BEHAVIOR OF FLOW STRESS OF ALUMINUM SHEETS USED FOR PRESSURE CAN DURING COMPRESSION AT ELEVATED TEMPERATURE

The behavior of flow stress of Al sheets used for pressure can prepared by different melt-treatment during plastic deformation at elevated temperature was studied by isothermal compression test using Gleeble1500 dynamic hot-simulation testing machine. The results show that the AI sheets possess the remarkable characteristic of steady state flow stress when they are deformed in the temperature range of 350-500℃ at strain rates within the range of 0.01-10.0s^-1. A hyperbolic sine relationship is found to correlate well the flow stress with the strain rate, and an Arrhenius relationship with the temperature, which implies that the process of plastic deformation at elevated temperature for this material is thermally activated. Compared with the AI pieces prepared by no or conventional melt-treatment, hot deformation activation energy of AI sheets prepared by high-efficient melt-treatment is the smallest （ Q= 168.0kJ/mol）, which reveals that the hot working formability of this material is very better, and has directly to do with the effective improvement of its metallurgical quality.

The Effect of Elevated Temperature on Bond Performance of Alkali-activated GGBFS Paste

The main reaction products were investigated by analysis of microstructure of alkali-activated ground granulated blast furnace slag （GGBFS） paste. An experimental research was performed on bond performance of alkali-activated GGBFS paste as a construction adhesive after exposure to 20-500℃. Through XRD analysis, a few calcium silicate hydrate, hydrotalcite and tetracalcium aluminate hydrate were determined as end products, and they were filled and packed each other at room temperature. In addition, akermanite dramatically increased at 800 ~C and above. The two key parameters, the ultimate load Pu.T and effective bond length Le, were determined using test data of carbon fiber-reinforced polymer （CFRP）-to-concrete bonded joints at elevated temperature. The experimental results indicate that the ultimate load Pu.T remains relatively stable initially and then decreases with increasing temperature. The effective bond length Le increases with increasing temperature except at 300℃. The proposed temperature-dependent effective bond length formula is shown to closely represent the test data.

Research of Test Method on Abrasion Resistance at Elevated Temperatures of Refractories

In this work,the factors and parameters of a test method on abrasion resistance at elevated temperatures were discussed and researched.First of all,the precision tests of the test method on abrasion resistance at elevated temperatures were conducted in 8 laboratories.The results such as the standard deviation and reproducibility show good repeatability and reliability.The relationship between the stability of refractory performance and the standard deviation of their wear value was analyzed.Then the impact of the heat treatment condition of unshaped refractories and oxidation of SiC sand as abrasive on the lost volume of the tested specimens was researched.