Ultrahigh strength and improved electrical conductivity in an aging strengthened copper alloy processed by combination of equal channel angular pressing and thermomechanical treatment

In this paper,equal channel angular pressing and thermomechanical treatment was employed to improve the strength and electrical conductivity of an aging strengthened Cu-Ti-Cr-Mg alloy,and the microstructure and properties of the alloy were investigated in detail.The results showed that the samples deformed by the combination of cryogenic equal channel angular pressing(ECAP)and rolling had good comprehensive properties after aging at 400℃.The tensile strength of the peak-aged and over-aged samples was 1120 MPa and 940 MPa,with their corresponding electrical conductivity of 14.7%IACS and 22.1%IACS,respectively.ECAP and cryogenic rolling introduced high density dislocations,leading to the inhibition of the softening effects and refinement of the grains.After a long time aging at 400℃,the alloy exhibited ultra-high strength with obvious increasing electrical conductivity.The high strength was attributed to the synergistic effect of work hardening,grain refinement strengthening and precipitation strengthening.The precipitation of a large amount of Ti atoms from the matrix led to the high electrical conductivity of the over-aged sample.

Simple shear extrusion versus equal channel angular pressing:A comparative study on the microstructure and mechanical properties of an Mg alloy

Two severe plastic deformation(SPD)techniques of simple shear extrusion(SSE)and equal channel angular pressing(ECAP)were employed to process an extruded Mg-6Gd-3Y-1.5Ag(wt%)alloy at 553 K for 1,2,4 and 6 passes.The microstructural evolutions were studied by electron back scattered diffraction(EBSD)analysis and transmission electron microscopy(TEM).The initial grain size of 7.5μm in the extruded alloy was reduced to about 1.3μm after 6 SPD passes.Discontinuous dynamic recrystallization was suggested to be operative in both SSE and ECAP,with also a potential contribution of continuous dynamic recrystallization at the early stages of deformation.The difference in the shear strain paths of the two SPD techniques caused different progression rate of dynamic recrystallization(DRX),so that the alloys processed by ECAP exhibited higher fractions of recrystallization and high angle grain boundaries(HAGBs).It was revealed that crystallographic texture was also significantly influenced by the difference in the strain paths of the two SPD methods,where dissimilar basal plane texture components were obtained.The compression tests,performed along extrusion direction(ED),indicated that the compressive yield stress(CYS)and ultimate compressive strength(UCS)of the alloys after both SEE and ECAP augmented continuously by increasing the number of passes.ECAP-processed alloys had lower values of CYS and UCS compared to their counterparts processed by SSE.This difference in the mechanical responses was attributed to the different configurations of basal planes with respect to the loading direction(ED)of each SPD technique.

Superplastic behavior of a fine-grained Mg-Gd-Y-Ag alloy processed by equal channel angular pressing

An extruded Mg-6Gd-3Y-1.5Ag(wt%) alloy was processed by 6 passes of equal channel angular pressing(ECAP) at 553 K using route Bc to refine the microstructure. Electron back-scattered diffraction(EBSD) analysis showed a fully recrystallized microstructure for the extruded alloy with a mean grain size of 8.6 μm. The microstructure of the ECAP-processed alloy was uniformly refined through dynamic recrystallization(DRX). This microstructure contained fine grains with an average size of 1.3 μm, a high fraction of high angle grain boundaries(HAGBs), and nano-sized Mg_(5)Gd-type particles at the boundaries of the DRXed grains, detected by transmission electron microscopy(TEM). High-temperature shear punch testing(SPT) was used to evaluate the superplastic behavior of both the extruded and ECAP-processed alloys by measuring the strain rate sensitivity(SRS) index(m-value). While the highest m-value for the extruded alloy was measured to be 0.24 at 673 K, the ECAP-processed alloy exhibited much higher m-values of 0.41 and 0.52 at 598 and 623 K, respectively,delineating the occurrence of superplastic flow. Based on the calculated average activation energy of 118 kJ mol^(-1) and m-values close to 0.5, the deformation mechanism for superplastic flow at the temperatures of 598 and 623 K for the ECAP-processed alloys was recognized to be grain boundary sliding(GBS) assisted by grain boundary diffusion.

