Analysis of the Composition and Physical and Mechanical Properties of Raw Materials for Thermal Insulation Fabrics

In this article, winter clothes, bedding, pillows, mattresses are produced in the Republic of Uzbekistan and used in the export products of foreign countries in domestic market shopping centers;existing nonwoven fabric samples were used as toys, children’s clothing as a heat retainer, a space-filler was selected on the basis of marketing survey analysis. Chemical bonding, processing technology, methods, linear density, thickness, air permeability, hygroscopicity, heat storage and heat transfer properties of the samples were analyzed experimentally based on the preparation methods, the fiber content was compared with the standard technology. The advantages and disadvantages of the samples were studied and recommendations for use in sewing according to consumer requirements were given.

玄武岩织物增强泡沫板材保温性能分析

探讨玄武岩织物复合板材的保温性能。以耐高温玄武岩长丝为原料,采用机织工艺织造纤维增强体预制件,并在平面织物和中空织物腔体中填充聚氨酯泡沫,织物表面复合树脂,加工了不同结构的三明治型复合板材,对板材的保温性能影响因素进行了分析。结果表明:同等密度的平面织物增强板材保温性能优于中空织物增强板材;中空织物面层的组织密度变化对板材保温性能影响不大;随着泡沫填充密度的增加,板材的导热系数上升,保温率下降。认为:在满足板材机械性能要求的前提下,控制填充材料的用量可以降低生产成本,提高板材保温性能。

EPS板-玄武岩纤维中空织物复合保温板力学性能试验

为研究一种EPS板-玄武岩纤维中空织物复合保温板的力学性能,设计了含附着层保温板的粘结强度,含附着层和多层夹芯复合保温板的抗压强度以及抗折强度试验。结果表明:当含附着层保温板的环氧树脂WSR6101/固化剂T31/无水乙醇构成的粘结剂配合比为6∶2∶1时,其保温板的粘结强度较佳,在实际工程应用中可以防止保温板内层脱落;与相同厚度的EPS板相比,含附着层和多层夹芯复合保温板的抗压强度分别增加了7%和5.3%,符合相关的规定,且含附着层保温板的抗压强度优于多层夹芯复合保温板的抗压强度;在满足基本工艺要求的情况下,复合保温板的抗折强度较为优异。

EPS-玄武岩纤维中空织物保温板热工性能研究

将EPS板与玄武岩纤维中空织物粘结,制备一种新型EPS-玄武岩纤维中空织物保温板,并测试其导热系数。结果表明,新型保温板具有良好的保温隔热效果;9层以上的建筑和体形系数不大于0.3时且用于外墙围护结构中,新型保温板中EPS板厚度为30 mm时,保温板的传热系数可以满足寒冷地区围护结构保温隔热的限值要求,当EPS板的厚度分别为10、20、30 mm时,新型保温板的传热系数均小于1.0 W/(m^2·K),满足建筑节能65%的指标要求。

EPS板-玄武岩纤维中空织物保温板导热性能模拟

通过数值模拟与试验方法,研究了EPS板-玄式岩纤维中空织物保温板的导热性能;采用一维稳态热流计法进行试验,测试了不同厚度EPS板与占武岩纤维中空织物组合而成的新型保温板的导热系数;并利用软件ANSYS Workbench对新型保温板的传热机理进行模拟,同时结合相关理论公式,对新型保温板的导热系数进行理论计算。数值模拟和实验结果表明,玄武岩纤维中空织物可以大幅降低EPS板的厚度,能够有效阻止温度降低,提高保温板整体的保温隔热性能;有限元模拟得到的导热系数预测值与实验测试结果相比,最大误差为8.8%,两者基本一致.

新型苯板-BFRP中空织物保温板导热性能研究

为测定不同厚度膨胀聚苯乙烯板(EPS)与玄武岩纤维(BFRP)中空织物组合而成的新型保温板导热系数,运用一维稳态热流计法开展试验研究;结合理论公式,计算新型保温板的导热系数。试验结果表明:新型苯板-玄武岩纤维中空织物保温板最优组合的导热系数为0.0272W/(m·K),与EPS板导热系数相比下降33.66%;在温度和湿度不变的条件下,使用玄武岩纤维中空织物可以大幅减小EPS板厚度;带附着层保温板的导热系数较小,保温隔热性能好;新型保温板导热系数的理论值与实测值基本一致,最大误差绝对值仅为8.55%。

多组分非织造保暖材料的设计与性能研究

在保暖材料向复合型多功能发展的趋势下，设计探究了一种多组分非织造保暖材料。将不同比例的木棉、远红外三维卷曲中空涤纶、ES纤维混合，通过非织造技术加工成非织造保暖材料。对其面密度、厚度、远红外辐射温升、保暖性、蓬松度与回复率、透气性、透湿性进行了测试分析。测试结果显示，木棉／远红外三维卷曲中空涤纶／Es40／40／20保暖材料的综合性能最好，克罗值为1．54℃·m^2／W，远红外辐射温升值2．7℃，透气率1608．7mm／s，透湿率98．94g/（m^2·h），蓬松度218．33cm^3／g，回复率86．90％。