By using waste bricks as aggregate,a kind of porous ecological concrete was prepared and the mixing technique and its properties were studied. Effects of the cement paste fluidity on workability of the porous ecologic...By using waste bricks as aggregate,a kind of porous ecological concrete was prepared and the mixing technique and its properties were studied. Effects of the cement paste fluidity on workability of the porous ecological concrete were investigated,and influences of the water-cement ratio,the aggregate-cement ratio and the aggregate size on compressive strength and porosity of the porous ecological concrete were also discussed. Results show that for preparation of the porous ecological concrete,the aggregates should be enveloped with neat cement paste,and recommended fluidity of the cement paste is 200～235 mm. With the increasing of the aggregate-cement ratio,porosity of the porous ecological concrete increases while the 28 d compressive strength decreases. With increasing of the water-cement ratio,porosity of the porous ecological concrete decreases. And relationship between compressive strength and water-cement ratio of the porous ecological concrete does not follow Bolomey's formula. As a result of this study the porous ecological concrete is prepared,its porosity is 38.93%,the water absorption is 11.39% and the compressive strength is 1.14 MPa.展开更多
Ecological reactive powder concrete (ECO-RPC) with small sized and differentvolume fraction steel fibers was prepared by substitution of ultra-fine industrial waste powder for50% to 60% cement by weight and replacemen...Ecological reactive powder concrete (ECO-RPC) with small sized and differentvolume fraction steel fibers was prepared by substitution of ultra-fine industrial waste powder for50% to 60% cement by weight and replacement of ground fine quartz sand with natural fine aggregate.The effect of steel fiber volume fraction and curing ages on the static mechanical behaviour ofECO-RPC was studied. Using the split Hopkinson pressure bar technique, the dynamic mechanicalbehaviour of ECO-RPC was investigated under different strain rates. The results show that the staticmechanical behaviour of ECO-RPC increases with the increase of steel fiber volume fraction andcuring ages. The type of ECO-RPC with the substitution of 25% ultra-fine slag, 25% ultra-fine flyash and 10% silica fume is better than the others with compressive strength, flexural strength, andfracture energy more than 200 MPa, 60 MPa and 30 kJ/m^2, respectively. ECO-RPC has excellent strainrate stiffening effects under dynamic load. Its peak stress, peak strain and the area understrain-stress curve increase with the increase of strain rate. Its fracture pattern changes frombrittleness to toughness under high strain rates.展开更多
基金support from the National Science Foundation(50178044) of ChinaJiangsu Provincial Natural Science Foundation (BK2005216) of China
文摘By using waste bricks as aggregate,a kind of porous ecological concrete was prepared and the mixing technique and its properties were studied. Effects of the cement paste fluidity on workability of the porous ecological concrete were investigated,and influences of the water-cement ratio,the aggregate-cement ratio and the aggregate size on compressive strength and porosity of the porous ecological concrete were also discussed. Results show that for preparation of the porous ecological concrete,the aggregates should be enveloped with neat cement paste,and recommended fluidity of the cement paste is 200～235 mm. With the increasing of the aggregate-cement ratio,porosity of the porous ecological concrete increases while the 28 d compressive strength decreases. With increasing of the water-cement ratio,porosity of the porous ecological concrete decreases. And relationship between compressive strength and water-cement ratio of the porous ecological concrete does not follow Bolomey's formula. As a result of this study the porous ecological concrete is prepared,its porosity is 38.93%,the water absorption is 11.39% and the compressive strength is 1.14 MPa.
文摘Ecological reactive powder concrete (ECO-RPC) with small sized and differentvolume fraction steel fibers was prepared by substitution of ultra-fine industrial waste powder for50% to 60% cement by weight and replacement of ground fine quartz sand with natural fine aggregate.The effect of steel fiber volume fraction and curing ages on the static mechanical behaviour ofECO-RPC was studied. Using the split Hopkinson pressure bar technique, the dynamic mechanicalbehaviour of ECO-RPC was investigated under different strain rates. The results show that the staticmechanical behaviour of ECO-RPC increases with the increase of steel fiber volume fraction andcuring ages. The type of ECO-RPC with the substitution of 25% ultra-fine slag, 25% ultra-fine flyash and 10% silica fume is better than the others with compressive strength, flexural strength, andfracture energy more than 200 MPa, 60 MPa and 30 kJ/m^2, respectively. ECO-RPC has excellent strainrate stiffening effects under dynamic load. Its peak stress, peak strain and the area understrain-stress curve increase with the increase of strain rate. Its fracture pattern changes frombrittleness to toughness under high strain rates.