Microstructure and mechanical properties of Mg-Gd-Y-Zr alloy processed by equal channel angular pressing

Microstructure evolution and texture development and their effects on mechanical properties of a Mg-Gd-Y-Zr alloy during equal channel angular pressing（ECAP） were investigated.It is found that the microstructure is still inhomogeneous after four passes,and two zones,namely the fine grain zone（FGZ） and the coarse grain zone（CGZ） are formed.The grain refinement occurs mainly by particle-stimulated nucleation（PSN） mechanism,which led to a more random texture after four passes of ECAP.In the ECAP-processed alloy,the strength did not increase while the ductility was enhanced dramatically compared with the as-received condition.The change of ductility of this alloy was discussed in terms of texture and second phase particles.

Influence of twist extrusion process on consolidation of pure aluminum powder in tubes by equal channel angular pressing and torsion

In comparison with the conventional equal channel angular pressing（ECAP） process,a comprehensive study of influence of twist extrusion（TE） process on consolidating pure aluminum powder in tubes（PITs） by equal channel angular pressing and torsion（ECAPT） was conducted via three-dimensional（3D） finite element simulation,experimental investigation and theoretical analysis.Simulation results revealed that during the consolidation of aluminum powder particles by ECAPT,TE process played a significant role of back pressure.Due to the torsional shear and high hydrostatic pressure exerted by twist channel,both the magnitude and homogeneity of the effective strain were increased markedly.After one pass of ECAPT process using a square channel with an inner angle of 90° and a twist slope angle of 36.5° at 200℃,commercial pure aluminum powder particles were successfully consolidated to nearly full density.Simulation and experimental results showed good agreement.In the microstructure observations,grains were greatly refined.At the same time,porosities were effectively eliminated by shrinking in size and breaking into small ones.Microhardness test indicated that strain distribution of ECAPT-processed billet was more homogeneous with respect to the ECAP-processed one.All these improvements may be attributed to the extreme intense shear strain induced during ECAPT and the increase in self-diffusion coefficient of aluminum due to the back pressure exerted by TE process.

Uniaxial compressive behavior of equal channel angular pressing Al at wide temperature and strain rate range

Uniaxial compressive experiments of ultrafine-grained Al fabricated by equal channel angular pressing(ECAP) method were performed at wide temperature and strain rate range. The influence of temperature on flow stress, strain hardening rate and strain rate sensitivity was investigated experimentally. The results show that both the effect of temperature on flow stress and its strain rate sensitivity of ECAPed Al is much larger than those of the coarse-grained Al. The temperature sensitivity of ultrafine-grained Al is comparatively weaker than that of the coarse-grained Al. Based on the experimental results, the apparent activation volume was estimated at different temperatures and strain rates. The forest dislocation interactions is the dominant thermally activated mechanism for ECAPed Al compressed at quasi-static strain rates, while the viscous drag plays an important role at high strain rates.

Refinement and consolidation of pure Al particles by equal channel angular pressing and torsion

Consolidation of pure Alpowder was conducted at 200 ℃ by equal channel angular pressing and torsion （ECAPT） method. The grain refinement and consolidation behavior were deeply investigated by scan electronic microscopy （SEM） and transmission electronic microscopy （TEM）. The density, hardness and room temperature compression properties of the deformed samples were measured. The experiment results show that ECAPT is an effective method of consolidating powders at relatively low temperatures. Pure A1 particles are successfully consolidated into dense bulk material after 4 passes of ECAPT at 200 ℃. The consolidated material possesses fine grain structure and excellent mechanical properties. The refinement and consolidation mechanisms were analyzed. ECAPT is a promising method to produce the high-performance bulk materials from particles.

