The surface of hollow glass microspheres (HGMs) was roughened by a HCl+NH_(4)F strategy,which achieved a broken ratio as 16.10%,and then metallized by electroless plating by Co nanoparticles up to 90 wt% (abbreviated ...The surface of hollow glass microspheres (HGMs) was roughened by a HCl+NH_(4)F strategy,which achieved a broken ratio as 16.10%,and then metallized by electroless plating by Co nanoparticles up to 90 wt% (abbreviated as Co-HGMs).The average grain size of Co was measured to range from 0.4 to 0.5 μm.Then Co-HGMs were mixed with liquid silicone rubber and xylene,and cured on a perspex plate applicable for flexible electromagnetic shielding.By attentive parameter optimization,a film about 0.836 mm in thickness was obtained with a density of 0.729 g/cm^(3),showing a shielding effectiveness of 15.2 dB in the X-band (8.2-12.4 GHz) at room temperature,which was ascribed to the formation of a conductive network of Co-HGMs inside the film.Simultaneously,the tensile strength of 0.89 MPa at an elongation ratio of 194.5% was also obtained,showing good mechanical properties and tensile strength.展开更多
文摘The surface of hollow glass microspheres (HGMs) was roughened by a HCl+NH_(4)F strategy,which achieved a broken ratio as 16.10%,and then metallized by electroless plating by Co nanoparticles up to 90 wt% (abbreviated as Co-HGMs).The average grain size of Co was measured to range from 0.4 to 0.5 μm.Then Co-HGMs were mixed with liquid silicone rubber and xylene,and cured on a perspex plate applicable for flexible electromagnetic shielding.By attentive parameter optimization,a film about 0.836 mm in thickness was obtained with a density of 0.729 g/cm^(3),showing a shielding effectiveness of 15.2 dB in the X-band (8.2-12.4 GHz) at room temperature,which was ascribed to the formation of a conductive network of Co-HGMs inside the film.Simultaneously,the tensile strength of 0.89 MPa at an elongation ratio of 194.5% was also obtained,showing good mechanical properties and tensile strength.