The oxide contents of TiO2, MnO, SrO and Fe2O3 in the body and graze layers of the Jiao-Tan-Xia (JTX) and Lao-Hu-Dong (LHD) porcelains in Southern Song Dynasty (1127-1279 A.D.) have been determined using an In- ternat...The oxide contents of TiO2, MnO, SrO and Fe2O3 in the body and graze layers of the Jiao-Tan-Xia (JTX) and Lao-Hu-Dong (LHD) porcelains in Southern Song Dynasty (1127-1279 A.D.) have been determined using an In- ternational Eagle-II μ-probe EDXRF spectrometer. The results show that the contents in the body are much different from those in the graze one. Therefore, the transient thickness (TT) between the body and graze layers can be meas- ured through determination of a distance of the drift change in the chemical contents. The TT average for the JTX porcelains is 161μm, while that for the LHD porcelains is 258μm, which are consistent with a range of 0.15-0.3mm in the Ru-Yao porcelains. The different TT is related to the variances in firing temperature and raw material for manu- facturing the respective porcelains.展开更多
基金Supported by the City University of Hong Kong Foundation (No.9010007) the Innovation Project Funds of CAS (Nos. KZCX2-SW-118+1 种基金 KZCX3-SW-120) the NKPBR Project Fund (No.2001CCB00100) and the SKLLQG0324 Foundation.
文摘The oxide contents of TiO2, MnO, SrO and Fe2O3 in the body and graze layers of the Jiao-Tan-Xia (JTX) and Lao-Hu-Dong (LHD) porcelains in Southern Song Dynasty (1127-1279 A.D.) have been determined using an In- ternational Eagle-II μ-probe EDXRF spectrometer. The results show that the contents in the body are much different from those in the graze one. Therefore, the transient thickness (TT) between the body and graze layers can be meas- ured through determination of a distance of the drift change in the chemical contents. The TT average for the JTX porcelains is 161μm, while that for the LHD porcelains is 258μm, which are consistent with a range of 0.15-0.3mm in the Ru-Yao porcelains. The different TT is related to the variances in firing temperature and raw material for manu- facturing the respective porcelains.