The mechanism of corrosion is mainly sustained by an electrochemical process, in which anodic and cathodic reactions take place, keeping their kinetics alive by electrons and ions fluxes. Several specific conditions c...The mechanism of corrosion is mainly sustained by an electrochemical process, in which anodic and cathodic reactions take place, keeping their kinetics alive by electrons and ions fluxes. Several specific conditions can accelerate corrosion processes. When studying anticorrosive coatings, one of them is the contamination of metallic surface by soluble salts prior to coating, leading to premature failure of the paint system due to corrosion between the metallic surface and the coating. So the surface preparation step prior to coating is a procedure of great importance to the coating anticorrosive performance. The aim of this step is to clean the surface by removing visible and non-visible contaminants. Usually, wet abrasive blasting methods are the most efficient ones to achieve the latter objective, because they may clean the surface, create a surface roughness and also remove the non-visible contaminants, as they use water as a media. On the other hand, evaporation of water after blasting may create flash rust and to avoid this, it is common to use corrosion inhibitors in the water of wet blasting methods. In this paper, the use of sodium tetraborate (borax) as a corrosion inhibitor in wet abrasive blasting is discussed. Electrochemical measurements and mass loss tests show that a borax content of 1% in a saline solution has the best inhibitory action over carbon steel and zinc surfaces, allowing postponing for the painting step some time. However, residual borax left on the surface generated blistering and corrosion under coating, during accelerated corrosion test in a humidity condensation chamber. Electrochemical impedance spectroscopy confirmed that borax accelerated the permeation of water through the coating, downgrading the anticorrosive performance of the paint system.展开更多
文摘The mechanism of corrosion is mainly sustained by an electrochemical process, in which anodic and cathodic reactions take place, keeping their kinetics alive by electrons and ions fluxes. Several specific conditions can accelerate corrosion processes. When studying anticorrosive coatings, one of them is the contamination of metallic surface by soluble salts prior to coating, leading to premature failure of the paint system due to corrosion between the metallic surface and the coating. So the surface preparation step prior to coating is a procedure of great importance to the coating anticorrosive performance. The aim of this step is to clean the surface by removing visible and non-visible contaminants. Usually, wet abrasive blasting methods are the most efficient ones to achieve the latter objective, because they may clean the surface, create a surface roughness and also remove the non-visible contaminants, as they use water as a media. On the other hand, evaporation of water after blasting may create flash rust and to avoid this, it is common to use corrosion inhibitors in the water of wet blasting methods. In this paper, the use of sodium tetraborate (borax) as a corrosion inhibitor in wet abrasive blasting is discussed. Electrochemical measurements and mass loss tests show that a borax content of 1% in a saline solution has the best inhibitory action over carbon steel and zinc surfaces, allowing postponing for the painting step some time. However, residual borax left on the surface generated blistering and corrosion under coating, during accelerated corrosion test in a humidity condensation chamber. Electrochemical impedance spectroscopy confirmed that borax accelerated the permeation of water through the coating, downgrading the anticorrosive performance of the paint system.
