The effects of prestrain and annealing temperature on phase transformation temperatures in Fel4Mn5Si8Cr4Ni shape memory alloy have been studied. The results showed that when the annealing temperature was 673 K, both t...The effects of prestrain and annealing temperature on phase transformation temperatures in Fel4Mn5Si8Cr4Ni shape memory alloy have been studied. The results showed that when the annealing temperature was 673 K, both the At and the Ms temperatures increased appreciably as the prestrain increased, the As temperature increased slightly with increasing prestrain; the resistivity difference at 303 K between the heating and cooling curve also increased with increasing prestrain, which agreed with the recovery strain. The shape memory effect in Fe-Mn-Si-Cr-Ni shape memory alloy is caused by the stress-induced γ→ε martensite transformation and its reverse transformation. When the prestrain was 10%, the Ms temperature decreased remarkably as the annealing temperature increased.展开更多
The work-hardening behaviour in an Fe-Mn-Si-Cr-Ni alloy has been investigated using tensile test at different temperatures and TEM observation. It was found that besides the intersection of εmartensite, the intersect...The work-hardening behaviour in an Fe-Mn-Si-Cr-Ni alloy has been investigated using tensile test at different temperatures and TEM observation. It was found that besides the intersection of εmartensite, the intersections of ε martensite with stacking fault and the cross-slip of dislocation which is difficult to occur in the alloy with low stacking fault energy are also important factors to the temperature dependent work-hardening behaviour.展开更多
The configurations of stacking faults and morphologies of strain induced ε martensite plates in an FeMnSiCrNi alloy were investigated through electron microscopy analysis. The Shockley partial dislocation structures....The configurations of stacking faults and morphologies of strain induced ε martensite plates in an FeMnSiCrNi alloy were investigated through electron microscopy analysis. The Shockley partial dislocation structures. sensitive to external stress. determine the configurations of stacking faults in γphase Partial dislocations at the front sides of stacking faults are usetul for the nucleation of εmartensite plates. The growth of ε martensite plates is accompanied with the disappearance of local pre-existing stacking faults, The ε martensite vanants behave in three morphologies of respective stopping. continuous penetrating and intersections with the formation of secondary ε martensite plates展开更多
文摘The effects of prestrain and annealing temperature on phase transformation temperatures in Fel4Mn5Si8Cr4Ni shape memory alloy have been studied. The results showed that when the annealing temperature was 673 K, both the At and the Ms temperatures increased appreciably as the prestrain increased, the As temperature increased slightly with increasing prestrain; the resistivity difference at 303 K between the heating and cooling curve also increased with increasing prestrain, which agreed with the recovery strain. The shape memory effect in Fe-Mn-Si-Cr-Ni shape memory alloy is caused by the stress-induced γ→ε martensite transformation and its reverse transformation. When the prestrain was 10%, the Ms temperature decreased remarkably as the annealing temperature increased.
文摘The work-hardening behaviour in an Fe-Mn-Si-Cr-Ni alloy has been investigated using tensile test at different temperatures and TEM observation. It was found that besides the intersection of εmartensite, the intersections of ε martensite with stacking fault and the cross-slip of dislocation which is difficult to occur in the alloy with low stacking fault energy are also important factors to the temperature dependent work-hardening behaviour.
文摘The configurations of stacking faults and morphologies of strain induced ε martensite plates in an FeMnSiCrNi alloy were investigated through electron microscopy analysis. The Shockley partial dislocation structures. sensitive to external stress. determine the configurations of stacking faults in γphase Partial dislocations at the front sides of stacking faults are usetul for the nucleation of εmartensite plates. The growth of ε martensite plates is accompanied with the disappearance of local pre-existing stacking faults, The ε martensite vanants behave in three morphologies of respective stopping. continuous penetrating and intersections with the formation of secondary ε martensite plates