The up-conversion luminescence composite NaYF4：Er3＋/TiO2 is prepared using the sol-gel method. The specimen has good crystallinity and two shapes, i.e., viereck and round, while the sizes of viereck and round partic...The up-conversion luminescence composite NaYF4：Er3＋/TiO2 is prepared using the sol-gel method. The specimen has good crystallinity and two shapes, i.e., viereck and round, while the sizes of viereck and round particles are both micron-sized. The TiO2 has an anatase structure, while the NaYF4 has a hexagonal phase, which can be hardly obtained through the common sol-gel method. Due to the big particle size and the high crystallinity of pure NaYF4： Er3＋, the composite has a small specific surface area that is less than Degussa P25 TiO2. The NaYF4：Er3＋/TiO2 composite shows several emission peaks at 211, 237, and 251 nm under the excitation of 388 nm, at 395 nm and 411 nm under the excitation of 500 nm, and at 467, 481,492, and 508 nm under the excitation of 570 nm.展开更多
Hexagonal NaYF4:Yb3+,Er3+ (β-NaYF4:Yb3+,Er3+) nanoparticles supported on TiO2 nanobelts were prepared using two-step pro- cedures of ion-exchangeable process and hydrothermal treatment: layered titanate nanobelts wer...Hexagonal NaYF4:Yb3+,Er3+ (β-NaYF4:Yb3+,Er3+) nanoparticles supported on TiO2 nanobelts were prepared using two-step pro- cedures of ion-exchangeable process and hydrothermal treatment: layered titanate nanobelts were first ion-exchanged with Y3+, Yb3+ and Er3+ cations to produce titanate nanobelts with these cations, and then, the product nanobelts in NaY solution were treated under hydrothermal con- dition to transform into anatase TiO2 nanobelts supported with β-NaYF4:Yb3+,Er3+ nanoparticles. The final p...展开更多
基金Project supported by the National Natural Science Foundation of China (Grant No. 20876125)the Research Fund for the Doctoral Program of Higher Education of China (Grant No. 20096101110013)the Northwest University Graduate Cross-Discipline Funds (Grant Nos. 09YJC27,09YJC24,and 201031)
文摘The up-conversion luminescence composite NaYF4：Er3＋/TiO2 is prepared using the sol-gel method. The specimen has good crystallinity and two shapes, i.e., viereck and round, while the sizes of viereck and round particles are both micron-sized. The TiO2 has an anatase structure, while the NaYF4 has a hexagonal phase, which can be hardly obtained through the common sol-gel method. Due to the big particle size and the high crystallinity of pure NaYF4： Er3＋, the composite has a small specific surface area that is less than Degussa P25 TiO2. The NaYF4：Er3＋/TiO2 composite shows several emission peaks at 211, 237, and 251 nm under the excitation of 388 nm, at 395 nm and 411 nm under the excitation of 500 nm, and at 467, 481,492, and 508 nm under the excitation of 570 nm.
基金Project supported by the "973" Basic Research Foundation of China (2006CB932605)the National Natural Science Foundation of China (20976002)
文摘Hexagonal NaYF4:Yb3+,Er3+ (β-NaYF4:Yb3+,Er3+) nanoparticles supported on TiO2 nanobelts were prepared using two-step pro- cedures of ion-exchangeable process and hydrothermal treatment: layered titanate nanobelts were first ion-exchanged with Y3+, Yb3+ and Er3+ cations to produce titanate nanobelts with these cations, and then, the product nanobelts in NaY solution were treated under hydrothermal con- dition to transform into anatase TiO2 nanobelts supported with β-NaYF4:Yb3+,Er3+ nanoparticles. The final p...