Enhanced corrosion resistance of epoxy resin coating via addition of CeO_(2) and benzotriazole

The use of fillers to enhance the corrosion protection of epoxy resins has been widely applied.In this work,cerium dioxide(CeO_(2))and benzotriazole(BTA)were introduced into an epoxy resin to enhance the corrosion resistance of Q235 carbon steel.Scanning electron microscopy results indicated that the CeO_(2) grains were rod-like and ellipsoidal in shape,and the distribution pattern of BTA was analyzed by energy dispersive spectroscope.The dynamic potential polarization curve proved the excellent corrosion resistance of the composite epoxy resin with CeO_(2) and BTA co-addition,and electrochemical impedance spectroscopy test analysis indicated the significantly enhanced long-term corrosion protection performance of the composite coating.And the optimal protective performance was provided by the coating containing 0.3%(mass)CeO_(2) and 20%(mass)BTA,which was attributed to the barrier performance of CeO_(2) particles and the chemical barrier effect of BTA.The formation of corrosion products was analyzed using X-ray diffraction.In addition,the corrosion resistance mechanism of the coating was also discussed in detail.

The Durability of Epoxy Resin Coating

The durability of epoxy resin coating was studied under environments with relative humidity （RH） of 98%-100%, at 55 ℃ for 900 h, at 65 ℃ for 700 h and at 75 ℃ for 400 h, respectively. Peel strength test, dynamical mechanical thermal analysis （DMTA）, infrared spectroscopy （IR） and energy dispersive X-ray spectroscopy （EDX） were employed for measurements. Peel strength indicated the development of adhesive property of the coating, DMTA indicated the development of physical property, IR revealed the development of chemical structure, and EDX showed surface element change of the coating. All these results show a good time- temperature equivalence characteristic between humidity aging time and temperature.

Developing polydopamine modified molybdenum disulfide/epoxy resin powder coatings with enhanced anticorrosion performance and wear resistance on magnesium lithium alloys

Epoxy resin powder coating has been successfully applied on the corrosion protection of magnesium lithium alloys.However,poor wear resistance and microcracks formed during the solidification have limited it extensive application.There are limited approaches to exploit such anti-corrosion and mechanical properties of magnesium lithium alloys.Herein,the epoxy resin powder coating with polydopamine modified molybdenum disulfide(MoS_(2)@PDA-EP powder coating with 0,0.1,0.2,0.5,1.0 wt.%loading)was well prepared by melt extrusion to investigate its anticorrosion performance and wear resistance.The results revealed that the addition of MoS_(2)@PDA enhanced the adhesion strength between coatings and alloys,wear resistance and corrosion protection of the powder coatings.Among them,the optimum was obtained by 0.2 wt.%MoS_(2)@PDA-EP powder coating which could be attributed to well dispersion and efficient adhesion with coating matrix.To conclude,MoS_(2)@PDA-EP powder coating is meaningfully beneficial for the anticorrosive and wear performance improvement of magnesium lithium alloys.

Influence of Surface State on Moisture Sensitivity of Carbon Fiber and Its Composite Interfacial Properties

The influence of surface state on the moisture sensitivity of carbon fiber was analyzed by applying a T800 grade carbon fiber with five different surface conditions,namely,with and without surface oxidation,in the presence or absence of sizing agent.The interfacial properties of their composites in the presence of two epoxy matrices（respectively EP07 and EP10） were also characterized by micro-droplet tests.The overall results show that both oxidized and sizing-coated fibers have higher moisture equilibrium content than that of the pristine unsurface-treated fiber,due to higher amount of activated carbon groups.After moisture absorption of the carbon fibers,almost all the fiber/epoxy systems show decrease in the interfacial shear strength and the unsurface-treated fiber system exhibits the largest decline.Moreover,both interfacial shear strength and interlaminar shear strength of carbon fiber/EP10 composite demonstrate better water resistance performance than that of the carbon fiber/EP07 composite,consistent with DSC results of the two resins.