Microstructural evolution of a recycled aluminum alloy deformed by equal channel angular pressing process

The microstructural evolution of a recycled aluminum alloy after equal channel angular pressing （ECAP） up to four passes was investigated using X-ray diffxaction （XRD） analysis and transmission electron microscopy （TEM）. Microhardness tests were performed to determine the associated changes in mechanical properties. An ultrafine-grained material has been obtained with a microstructure showing a mixture of highly strained crystallites. A high density of dislocations was achieved as a result of severe plastic deformation （SPD） through the die. Changes in mechanical behavior are also revealed after ECAP due to strain hardening. Thermal analysis and TEM micrographs ob- tained after annealing indicate the succession of the recovery, recrystallization, and grain growth phenomena. Moreover, the energy stored during ECAP may be related to the dislocation density introduced by SPD. We finally emphasize the role played by the precipitates in this alloy.

Effect of annealing temperature on martensitic transformation of Ti_(49.2)Ni_(50.8) alloy processed by equal channel angular pressing

The effect of annealing temperature on the martensitic transformation of a Ti49.2Ni50.8 alloy processed by equal channel angular pressing （ECAP） was investigated by X-ray diffraction （XRD）, transmission electron microscopy （TEM） and differential scanning calorimetry （DSC）. The as-ECAP processed and subsequently annealed Ti49.2Ni50.8 alloys consist of B2 parent phase, Ti4Ni2O phase and B19′ martensite at room temperature. Upon cooling, all samples show B2→R→B19′ two-stage transformation. Upon heating, when the annealing temperature is less than 400℃, the samples show B19′→R→B2 two-stage transformation; when the annealing temperature is higher than 500 ℃, the samples show B19′→B2 single-stage transformation. The B2-R transformation is characterized by wide interval due to the dislocations introduced during ECAP.

EFFECT OF EQUAL-CHANNEL ANGULAR PRESSING ON STRUCTURE OF Al ALLOY 2024

ＥＦＦＥＣＴＯＦＥＱＵＡＬＣＨＡＮＮＥＬＡＮＧＵＬＡＲＰＲＥＳＳＩＮＧＯＮＳＴＲＵＣＴＵＲＥＯＦＡｌＡＬＬＯＹ２０２４①ＬｉｕＺｕｙａｎ，ＬｉａｎｇＧｕｏｘｉａｎ，ＷａｎｇＥｒｄｅ，ＷａｎｇＺｈｏｎｇｒｅｎＳｃｈｏｏｌｏｆＭａｔｅｒｉａｌｓＳｃｉｅ...

Reducing the tension-compression yield asymmetry of extruded Mg-Zn-Ca alloy via equal channel angular pressing

The influence of equal channel angular pressing on the tension-compression yield asymmetry of extruded Mg-5.3 Zn-0.6 Ca(weight percent)alloy has been investigated.The microstructure was obviously refined by the large strain during the equal channel angular pressing,accompanied with very fine Ca_(2)Mg_(6)Zn_(3) phases with average diameter of 70 nm.The weak tension-compression yield asymmetry after equal channel angular pressing is mainly attributed to the reduced volume fraction of extension twinning during the compression,because the slope(k)of twinning in Hall-Petch relationship is higher than that of dislocation slip,and the twinning deformation is difficult to take place with decreasing grain size.The basal slip is more active in the alloy after equal channel angular pressing,due to the non-basal texture components,which hinders the twinning activation and reduces the yield asymmetry.Furthermore,the presence of fine precipitate restricts the twinning activation,which also contributes to the reduction of yield asymmetry.

The effect of Equal Channel Angular Pressing process on the microstructure of AZ31 Mg alloy strip shaped specimens

Equal Channel Angular Pressing(ECAP)is one of the most applicable Sever Plastic Deformation(SPD)processes which leads to strength and ductility improvement through the grain refining and development of a suitable texture.In this study,after designing and manufacturing a suitable die,4 pass ECAP process at route C is done on strip shaped specimens of AZ31 magnesium alloy in order to achieve desirable microstructural and mechanical properties.Microstructure then got studied through the optical microscopy.Results show that mean grain size is decreased and grain size distribution got close to normal distribution state by increasing the pass number.However,the grain size is reduced by increasing of ECAP temperature.

