Experimental study on thermal and mechanical properties of tailings-based cemented paste backfill with CaCl_(2)·6H_(2)O/expanded vermiculite shape stabilized phase change materials

CaCl_(2)·6H_(2)O/expanded vermiculite shape stabilized phase change materials(CEV)was prepared by atmospheric impregnation method.Using gold mine tailings as aggregate of cemented paste backfill(CPB)material,the CPB with CEV added was prepared,and the specific heat capacity,thermal conductivity,and uniaxial compressive strength(UCS)of CPB with different cement-tailing ratios and CEV addition ratios were tested,the influence of the above variables on the thermal and mechanical properties of CPB was analyzed.The results show that the maximum encapsulation capacity of expanded vermiculite for CaCl_(2)·6H_(2)O is about 60%,and the melting and solidification enthalpies of CEV can reach 98.87 J/g and 97.56 J/g,respectively.For the CPB without CEV,the specific heat capacity,thermal conductivity,and UCS decrease with the decrease of cement-tailing ratio.For the CPB with CEV added,with the increase of CEV addition ratio,the specific heat capacity increases significantly,and the sensible heat storage capacity and latent heat storage capacity can be increased by at least 10.74%and 218.97%respectively after adding 12%CEV.However,the addition of CEV leads to the increase of pores,and the thermal conductivity and UCS both decrease with the increase of CEV addition.When cement-tailing ratio is 1:8 and 6%,9%,and 12%of CEV are added,the 28-days UCS of CPB is less than 1 MPa.Considering the heat storage capacity and cost price of backfill,the recommended proportion scheme of CPB material presents cement-tailing ratio of 1:6 and 12%CEV,and the most recommended heat storage/release temperature cycle range of CPB with added CEV is from 20 to 40℃.This work can provide theoretical basis for the utilization of heat storage backfill in green mines.

Fabrication, property characterization and thermal performance of composite phase change material plates based on tetradecanol-myristic acid binary eutectic mixture/expanded perlite and expanded vermiculite for building application

A binary eutectic mixture composed of tetradecanol(TD)and myristic acid(MA)was maximally absorbed into the microstructures of expanded perlite(EP)and expanded vermiculite(EVMT),respectively,through a self-made vacuum adsorption roller to prepare phase change material(PCM)particle(PCP).Then EP and EVMT-based composite PCM plates were respectively fabricated through a mold pressing method.The thermal property,chemical stability,microstructure and durability were characterized by differential scanning calorimeter(DSC),Fourier transform infrared spectroscope(FT-IR),scanning electron microscope(SEM)and thermal cycling tests,respectively.The results show that both PCPs have high latent heats with 110 J/g for EP-based PCP and more than 130 J/g for EVMT-based PCP,compact microstructure without PCM leakage,stable chemical property and good durability.The research results have proved the feasibility for the vacuum adsorption roller used in the composite PCM fabrication.Results of thermal storage performance experiment indicate that the fabricated PCM plates have better thermal inertia than common building materials,and the thermal storage performance of PCM plates has nonlinearly changed with outside air velocity and temperature increase.Therefore,PCM plates show a significant potential for the practical application of building thermal storage.

Microstructure and Characterization of Capric-stearic Acid/Modified Expanded Vermiculite Thermal Storage Composites

In order to improve the thermal storage capacity of expanded vermiculite（EV） based formstable composite PCM（FS-PCM） via organic modification of EV, first, EV was modified with a sodium stearate（Na St） as surface modifier, and organic EV（OEV） with hydrophobicity and higher adsorption capacity for fatty acid was obtained. A novel capric-stearic acid eutectic（CA-SA）/OEV FS-PCM with high thermal storage capacity was then developed. OEV and CA-SA/OEV were characterized by scanning electron microscopy（SEM）, X-ray diffraction（XRD）, Fourier transform infrared spectroscopy（FTIR）, differential scanning calorimetry（DSC）, thermal gravimetry（TG）, and thermal cycling test. Results showed that OEV has obvious hydrophobicity and a higher adsorption capacity for fatty acid. Its adsorption ratio has increased by 48.71% compared with that of EV. CA-SA/OEV possesses high thermal storage density（112.52 J/g）, suitable melting temperature（20.49 ℃）, good chemical compatibility, excellent thermal stability and reliability, indicating great application potential for building energy efficiency. Moreover, organic modification of inorganic matrix may offer novel options for improving its adsorption capacity for organic PCMs and increasing heat storage capacity of corresponding FS-PCMs.

Preparation and characterization of capric-palmitic-stearic acid ternary eutectic mixture/expanded vermiculite composites as form-stabilized thermal energy storage materials

In this study, a composite of form-stable phase change materials （FSPCMs） were prepared by the incorporation of a eutectic mixture of capric-palmitic-stearic acid （CA-PA-SA） into expanded vermiculite （EV） via vacuum impregnation. In the composites, CA-PA-SA was utilized as a thermal energy storage material, and EV served as the supporting material. X-ray diffraction and Fourier transform infrared spectroscopy results demonstrated that CA-PA-SA and EV in the composites only undergo physical combination, not a chemical reaction. Scanning electron microscopy images indicated that CA-PA-SA is sufficiently absorbed in the expanded vermiculite porous network. According to differential scanning calorimetry results, the 70 wt% CA-PA-SA/EV sample melts at 19.3 ℃ with a latent heat of 117.6J/g and solidifies at 17.1 ℃ with a latent heat of 118.3J/g. Thermal cycling measurements indicated that FSPCMs exhibit adequate stability even after being subjected to 200 melting-freezing cycles. Furthermore, the thermal conductivity of the composites increased by approximately 49.58% with the addition of 5 wt% of Cu powder. Hence, CA-PA-SA/EV FSPCMs are effective latent heat thermal energy storage building materials.