Structures and Properties of Iron Matrix Composites with Tungsten Carbide Particle by EPC-V Process

In this paper the Expendable Pattern Casting with dry sand Vacuum(EPC-V) process is used to manufacture iron matrix composites with tungsten carbide particle.Microstructures of the composites layers were analyzed.The abrasive wear resistance of the composites layers were tested and compared with that of high chromium cast iron.The results show that the iron matrix composites with tungsten carbide particle have high hardness.The abrasive wear resistance of composites with tungsten carbide particle is higher than that of high chromium cast iron.The properties of the matrix materials have been improved remarkably.

镁合金负压消失模铸造充型过程的研究

镁合金负压消失模铸造充型过程的直接观察实验的结果表明 ,不抽真空时 ,金属前沿呈微凸形平缓地向前推进 ;抽真空时 ,因在模样分解产物的排除方向上存在一正的压力梯度 ,金属液优先沿模样壁充填型腔使流动形态呈不规则的凹形形态。提高真空度 ,不规则的流动形态的凹度更大且充型时间明显缩短。浇注方式对流动形态和充型时间的影响不大 ,与顶注和侧注相比 ,底注时充型过程最为平稳 ,且其充型时间最长。根据试验结果 。

柴油机气缸体消失模铸造生产工艺分析

在柴油机气缸体中采用消失模铸造工艺,不仅能提高柴油机气缸体的结构强度,还可以提高其整体刚度,以满足柴油机工作中各项性能的稳定。分析了柴油机气缸体的消失模铸造工艺。观察其生产过程,分析了生产工艺的优劣。

铸钢件进料口的铸造工艺模拟及改进

运用传统的铸造工艺设计方法对铸钢件进料口的铸造工艺进行了初步设计,利用V-Cast模拟软件对进料口初始工艺的凝固过程进行了数值模拟,分析了初始工艺产生缺陷的部位和原因。最终决定采用消失模铸造来生产铸件,并取得了良好的结果。

汽车覆盖件模具实型铸造实践

本文简要论述了在传统生产条件下，运用ＥＰＣ法开发生产汽车覆盖件模具进行的工艺分析、工艺设计，提出了生产中应注意的一些问题。得出结论：对于通用汽车覆盖件模具铸铁件可用普通可发性 ＥＰＣ作为模型材料，ＣＯ２－水玻璃砂作为造型材料，获得高质量铸件。

机械振动振幅对消失模铸造ZGMn13钢组织和性能的影响

采用显微组织观察、硬度测试、室温冲击试验研究了不同振幅机械振动对消失模铸造ZGMn13钢组织和性能的影响。结果表明：浇注过程中施加振动,使ZGMn13钢中非金属夹杂物分布更加均匀、细小,晶粒明显细化,试样硬度和冲击吸收能量有所提高。振幅在0.3～0.6 mm内,随着振动振幅的增加, ZGMn13铸钢晶粒逐渐细化,硬度和冲击吸收能量逐渐提高。振幅0.6 mm时,硬度和冲击吸收能量达到最大值,分别为413HB和1.7J,比未振动的ZGMn13钢试样分别提高了27.9%（323→413HB）和21.4%（1.4→1.7J）。