The phase diagram of ternary system ErCl_3-CaCl_2-MgCl_2 has been investigated be means of differentialthermal analysis (DTA). It was found that there were three surfaces corresponding to the primary crystalliza-tion ...The phase diagram of ternary system ErCl_3-CaCl_2-MgCl_2 has been investigated be means of differentialthermal analysis (DTA). It was found that there were three surfaces corresponding to the primary crystalliza-tion of ErCl_3, CaCl_2 and MgCl_2 respectively, three univariant curves related to the a seondary crystallizationand a ternary eutectic point E (67. 8 wt% ErCl_3, 17. 2 wt% CaCl_2, 15. 0 wt% MgCl_2. 524°C ) in the systemErCl_3-CaCl_2-MgCl_2.展开更多
Based on the thermodynamically self-consistent analysis and optimization of three sub-binary systems of the ternary system PrCl_3-CaCl_2-MgCl_2,the thermodynamics of this ternary system has been studied.Using Hillert ...Based on the thermodynamically self-consistent analysis and optimization of three sub-binary systems of the ternary system PrCl_3-CaCl_2-MgCl_2,the thermodynamics of this ternary system has been studied.Using Hillert model and taking MgCl_2 as an asymmetric component,the PrCl_3-CaCl_2-MgCl_2 phase diagram has been calculated.The agreement between calculated and measured compositions and temperatures at deflecting points on liquidus is good.The system is a simple eutectic one with a eutectic point at 26.0mol% PrCl_3, 41.5mol% CaCl_2,32.5mol% MgCl_2;560℃(calculated)and 26.0mol% PrCl_3,39.4mol% CaCl_2,34.6mol% MgCl_2;546℃(measured),respectively.展开更多
The phase diagram of ternary system ErCl_3-CaCl_2-LiCl has been investigated by means of DTA. It was found that there are four fields corresponding to the primary crystallization of ErCl_3,CaCl_2, LiCl and Li_3ErCl_6 ...The phase diagram of ternary system ErCl_3-CaCl_2-LiCl has been investigated by means of DTA. It was found that there are four fields corresponding to the primary crystallization of ErCl_3,CaCl_2, LiCl and Li_3ErCl_6 respectively, five univariant curves related to the secondary crystallization, a ternary eutectic E(58. 5% ErCl_3, 23. 7% CaCl_2, 17. 8%LiCl, 397 ℃) and a ternary peritectic point P(52. 5% ErCl_3, 27. 2% CaCl_2, 20. 3% LiCl, 428 ℃) in the phase diagram. Two ternary reactions occur in the system: L =ErCl_3 + Li_3ErCl_6 +CaCl_2; L+LiCl=Li_3ErCl_6 +CaCl_2.展开更多
Three surfaces corresponding to the primary crystallization of PrCl_3,CaCl_2 and MgCl_2 respectively,3 univariant curves related to the secondary crystallization and a ternary eutectic(44.8 wt-% PrCl_3,31.8 wt-% CaCl_...Three surfaces corresponding to the primary crystallization of PrCl_3,CaCl_2 and MgCl_2 respectively,3 univariant curves related to the secondary crystallization and a ternary eutectic(44.8 wt-% PrCl_3,31.8 wt-% CaCl_2,546℃)were found in system PrCl_3-CaCl_2-MgCl_2 by means of DTA.A reaction occurs in this system: L=PrCl_3+CaCl_2+MgCl_2.展开更多
The liquidus of ternary system NdCl_3-MgCl_2-LiCl has been determined by means of DTA.It was found that there are two surfaces corresponding to the primary crystallization of NdCl_3 and α-(MgCl_2,LiCl)respectively,an...The liquidus of ternary system NdCl_3-MgCl_2-LiCl has been determined by means of DTA.It was found that there are two surfaces corresponding to the primary crystallization of NdCl_3 and α-(MgCl_2,LiCl)respectively,and a univariant line related to the secondary crystallization with a minimum M(68.5 wt-% NdCl_3,2.7 wt-% MgCl_2,28.8 wt-% LiCl_2 441℃)in the system.展开更多
Five fields corresponding to the primary crystallization of PrCl_3,Sr_3PrCl_9,α(SrCl_2, CaCl_2),α_1(CaCl_2,SrCl_2)and α_2(SrCl_2,CaCl_2)respectively,six univariant lines related to the secondary crystallization,one...Five fields corresponding to the primary crystallization of PrCl_3,Sr_3PrCl_9,α(SrCl_2, CaCl_2),α_1(CaCl_2,SrCl_2)and α_2(SrCl_2,CaCl_2)respectively,six univariant lines related to the secondary crystallization,one ternary eutectic(48.0 wt-％ PrCl_3,23.5 wt-％ SrCl_2; 590℃)and ternary peritectic point(45.5 wt-％ PrCl_3,24.5 wt-％ SrCl_2;614℃) were determined by DTA.Attempts were also made to explore the rule governing the alteration in the phase diagram containing rare earth chloride,formation of compound and its stability by means of polarization and counter-polarization.展开更多
The phase diagrams of binary systems SmCl_3-CaCl_2 and SmCl_3-LiCl were determined by DTA and X-ray diffraction analysis.The system SmCl_3-CaCl_2 is of a simple eutectic type with eutectic point of 55.8mol-% SmCl_3 at...The phase diagrams of binary systems SmCl_3-CaCl_2 and SmCl_3-LiCl were determined by DTA and X-ray diffraction analysis.The system SmCl_3-CaCl_2 is of a simple eutectic type with eutectic point of 55.8mol-% SmCl_3 at 545℃.The system SmCl_3-LiCl is of the type with incongruent melting phase 2SmCl_3·LiCl at peritectic point 434℃ and with eutectic point of 31.5 mol-% SmCl_3 at 395℃.展开更多
Two surfaces correponding to LaCl_3 and α-solid solution(MgCl_2.LiCl) respectively: and one secondary crystallization curve with a minimum M at 63.8 wt-％ LaCl_3,2.0 wt-％ MgCl_2,34.2 wt-％ LiCl and 492℃ were fonud ...Two surfaces correponding to LaCl_3 and α-solid solution(MgCl_2.LiCl) respectively: and one secondary crystallization curve with a minimum M at 63.8 wt-％ LaCl_3,2.0 wt-％ MgCl_2,34.2 wt-％ LiCl and 492℃ were fonud by means of DTA.In combination with liquidus determination.an approach was also made to the alteration in LnCl_3-MgCl_2-LiCl svstem,where Lu denotes La.Ce.Pr or Nd.展开更多
文摘The phase diagram of ternary system ErCl_3-CaCl_2-MgCl_2 has been investigated be means of differentialthermal analysis (DTA). It was found that there were three surfaces corresponding to the primary crystalliza-tion of ErCl_3, CaCl_2 and MgCl_2 respectively, three univariant curves related to the a seondary crystallizationand a ternary eutectic point E (67. 8 wt% ErCl_3, 17. 2 wt% CaCl_2, 15. 0 wt% MgCl_2. 524°C ) in the systemErCl_3-CaCl_2-MgCl_2.