Microstructure evolution and mechanical behavior of AZ31 Mg alloy processed by equal-channel angular pressing

AZ31 Mg alloy bar was subjected to 8-pass equal-channel angular pressing(ECAP) at 623 K. Microstructure evolution was observed by optical microscopy(OM) on cross section and X-ray diffraction analysis. The room temperature mechanical properties of the ECAP processed specimens were also investigated. A fine-grained structure with an average sub-grain size of 9 μm is obtained after 7 ECAP passes. XRD analysis indicates that after ECAP,in placing of {1 010},planes {1 011} and {1 012} become the dominant directions that are favourable for grain refinement. ECAP processed AZ31 Mg alloy exhibits significant improvement in elongation but decrease in strength. The elongation of the specimen increases continuously up to 2 passes and then remains stable at further passes. This improvement can be related to the evolution of crystallographic texture and the scattered orientation of the basal plane(0001).

Microstructure and texture evolution of Al-7075 alloy processed by equal channel angular pressing

Equal channel angular pressing is an effective technique to control the texture and microstructure of metals and alloys. Texture and microstructure of an Al-7075 alloy subjected to repetitive equal channel angular pressing through a 90° die were evaluated by X-ray diffractometer and orientation imaging microscopy. It is observed that processing through different routes leads to different types of textures, in both qualitative and quantitative senses. The texture calculation by Labotex software reveals that texture strengthens after the first pass and weakens by progressing ECAP process up to 4 passes. Microstructure investigations show that after 4 passes of equal channel angular pressing via routes BC and A, very fine grains with average grain size of about 700 nm and 1 μm appear, respectively, and most of the grains evolve into arrays of high angle boundaries. The effects of covering the Al-7075 billets with copper tube on texture and microstructure were also studied.

Effect of Y content and equal channel angular pressing on the microstructure, texture and mechanical property of extruded Mg-Y alloys

The microstructure, texture and mechanical property evolution of the extruded Mg-x Y(x = 1, 5 wt.%) alloys during equal channel angular pressing(ECAP) were systematically investigated using an optical microscope, electron backscatter diffraction(EBSD) and uniaxial tensile test. The Mg-Y alloys exhibited a weakened basal texture before the ECAP, and the texture was further weakened with the max basal poles dispersed along ~45° between the extrusion direction and the transverse direction after the ECAP. The Mg-5 Y alloys always exhibited a finer grain size comparing to that of Mg-1 Y for the same ECAP process. With a proper ECAP process, both the strength and elongation of Mg-5 Y alloy could be improved simultaneously after the ECAP, i.e., the yield strength(273.9 ± 1.2 MPa), ultimate strength(306.4 ± 3.0 MPa),and elongation(23.9 ± 1.0%) were increased by 10%, 6%, and 72%, respectively, comparing to that before the ECAP. This was considered to be arose from the combined effects of grain refinement, significant improved microstructure homogeneity and solid solution hardening.In addition, it was found that Mg-Y alloy with better comprehensive properties could be obtained by the decreasing-temperature ECAP processes. The yield strength-grain size relationship could be well described by the Hall-Petch relation for all the ECAPed Mg-Y alloys,which was consistent with that the texture changes did not significantly affect the average Schmid factors of basal, prismatic and pyramidal slips for both Mg-Y alloys.

Microstructure and mechanical property of a high-strength Mg-10Gd-6Y-1.5Zn-0.5Zr alloy prepared by multi-pass equal channel angular pressing

In this work,a high-strength Mg–10Gd–6Y–1.5Zn–0.5Zr(wt.%)alloy was fabricated by successive multi-pass equal channel angular pressing(ECAP).The microstructure and mechanical property of as-cast and ECAP alloys were systematically researched by X-ray diffractometer,scanning electron microscopy,transmission electron microscopy and compression test.The results show that the microstructure of as-cast alloy consists ofα-Mg grains,Mg24Y5 networks,18R blocks,fine 14H lamellas,and fewY-rich particles.After 8 passes ECAP,dynamic recrystallization ofα-Mg is developed and their average grain size decreases to about 1μm.The network Mg_(24)Y_(5) phase at grain boundaries is broken into small particles with average diameter lower than 0.5μm.Moreover,18R blocks are kinked and delaminated,or broken into small particles and blended with Mg24Y5 particles.14H lamellas grow gradually or are dynamically precipitated within certainα-Mg grains.Compression tests indicate that 8p ECAP alloy exhibits excellent mechanical property with compressive strength of 537 MPa and fracture strain of 17.0%.The significant improvement for both strength and ductility of deformed alloy could be ascribed to DRX grains,refined Mg24Y5 particles,18R kinking and dynamical precipitation of 14H.

