Oxyfluoride glasses were developed with composition 60GeO 2 ·10AlF 3 ·25BaF 2 ·（1.95-x）GdF 3 · 3YbF 3 ·0.05TmF 3 ·xErF 3 （x=0.02,0.05,0.08,0.11,0.14,0.17）in mole percent.Intense blue...Oxyfluoride glasses were developed with composition 60GeO 2 ·10AlF 3 ·25BaF 2 ·（1.95-x）GdF 3 · 3YbF 3 ·0.05TmF 3 ·xErF 3 （x=0.02,0.05,0.08,0.11,0.14,0.17）in mole percent.Intense blue（476 nm）,green（524 and 546 nm）and red（658 nm）emissions which identified from the 1G 4 →3H 6 transition of Tm3＋and the（2H 11/2 ,4S 3/2 ）→4I 15/2 ,4F 9/2 →4I 15/2 transitions of Er3＋,respectively,were simultaneously observed under 980 nm excitation at room temperature.The results show that multicolor luminescence including white light can be adjustably tuned by changing doping concentrations of Er3＋ion or the excitation power.In addition,the energy transfer processes among Tm3＋,Er3＋and Yb3＋ions,and up-conversion mechanisms are discussed.展开更多
The Yb3+/Er3+ doped TeO2-WO3-ZnO glasses were prepared. The absorption spectra, emission spectra and fluorescence lifetime of Er3+ at 1.5 um, excited by 970 nm were measured. The influence of Er2O3, Yb2O3 and OH-conte...The Yb3+/Er3+ doped TeO2-WO3-ZnO glasses were prepared. The absorption spectra, emission spectra and fluorescence lifetime of Er3+ at 1.5 um, excited by 970 nm were measured. The influence of Er2O3, Yb2O3 and OH-contents on emission properties of Er3+ at 1.5μm was investigated. The optimum doping concentrations for Er3+ and Yb3+ is around 3.34×1020 ions/cm3 and 6.63×1020 ions/cm3, respectively. The peak emission cross section is 0.83~0.87 pm2. With the increasing concentration of Yb3+, the FWHM of Er3+ emission at 1.5μm in the glass increases from 77 nm to 83 nm. The results show that Yb3+/Er3+ doped TeO2-WO3-ZnO glasses are promising candidate for Er3+-doped broadband optical amplifier.展开更多
To simulate the effects of burnable poison doping in nuclear fuel UO2,Er2O3(or Gd2O3)-doped CeO2 pellets were prepared. Changes in lattice constant and atomic disordering for CeO2 due to the Er2O3 and Gd2O3 doping wer...To simulate the effects of burnable poison doping in nuclear fuel UO2,Er2O3(or Gd2O3)-doped CeO2 pellets were prepared. Changes in lattice constant and atomic disordering for CeO2 due to the Er2O3 and Gd2O3 doping were measured by means of XRD and XAFS. By the Er2O3 doping,the lattice constant decreased,and a disordering of lattice structure was induced in the samples. The doping with Er2O3 also induced the disordering of atomic arrangement around Er atoms,which was observed through the change in XAFS spectra. In contrast,the effect of Gd2O3 doping was smaller than that of Er2O3 doping. The result was discussed in terms of ionic size of dopants in CeO2 crystal.展开更多
基金Funded by the National Natural Science Foundation of China (No. 50772045)the Society Development Foundation of Yunnan Province (No. 2007E036M)
文摘Oxyfluoride glasses were developed with composition 60GeO 2 ·10AlF 3 ·25BaF 2 ·（1.95-x）GdF 3 · 3YbF 3 ·0.05TmF 3 ·xErF 3 （x=0.02,0.05,0.08,0.11,0.14,0.17）in mole percent.Intense blue（476 nm）,green（524 and 546 nm）and red（658 nm）emissions which identified from the 1G 4 →3H 6 transition of Tm3＋and the（2H 11/2 ,4S 3/2 ）→4I 15/2 ,4F 9/2 →4I 15/2 transitions of Er3＋,respectively,were simultaneously observed under 980 nm excitation at room temperature.The results show that multicolor luminescence including white light can be adjustably tuned by changing doping concentrations of Er3＋ion or the excitation power.In addition,the energy transfer processes among Tm3＋,Er3＋and Yb3＋ions,and up-conversion mechanisms are discussed.
文摘The Yb3+/Er3+ doped TeO2-WO3-ZnO glasses were prepared. The absorption spectra, emission spectra and fluorescence lifetime of Er3+ at 1.5 um, excited by 970 nm were measured. The influence of Er2O3, Yb2O3 and OH-contents on emission properties of Er3+ at 1.5μm was investigated. The optimum doping concentrations for Er3+ and Yb3+ is around 3.34×1020 ions/cm3 and 6.63×1020 ions/cm3, respectively. The peak emission cross section is 0.83~0.87 pm2. With the increasing concentration of Yb3+, the FWHM of Er3+ emission at 1.5μm in the glass increases from 77 nm to 83 nm. The results show that Yb3+/Er3+ doped TeO2-WO3-ZnO glasses are promising candidate for Er3+-doped broadband optical amplifier.
基金Project supported by Japan Society for the Promotion of Science (JSPS) Research (Grant-in-aid for Scientific Research B No. 21360469)the Osaka Nuclear Science Association (ONSA),the XAFS Measurements at KEK-PF were Performed with the Approval of KEK (2009G536)
文摘To simulate the effects of burnable poison doping in nuclear fuel UO2,Er2O3(or Gd2O3)-doped CeO2 pellets were prepared. Changes in lattice constant and atomic disordering for CeO2 due to the Er2O3 and Gd2O3 doping were measured by means of XRD and XAFS. By the Er2O3 doping,the lattice constant decreased,and a disordering of lattice structure was induced in the samples. The doping with Er2O3 also induced the disordering of atomic arrangement around Er atoms,which was observed through the change in XAFS spectra. In contrast,the effect of Gd2O3 doping was smaller than that of Er2O3 doping. The result was discussed in terms of ionic size of dopants in CeO2 crystal.