基金Project Supported by National Natural Science Foundation of China
文摘Based on the thermodynamically self-consistent analysis and optimization of three sub-binary systems of the ternary system PrCl_3-CaCl_2-MgCl_2,the thermodynamics of this ternary system has been studied.Using Hillert model and taking MgCl_2 as an asymmetric component,the PrCl_3-CaCl_2-MgCl_2 phase diagram has been calculated.The agreement between calculated and measured compositions and temperatures at deflecting points on liquidus is good.The system is a simple eutectic one with a eutectic point at 26.0mol% PrCl_3, 41.5mol% CaCl_2,32.5mol% MgCl_2;560℃(calculated)and 26.0mol% PrCl_3,39.4mol% CaCl_2,34.6mol% MgCl_2;546℃(measured),respectively.
文摘The phase diagram of ternary system ErCl_3-CaCl_2-LiCl has been investigated by means of DTA. It was found that there are four fields corresponding to the primary crystallization of ErCl_3,CaCl_2, LiCl and Li_3ErCl_6 respectively, five univariant curves related to the secondary crystallization, a ternary eutectic E(58. 5% ErCl_3, 23. 7% CaCl_2, 17. 8%LiCl, 397 ℃) and a ternary peritectic point P(52. 5% ErCl_3, 27. 2% CaCl_2, 20. 3% LiCl, 428 ℃) in the phase diagram. Two ternary reactions occur in the system: L =ErCl_3 + Li_3ErCl_6 +CaCl_2; L+LiCl=Li_3ErCl_6 +CaCl_2.
文摘Three surfaces corresponding to the primary crystallization of PrCl_3,CaCl_2 and MgCl_2 respectively,3 univariant curves related to the secondary crystallization and a ternary eutectic(44.8 wt-% PrCl_3,31.8 wt-% CaCl_2,546℃)were found in system PrCl_3-CaCl_2-MgCl_2 by means of DTA.A reaction occurs in this system: L=PrCl_3+CaCl_2+MgCl_2.
文摘The liquidus of ternary system NdCl_3-MgCl_2-LiCl has been determined by means of DTA.It was found that there are two surfaces corresponding to the primary crystallization of NdCl_3 and α-(MgCl_2,LiCl)respectively,and a univariant line related to the secondary crystallization with a minimum M(68.5 wt-% NdCl_3,2.7 wt-% MgCl_2,28.8 wt-% LiCl_2 441℃)in the system.
文摘Five fields corresponding to the primary crystallization of PrCl_3,Sr_3PrCl_9,α(SrCl_2, CaCl_2),α_1(CaCl_2,SrCl_2)and α_2(SrCl_2,CaCl_2)respectively,six univariant lines related to the secondary crystallization,one ternary eutectic(48.0 wt-％ PrCl_3,23.5 wt-％ SrCl_2; 590℃)and ternary peritectic point(45.5 wt-％ PrCl_3,24.5 wt-％ SrCl_2;614℃) were determined by DTA.Attempts were also made to explore the rule governing the alteration in the phase diagram containing rare earth chloride,formation of compound and its stability by means of polarization and counter-polarization.
文摘The phase diagrams of binary systems SmCl_3-CaCl_2 and SmCl_3-LiCl were determined by DTA and X-ray diffraction analysis.The system SmCl_3-CaCl_2 is of a simple eutectic type with eutectic point of 55.8mol-% SmCl_3 at 545℃.The system SmCl_3-LiCl is of the type with incongruent melting phase 2SmCl_3·LiCl at peritectic point 434℃ and with eutectic point of 31.5 mol-% SmCl_3 at 395℃.
文摘Two surfaces correponding to LaCl_3 and α-solid solution(MgCl_2.LiCl) respectively: and one secondary crystallization curve with a minimum M at 63.8 wt-％ LaCl_3,2.0 wt-％ MgCl_2,34.2 wt-％ LiCl and 492℃ were fonud by means of DTA.In combination with liquidus determination.an approach was also made to the alteration in LnCl_3-MgCl_2-LiCl svstem,where Lu denotes La.Ce.Pr or Nd.