Microstructure and mechanical properties of ZE10 magnesium alloy prepared by equal channel angular pressing

ZE10 magnesium alloy was subjected to equal-channel angular pressing （ECAP） up to 12 passes in a die with an angle of 120° between the two channels at 250-300℃. An inhomogeneous microstructure of bimodal grains including fine grains of 1-2 μm as well as coarse grains of about 20μm was obtained after the initial 1-4 ECAP passes. The grain size became increasingly homogeneous with further ECAP processing and the grains were significantly refined to 1-2 ktm after 8 passes and further refined to 0.5-1 μm after 12 passes. The alloy＇s yield strength changed slightly but the ductility improved greatly initially up to 4-6 passes corresponding to the bimodal grain microstructure. And after the subsequent pressing of more than 8 passes, the tensile strength including yield strength improved while the elongation decreased gradually.

Mechanical responses, texture and microstructural evolution of high purity aluminum deformed by equal channel angular pressing

Ultrafine-grained(UFG) high purity aluminum exhibits a variety of attractive mechanical properties and special deformation behavior. Equal channel angular pressing(ECAP) process can be used to easily and effectively refine metals. The microstructure and microtexture evolutions and grain boundary characteristics of the high purity aluminum(99.998%) processed by ECAP at room temperature are investigated by means of TEM and EBSD. The results indicate that the shear deformation resistance increases with repeated EACP passes, and equiaxed grains with an average size of 0.9 μm in diameter are formed after five passes. Although the orientations distribution of grains tends to evolve toward random orientations, and microtextures(80°, 35°, 0°),(40°, 75°, 45°) and(0°, 85°, 45°) peak in the sample after five passes. The grain boundaries in UFG aluminum are high-angle geometrically necessary boundaries. It is suggested that the continuous dynamic recrystallization is responsible for the formation of ultrafine grains in high purity aluminum. Microstructure evolution in the high purity aluminum during ECAP is proposed.

Friction stir welding of AZ31 magnesium alloys processed by equal channel angular pressing

Equal channel angular pressing （ECAP） is an effective thermo-mechanical process to make ultrafine grains. An investigation was carried out on the friction stir welding （FSW） of ECAPed AZ31 magnesium alloys with a thickness of 15 mm. For different process parameters, the optimum FSW conditions of ECAPed AZ31 magnesium alloys were examined. The basic characterization of weld formation and the mechanical properties of the joints were discussed. The results show that the effect of welding parameters on welding quality was evident and welding quality was sensitive to welding speed. Sound joints could be obtained when the welding speed was 37.5 mm/min and the rotation speed of the stir tool was 750 r/min. The maximum tensile strength （270 MPa） of FSW was 91% that of the base materials. The value of microhardness varied between advancing side and retreating side because of the speed field near the pin of the stir tool, which weakened the deformed stress field. The value of microhardness of the welding zone was lower than that of the base materials. The maximum value was located near the heat-affected zone （HAZ）. Remarkable ductile character was observed from the fracture morphologies of welded joints.

DSC analysis of commercial Cu-Cr-Zr alloy processed by equal channel angular pressing

Samples of a commercial Cu-lCr-0.1Zr(mass fraction,%) alloy were subjected to equal channel angular pressing(ECAP) up to 16 passes at room temperature following route Bc.Differential scanning calorimetry(DSC) was used to highlight the precipitation sequence and to calculate the stored energy,recrystallization temperature and activation energy after each ECAP pass.On another hand,electrical properties were correlated with the dislocation density.Results show that the stored energy increases upon increasing ECAP pass numbers,while the recrystallization temperature decreases significantly.