Pt-WO3 nanoparticles uniformly dispersed on Vulcan XC-72R carbon black were prepared by an ethylene glycol method.The morphology,composition,nanostructure,electrochemical characteristics and electrocatalytic activity ...Pt-WO3 nanoparticles uniformly dispersed on Vulcan XC-72R carbon black were prepared by an ethylene glycol method.The morphology,composition,nanostructure,electrochemical characteristics and electrocatalytic activity were characterized,and the formation mechanism was investigated.The average particle size was 2.3 nm,the same as that of Pt/C catalyst.The W/Pt atomic ratio was 1/20,much lower than the design of 1/3.The deposition of WO3·xH2O nanoparticles on Vulcan XC-72R carbon black was found to be very difficult by TEM.From XPS and XRD,the Pt nanoparticles were formed in the colloidal solution of Na2WO4,the EG insoluble Na2WO4 resulted in the decreased relative crystallinity and increased crystalline lattice constant compared with those of Pt/C catalyst and,subsequently,the higher specific electrocatalytic activity as determined by CV.The Pt-mass and Pt-electrochemically-active-specific-surface-area based anodic peak current densities for ethanol oxidation were 422.2 mA·mg-1Pt and 0.43 mA·cm-2Pt,1.2 and 1.1 times higher than those of Pt/C catalyst,respectively.展开更多
基金Funded by the National Basic Research Program of China (No. 2009CB220100)the Beijing Excellent Talent Support Program (No. 20071D1600300396)
文摘Pt-WO3 nanoparticles uniformly dispersed on Vulcan XC-72R carbon black were prepared by an ethylene glycol method.The morphology,composition,nanostructure,electrochemical characteristics and electrocatalytic activity were characterized,and the formation mechanism was investigated.The average particle size was 2.3 nm,the same as that of Pt/C catalyst.The W/Pt atomic ratio was 1/20,much lower than the design of 1/3.The deposition of WO3·xH2O nanoparticles on Vulcan XC-72R carbon black was found to be very difficult by TEM.From XPS and XRD,the Pt nanoparticles were formed in the colloidal solution of Na2WO4,the EG insoluble Na2WO4 resulted in the decreased relative crystallinity and increased crystalline lattice constant compared with those of Pt/C catalyst and,subsequently,the higher specific electrocatalytic activity as determined by CV.The Pt-mass and Pt-electrochemically-active-specific-surface-area based anodic peak current densities for ethanol oxidation were 422.2 mA·mg-1Pt and 0.43 mA·cm-2Pt,1.2 and 1.1 times higher than those of Pt/C catalyst,respectively.