Er3 +/Yb3 +-codoped oxyfluoride crystallite glass was prepared with melting technique. The compositions and the melting temperature and the annealing temperature of the rare earth-doped crystallite glass were studied ...Er3 +/Yb3 +-codoped oxyfluoride crystallite glass was prepared with melting technique. The compositions and the melting temperature and the annealing temperature of the rare earth-doped crystallite glass were studied in detail. The emission spectra of samples were measured with the Hitachi F-4500 fluorescent photometer pumped by 980 nm wavelength laser. The up-conversion luminescence mechanism was illuminated on the view of the photophysics. By measuring the relationship between luminescent intensity and pump power, it is confirmed that the emission peaks at 550 nm belong to two-photon process, while that at 665 nm belongs to three-photon process. Moreover, the distributions of crystalline were determined by SEM.展开更多
A laser-diode-pumped 1.54-μm passive Q-switched erbium doped glass laser was reported. We utilize a laser diode with wavelength of 973nm to pump a 1-mm Er/Yb co-doped phosphate glass with the erbium and ytterbium con...A laser-diode-pumped 1.54-μm passive Q-switched erbium doped glass laser was reported. We utilize a laser diode with wavelength of 973nm to pump a 1-mm Er/Yb co-doped phosphate glass with the erbium and ytterbium concentrations of 1 wt.% and 21 wt.%, respectively. A Co^2+ :MgAl2O4 slab crystal was used as a passive Q- switcher. Q-switched pulses with repetition frequency of 800Hz, width of 7.4ns, peak power of 2.2kW and average power of 13.3 m W were obtained when absorbed pump power was 4 75 m W. A sandwich structure of the Q- switched microchip Er/Yb glass laser was demonstrated, which shows shorter pulse width of 6.8 ns. Dependences of pulse duration and repetition frequency on pump power were also investigated.展开更多
The glass sample based on the composition of 45PbF_2-45GeO_2-10WO_3 co-doped with Yb^(3+)/Er^(3+) was prepared by the fusion method in two steps: melted at 950 ℃ for 20~25 min then annealed at 380 ℃ for 4 h. Throug...The glass sample based on the composition of 45PbF_2-45GeO_2-10WO_3 co-doped with Yb^(3+)/Er^(3+) was prepared by the fusion method in two steps: melted at 950 ℃ for 20~25 min then annealed at 380 ℃ for 4 h. Through the V-prism it is found that the refractive index of host glass and the sample are 1.517 and 1.65 respectively. The transmittance was observed by using the ultraviolet-visible-infrared spectrometer in the wavelength range from 0.35 to 2.5μm. The transmittance of the host glass is beyond 73%. That of the sample is beyond 50% and there are characteristic absorption peaks of rare-earth ions. The emission spectrum was measured by using the Hitachi F-4500 fluorescent spectrometer pumped by 980 nm semiconductor laser. There are a strong emission peak at 530 nm and a weak peak at 650 nm.展开更多
yb^3+:Er^3+ co-doped oxy-fluoride ceramics glass has been prepared. The mechanism of up-conversion emissions about Er^3+ was discussed, and the temperature properties of green up-conversion fluorescence between 30...yb^3+:Er^3+ co-doped oxy-fluoride ceramics glass has been prepared. The mechanism of up-conversion emissions about Er^3+ was discussed, and the temperature properties of green up-conversion fluorescence between 303 and 823 K were investigated. The results show that the sensitivity of this sample reaches its maximum value, about 0.0047 K^-1, when the temperature is 383 K, indicating that this kind of sample can be used as high temperature and high sensitivity optical temperature sensor.展开更多
Transparent Tm^3+/Er^3+/yb^3+ co-doped oxyfluorogermanate glass ceramics containing BaF2 nanocrystals are prepared. Under excitation of a 980-nm laser diode (LD), compared with the glass before heat treatment, th...Transparent Tm^3+/Er^3+/yb^3+ co-doped oxyfluorogermanate glass ceramics containing BaF2 nanocrystals are prepared. Under excitation of a 980-nm laser diode (LD), compared with the glass before heat treatment, the Tm^3+/Er^3+/yb^3+ co-doped oxyfluorogermanate glass ceramics can emit intense blue, green and red up-conversion luminescence and Stark- split peaks; X-ray diffraction (XRD) and transmission electron microscope (TEM) results show that BaF2 nanocrystals with an average diameter of 20 nm are precipitated from the glass matrix. Stark splitting of the up-conversion luminescence peaks in the glass ceramics indicates that Tm^3+, Er^3+ and (or) Yb^3+ ions are incorporated into the BaF2 nanocrystals. The up-conversion luminescence intensities of Tm^3+, Er^3+ and the splitting degree of luminescence peaks in the glass ceramics increase significantly with the increase of heat treat temperature and heat treat time extension. In addition, the possible energy transfer process between rare earth ions and the up-conversion luminescence mechanism are also proposed.展开更多
文摘Er3 +/Yb3 +-codoped oxyfluoride crystallite glass was prepared with melting technique. The compositions and the melting temperature and the annealing temperature of the rare earth-doped crystallite glass were studied in detail. The emission spectra of samples were measured with the Hitachi F-4500 fluorescent photometer pumped by 980 nm wavelength laser. The up-conversion luminescence mechanism was illuminated on the view of the photophysics. By measuring the relationship between luminescent intensity and pump power, it is confirmed that the emission peaks at 550 nm belong to two-photon process, while that at 665 nm belongs to three-photon process. Moreover, the distributions of crystalline were determined by SEM.
