The tensile creep deformation and damage evolution in a Ni-base superalloy at 900℃/170MPa were investigated. At the first creep stage, abnormal creep occured due to the resolution of fine particles, and the deformati...The tensile creep deformation and damage evolution in a Ni-base superalloy at 900℃/170MPa were investigated. At the first creep stage, abnormal creep occured due to the resolution of fine particles, and the deformation initiated from grain boundary areas. It is evident that nearly all of the dislocations were in γ matrix channels in form of dislocation pairs and the dislocations were impeded at γ/γ' interfaces, thus the dislocation networks developed deformation. At the steady creep stage, impeded dislocations atγ/γ' interfaces climbed over γ' phases by diffusion-dominant mechanism. At the last creep stage, voids were formed around carbides at grain boundary which leaded to accumulated damage and caused creep rate accelerated. With the dislocation networks being broken, the voids connected and grew into micro-cracks gradually. Finally the cracks propagated along grain boundary area and resulted in failure.展开更多
文摘The tensile creep deformation and damage evolution in a Ni-base superalloy at 900℃/170MPa were investigated. At the first creep stage, abnormal creep occured due to the resolution of fine particles, and the deformation initiated from grain boundary areas. It is evident that nearly all of the dislocations were in γ matrix channels in form of dislocation pairs and the dislocations were impeded at γ/γ' interfaces, thus the dislocation networks developed deformation. At the steady creep stage, impeded dislocations atγ/γ' interfaces climbed over γ' phases by diffusion-dominant mechanism. At the last creep stage, voids were formed around carbides at grain boundary which leaded to accumulated damage and caused creep rate accelerated. With the dislocation networks being broken, the voids connected and grew into micro-cracks gradually. Finally the cracks propagated along grain boundary area and resulted in failure.