Investigation on the Phase Diagram of Ternary System ErCl_3-CaCl_2-LiCl

The phase diagram of ternary system ErCl_3-CaCl_2-LiCl has been investigated by means of DTA. It was found that there are four fields corresponding to the primary crystallization of ErCl_3,CaCl_2, LiCl and Li_3ErCl_6 respectively, five univariant curves related to the secondary crystallization, a ternary eutectic E(58. 5% ErCl_3, 23. 7% CaCl_2, 17. 8%LiCl, 397 ℃) and a ternary peritectic point P(52. 5% ErCl_3, 27. 2% CaCl_2, 20. 3% LiCl, 428 ℃) in the phase diagram. Two ternary reactions occur in the system: L =ErCl_3 + Li_3ErCl_6 +CaCl_2; L+LiCl=Li_3ErCl_6 +CaCl_2.

Phase Diagram of Ternary System ErCl_3-CaCl_2-MgCl_2

The phase diagram of ternary system ErCl_3-CaCl_2-MgCl_2 has been investigated be means of differentialthermal analysis (DTA). It was found that there were three surfaces corresponding to the primary crystalliza-tion of ErCl_3, CaCl_2 and MgCl_2 respectively, three univariant curves related to the a seondary crystallizationand a ternary eutectic point E (67. 8 wt% ErCl_3, 17. 2 wt% CaCl_2, 15. 0 wt% MgCl_2. 524°C ) in the systemErCl_3-CaCl_2-MgCl_2.

冶炼时添加ErCl_3对AZ91镁合金组织与性能的影响

研究了冶炼AZ91镁合金时添加不同量的ErCl3对镁合金的拉伸性能、组织和断口形貌的影响。结果表明:添加ErCl3具有阻燃、净化作用,还可以提高合金的抗拉强度σb和延伸率δ。当添加ErCl3质量分数为1.8%时,σb和δ分别从156MPa和1.8%上升到最大值220MPa和4.1%,分别提高了41%和128%。随着ErCl3加入量的进一步提高,开始形成Al7ErMn5稀土相和稀土氧化物夹杂,合金的力学性能反而下降。添加ErCl3增加了二次裂纹的数量,但是不改变镁合金的断裂机制,断口形貌仍为准解理断裂。

ErCl_3－CaCl_2－LiCl三元体系相图的研究

利用ＤＴＡ研究了ＥｒＣｌ_３ＣａＣｌ_２ＬｉＣｌ三元体系相图。发现该相图有对应于ＥｒＣｌ_３、ＣａＣｌ_２、ＬｉＣｌ和Ｌｉ_３ＥｒＣｌ_６的４个液相面，５条二次结晶线，一个三元低共熔点Ｅ（５８．５％ＥｒＣｌ_３，２３．７％ＣａＣｌ_２，１７．８％ＬｉＣｌ，３９７℃），一个三元转熔点Ｐ（５２．５％ＥｒＣｌ_３，２７．２％ＣａＣｌ_２，２０．３％ＬｉＣｌ，４２８℃）。相应的４相平衡反应为：Ｌ＝ＥｒＣｌ_３＋Ｌｉ_３ＥｒＣｌ_６＋ＣａＣｌ_２；Ｌ＋ＬｉＣｌ＝Ｌｉ_３ＥｒＣｌ_６＋ＣａＣｌ_２．

ErCl_3－MgCl_2－LiCl三元体系的液相限

ＥｒＣｌ＿３－ＭｇＣｌ＿２－ＬｉＣｌ三元体系的液相限彭绍琴，郑朝贵（北京大学化学系北京１００８７１）关键词ＥｒＣｌ＿３，ＥｒＣｌ＿３－ＭｇＣｌ＿２－ＬｉＣｌ三元体系，相图研究稀土熔盐相图对于了解稀土化合物的基本物理化学性质，从已知相图提取热力学数据，...

石墨炉原子吸收光谱法中氯化铒和硝酸铒的背景吸收特性研究

研究了石墨炉原子吸收光谱法中ＥｒＣｌ３、Ｅｒ（ＮＯ３）３基体的背景吸收影响。背景吸收波长特性的研究说明，ＥｒＣｌ３与Ｅｒ（ＮＯ３）３的背景吸收都具有明显的波长特性。将铒基体转化为Ｅｒ（ＮＯ３）３有利于降低背景吸收值。ＥｒＣｌ３背景吸收的时间特性和原子化温度与原子化方式有关。铒基体的背景吸收峰高与灰化温度有关。