基金Supported by the Program for the New Century Excellent Talents, Excellent Young Teachers in Universities and Scientific Research Foundation for Returned 0verseas Chinese Scholars by M0E and the Natural Science Foundation of Tianjin City 05YFGPGX05100.
文摘A laser-diode-pumped 1.54-μm passive Q-switched erbium doped glass laser was reported. We utilize a laser diode with wavelength of 973nm to pump a 1-mm Er/Yb co-doped phosphate glass with the erbium and ytterbium concentrations of 1 wt.% and 21 wt.%, respectively. A Co^2+ :MgAl2O4 slab crystal was used as a passive Q- switcher. Q-switched pulses with repetition frequency of 800Hz, width of 7.4ns, peak power of 2.2kW and average power of 13.3 m W were obtained when absorbed pump power was 4 75 m W. A sandwich structure of the Q- switched microchip Er/Yb glass laser was demonstrated, which shows shorter pulse width of 6.8 ns. Dependences of pulse duration and repetition frequency on pump power were also investigated.
文摘The glass sample based on the composition of 45PbF_2-45GeO_2-10WO_3 co-doped with Yb^(3+)/Er^(3+) was prepared by the fusion method in two steps: melted at 950 ℃ for 20~25 min then annealed at 380 ℃ for 4 h. Through the V-prism it is found that the refractive index of host glass and the sample are 1.517 and 1.65 respectively. The transmittance was observed by using the ultraviolet-visible-infrared spectrometer in the wavelength range from 0.35 to 2.5μm. The transmittance of the host glass is beyond 73%. That of the sample is beyond 50% and there are characteristic absorption peaks of rare-earth ions. The emission spectrum was measured by using the Hitachi F-4500 fluorescent spectrometer pumped by 980 nm semiconductor laser. There are a strong emission peak at 530 nm and a weak peak at 650 nm.
基金Project supported by the National Natural Science Foundation of China (Grant No. 10804015 )the Science Foundation of the Education Department of Liaoning Province of China (Grant No. 2009A417)
文摘yb^3+:Er^3+ co-doped oxy-fluoride ceramics glass has been prepared. The mechanism of up-conversion emissions about Er^3+ was discussed, and the temperature properties of green up-conversion fluorescence between 303 and 823 K were investigated. The results show that the sensitivity of this sample reaches its maximum value, about 0.0047 K^-1, when the temperature is 383 K, indicating that this kind of sample can be used as high temperature and high sensitivity optical temperature sensor.
基金Project supported by the National Natural Science Foundation of China (Grant Nos.61265004 and 51272097)the Specialized Research Fund for the Doctoral Program of Higher Education of China (Grant No.20125314120018)
文摘Transparent Tm^3+/Er^3+/yb^3+ co-doped oxyfluorogermanate glass ceramics containing BaF2 nanocrystals are prepared. Under excitation of a 980-nm laser diode (LD), compared with the glass before heat treatment, the Tm^3+/Er^3+/yb^3+ co-doped oxyfluorogermanate glass ceramics can emit intense blue, green and red up-conversion luminescence and Stark- split peaks; X-ray diffraction (XRD) and transmission electron microscope (TEM) results show that BaF2 nanocrystals with an average diameter of 20 nm are precipitated from the glass matrix. Stark splitting of the up-conversion luminescence peaks in the glass ceramics indicates that Tm^3+, Er^3+ and (or) Yb^3+ ions are incorporated into the BaF2 nanocrystals. The up-conversion luminescence intensities of Tm^3+, Er^3+ and the splitting degree of luminescence peaks in the glass ceramics increase significantly with the increase of heat treat temperature and heat treat time extension. In addition, the possible energy transfer process between rare earth ions and the up-conversion luminescence mechanism are also proposed.