m2 and 96 shore-A, respectively. Then short E-glass fiber (2 - 3 mm) reinforced PP-based composites (20% fiber by weight) were fabricated and mechanical properties were compared with short jute-based composites. Short jute-based composites showed excellent mechanical properties and comparable to short E-glass-based composites. Soil degradation test of both types of composites indi-cated that jute/PP composites significantly lost much of its mechanical properties but E-glass/PP composites retained major portion of its original integrity. Interfaces of the degraded composites were investigated by scanning electron microscopy and supported the biodegradation properties of jute/PP composites.展开更多
In this study, a laminated woven bamboo/woven E glass/unsaturated polyester composite is developed to combat a ballistic impact from bullet under shooting test. The aim of this study is to understand the fundamental e...In this study, a laminated woven bamboo/woven E glass/unsaturated polyester composite is developed to combat a ballistic impact from bullet under shooting test. The aim of this study is to understand the fundamental effects of the woven bamboo arrangement towards increasing ballistic resistance properties. The work focusses on the ballistic limit test known as NIJ V50, which qualifies materials to be registered for use in combat armor panels. The results show that the composites withstood 482.5 m/s ± 5 limit of bullet velocity, satisfying the NIJ test at level II. The findings give a strong sound basis decision to engineers whether or not green composites are qualified to replace synthetic composites in certain engineering applications.展开更多
文摘In the present paper, the high velocity impact of 9 mm soft lead projectile on 10 mm and 30 mm thick Eglass/epoxy composites was studied using a 450 kV Flash X-ray radiography(FXR) system. The basic parameters of FXR imaging, such as effect of ratio of target to film(TF) and source to target(ST) distances and X-ray penetration thickness of the composite material were optimized based on clarity and the actual dimensions of the objects. The optimized parameters were used in the FXR imaging of the ballistic event of 9 mm soft projectile on E-glass/epoxy composite. The real time deformation patterns of both the projectile and composite target during the ballistic impact were captured and studied at different time intervals. The notable failure modes of the 10 mm thick target with time include fibre breakage, bulging on the back side, delamination, recovery of the bulging, reverse bulging and its recovery. However, with increase in thickness of the target to 30 mm the only failure mechanism observed is the breaking of fibres. The ballistic impact event was also numerically simulated using commercially available LS-DYNA software. The numerically simulated deformation patterns of the projectile and target at different time intervals are closely matching with the corresponding radiographic images.
文摘Short jute fiber (2 - 3 mm) reinforced polypropylene PP-based composites (20% fiber by weight) were fabricated using compression molding and the mechanical properties were evaluated. Tensile strength (TS), tensile modulus (TM), elongation at break (Eb%), flexural strength (FS), flexural modulus (FM), impact strength (IS), and hardness of the composites were found to be 32 MPa, 850 MPa, 12%, 38 MPa, 1685 MPa, 18 kJ/m2 and 96 shore-A, respectively. Then short E-glass fiber (2 - 3 mm) reinforced PP-based composites (20% fiber by weight) were fabricated and mechanical properties were compared with short jute-based composites. Short jute-based composites showed excellent mechanical properties and comparable to short E-glass-based composites. Soil degradation test of both types of composites indi-cated that jute/PP composites significantly lost much of its mechanical properties but E-glass/PP composites retained major portion of its original integrity. Interfaces of the degraded composites were investigated by scanning electron microscopy and supported the biodegradation properties of jute/PP composites.
基金the Fundamental Research Grant Scheme(FRGS)1/2013/TK01/UPNM/01/2Universiti Pertahanan National Malaysia(UPNM)for supporting the research work
文摘In this study, a laminated woven bamboo/woven E glass/unsaturated polyester composite is developed to combat a ballistic impact from bullet under shooting test. The aim of this study is to understand the fundamental effects of the woven bamboo arrangement towards increasing ballistic resistance properties. The work focusses on the ballistic limit test known as NIJ V50, which qualifies materials to be registered for use in combat armor panels. The results show that the composites withstood 482.5 m/s ± 5 limit of bullet velocity, satisfying the NIJ test at level II. The findings give a strong sound basis decision to engineers whether or not green composites are qualified to replace synthetic composites in certain engineering applications.