Gd3Sc2Ga3O12 polycrystalline material for single crystal growth was prepared with Ga, Gd2O3 and Sc2O3 as starting materials and aqueous ammonia as the precipitator by co-precipitation method. The precursors sintered a...Gd3Sc2Ga3O12 polycrystalline material for single crystal growth was prepared with Ga, Gd2O3 and Sc2O3 as starting materials and aqueous ammonia as the precipitator by co-precipitation method. The precursors sintered at various temperatures were characterized by infrared spectra （IR）, X-ray diffractometry （XRD） and transmitted electron microscopy （TEM）. The results showed that pure GSGG phase could be obtained at 900 ℃. The sintered powders were well-dispersed and less-aggregated in the sintered temperature range of 900 - 1000 ℃. XRD and TEM show that the polycrystalline particle sizes of the polycrystalline powders were about 20 - 50 nm. Compared with the method that Ga2O3, Gd2O3 and Sc2O3 were mixed directly and sintered to get polycrystalline materials, the synthesized temperature was lower and sintered time was shorter. Thus co-precipitation was a good method to synthesize GSGG polycrystalline material.展开更多
Absorption, excitation and emission spectra as well as decay time measurements at 10, 77, and 300 K were perfumed for Gd3Sc2Ga3O12 garnet single-crystal doped with Cr^3＋ and Nd^3＋ ions. Strong reabsorption of Cr3＋ ...Absorption, excitation and emission spectra as well as decay time measurements at 10, 77, and 300 K were perfumed for Gd3Sc2Ga3O12 garnet single-crystal doped with Cr^3＋ and Nd^3＋ ions. Strong reabsorption of Cr3＋ emission by Nd3＋ absorption lines was ob- served. The assignments of f-f and d-d transitions were proposed. The broad emission band of chromium ions is an indication that weak/intermediate crystal field strength is present at the Cr3＋ site.展开更多
基金Project supported by the National Natural Science Foundation of China (50472104 60478025)
文摘Gd3Sc2Ga3O12 polycrystalline material for single crystal growth was prepared with Ga, Gd2O3 and Sc2O3 as starting materials and aqueous ammonia as the precipitator by co-precipitation method. The precursors sintered at various temperatures were characterized by infrared spectra （IR）, X-ray diffractometry （XRD） and transmitted electron microscopy （TEM）. The results showed that pure GSGG phase could be obtained at 900 ℃. The sintered powders were well-dispersed and less-aggregated in the sintered temperature range of 900 - 1000 ℃. XRD and TEM show that the polycrystalline particle sizes of the polycrystalline powders were about 20 - 50 nm. Compared with the method that Ga2O3, Gd2O3 and Sc2O3 were mixed directly and sintered to get polycrystalline materials, the synthesized temperature was lower and sintered time was shorter. Thus co-precipitation was a good method to synthesize GSGG polycrystalline material.
基金supported by Ministry of Science and Higher Education (N N507 372335)
文摘Absorption, excitation and emission spectra as well as decay time measurements at 10, 77, and 300 K were perfumed for Gd3Sc2Ga3O12 garnet single-crystal doped with Cr^3＋ and Nd^3＋ ions. Strong reabsorption of Cr3＋ emission by Nd3＋ absorption lines was ob- served. The assignments of f-f and d-d transitions were proposed. The broad emission band of chromium ions is an indication that weak/intermediate crystal field strength is present at the Cr3＋ site.