Diffusion bonding of as-cast Mg−6Gd−3Y magnesium alloy was carried out at temperatures of 400−480℃ with bonding pressure of 6 MPa for 90 min.Diffusion bonded joints were solution treated at 495℃ for 14 h and then ag...Diffusion bonding of as-cast Mg−6Gd−3Y magnesium alloy was carried out at temperatures of 400−480℃ with bonding pressure of 6 MPa for 90 min.Diffusion bonded joints were solution treated at 495℃ for 14 h and then aged at 200℃ for 30 h.Microstructures and mechanical properties of joints were analyzed.The results showed that rare earth elements and their compounds gathering at bonding interface hindered the grain boundary migration crossing bonding interface.Tensile strength of as-bonded and as-solution treated joints increased firstly and then decreased with the bonding temperature increasing due to the combined effects of grain coarsening and solid-solution strengthening.As-bonded and solution-treated joints fractured at matrix except the joint bonded at 400℃,while aged joints fractured at bonding interface.The highest ultimate tensile strength of 279 MPa with elongation of 2.8%was found in joint bonded at 440℃ with solution treatment followed by aging treatment.展开更多
Based on traditional twin-roll casting process,Invar/Cu clad strips were successfully fabricated by using solid Invar alloy strip and molten Cu under conditions of high temperature,high pressure and plastic deformatio...Based on traditional twin-roll casting process,Invar/Cu clad strips were successfully fabricated by using solid Invar alloy strip and molten Cu under conditions of high temperature,high pressure and plastic deformation.A series of tests including tensile test,bending test,T-type peeling test and scanning electron microscope(SEM)and energy dispersive spectrometer(EDS)measurements were carried out to analyze the mechanical properties of Invar/Cu clad strips and the micro-morphology of tensile fracture surfaces and bonding interfaces.The results indicate that no delamination phenomenon occurs during the compatible deformation of Invar/Cu in bending test and only one stress platform exists in the tensile stress-strain curve when the bonding strength is large.On the contrary,different mechanical properties of Invar and Cu lead to delamination phenomenon during the uniaxial tensile test,which determines that two stress platforms occur on the stress-strain curve of Invar/Cu clad strips when two elements experience necking.The average peeling strength can be increased from13.85to42.31N/mm after heat treatment at800℃for1h,and the observation of the Cu side at peeling interface shows that more Fe is adhered on the Cu side after the heat treatment.All above illustrate that heat treatment can improve the strength of the bonding interface of Invar/Cu clad strips.展开更多
基金financially supported by the Science Innovation Foundation of Shanghai Academy of Spaceflight Technology,China (No.SAST2020-117)。
文摘Diffusion bonding of as-cast Mg−6Gd−3Y magnesium alloy was carried out at temperatures of 400−480℃ with bonding pressure of 6 MPa for 90 min.Diffusion bonded joints were solution treated at 495℃ for 14 h and then aged at 200℃ for 30 h.Microstructures and mechanical properties of joints were analyzed.The results showed that rare earth elements and their compounds gathering at bonding interface hindered the grain boundary migration crossing bonding interface.Tensile strength of as-bonded and as-solution treated joints increased firstly and then decreased with the bonding temperature increasing due to the combined effects of grain coarsening and solid-solution strengthening.As-bonded and solution-treated joints fractured at matrix except the joint bonded at 400℃,while aged joints fractured at bonding interface.The highest ultimate tensile strength of 279 MPa with elongation of 2.8%was found in joint bonded at 440℃ with solution treatment followed by aging treatment.
基金Project (51474189) supported by the National Natural Science Foundation of ChinaProject (E2018203446) supported by the Excellent Youth Foundation of Hebei Scientific Committee,ChinaProject (QN2015214) supported by the Educational Commission of Hebei Province,China
文摘Based on traditional twin-roll casting process,Invar/Cu clad strips were successfully fabricated by using solid Invar alloy strip and molten Cu under conditions of high temperature,high pressure and plastic deformation.A series of tests including tensile test,bending test,T-type peeling test and scanning electron microscope(SEM)and energy dispersive spectrometer(EDS)measurements were carried out to analyze the mechanical properties of Invar/Cu clad strips and the micro-morphology of tensile fracture surfaces and bonding interfaces.The results indicate that no delamination phenomenon occurs during the compatible deformation of Invar/Cu in bending test and only one stress platform exists in the tensile stress-strain curve when the bonding strength is large.On the contrary,different mechanical properties of Invar and Cu lead to delamination phenomenon during the uniaxial tensile test,which determines that two stress platforms occur on the stress-strain curve of Invar/Cu clad strips when two elements experience necking.The average peeling strength can be increased from13.85to42.31N/mm after heat treatment at800℃for1h,and the observation of the Cu side at peeling interface shows that more Fe is adhered on the Cu side after the heat treatment.All above illustrate that heat treatment can improve the strength of the bonding interface of Invar/Cu clad strips.