100t EAL-LF-VD-Φ500 mm铸坯流程4Cr5MoSiV1模具钢的生产实践

生产的4Cr5MoSiVl钢(/%:0.38~0.40C,0.88~0.92Si,0.42~0.44Mn,0.001~0.003S,0.007~0.014P,5.00~5.55Cr,1.37~1.40Mo,0.98~1.00V,0.015~0.025Alt)的工艺流程为65%铁水+35%废钢-100 t EAF-LF-VD-Φ500 mm坯连铸-Φ120 mm圆钢轧制。通过控制EAF终点[C]0.06%~0.10%,终点[P]0.006%,出钢加1 kg/t铝块预脱氧,LF精炼渣碱度2.5~3.0,喂钙线后软吹≥10 min,VD≤67 Pa,100×2 L/min氩气搅拌≥15min,中间包钢水过热20~30℃,连铸结晶器电磁搅拌(310 A,1.5 Hz),保护浇铸,拉速0.34~0.35 m/min等工艺措施,10炉4Cr5MoSiVl钢中[O],[N]和[H]分别为10×10^(-6)~12×10^(-6),72×10^(-6)~80×10^(-6),1.2×10^(-6)~1.4×10^(-6),各项指标均满足协议要求。