In this study, a work-of-fracture method using a three-point bend beam （3PBB） specimen, which is commonly used to determine the fracture energy of concrete, was adapted to evaluate the mode-I fracture and durability...In this study, a work-of-fracture method using a three-point bend beam （3PBB） specimen, which is commonly used to determine the fracture energy of concrete, was adapted to evaluate the mode-I fracture and durability of fiber-reinforced polymer （FRP） composite-concrete bonded interfaces. Interface fracture properties were evaluated with established data reduction procedures. The proposed test method is primarily for use in evaluating the effects of freeze-thaw （F-T） and wet-dry （W-D） cycles that are the accelerated aging protocols on the mode-I fracture of carbon FRP-concrete bonded interfaces. The results of the mode-I fracture tests of F-T and W-D cycle-conditioned specimens show that both the critical load and fracture energy decrease as the number of cycles increases, and their degradation pattern has a nearly linear relationship with the number of cycles. However, compared with the effect of the F-T cycles, the critical load and fracture energy degrade at a slower rate with W-D cycles, which suggests that F-T cyclic conditioning causes more deterioration of carbon fiber-reinforced polymer （CFRP）-concrete bonded interface. After 50 and 100 conditioning cycles, scaling of concrete was observed in all the specimens subjected to F-T cycles, but not in those subjected to W-D cycles. The examination of interface fracture surfaces along the bonded interfaces with varying numbers of F-T and W-D conditioning cycles shows that （1） cohesive failure of CFRP composites is not observed in all fractured surfaces; （2） for the control specimens that have not been exposed to any conditioning cycles, the majority of interface failure is a result of cohesive fracture of concrete （peeling of concrete from the concrete substrate）, which means that the cracks mostly propagate within the concrete; and （3） as the number of F-T or W-D conditioning cycles increases, adhesive failure along the interface begins to emerge and gradually increases. It is thus concluded that the fracture properties （i.e., the critical load and fracture energy） of the bonded interface are controlled primarily by the concrete cohesive fracture before conditioning and by the adhesive interface fracture after many cycles of F-T or W-D conditioning. As demonstrated in this study, a test method using 3PBB specimens combined with a fictitious crack model and experimental conditioning protocols for durability can be used as an effective qualification method to test new hybrid material interface bonds and to evaluate durability-related effects on the interfaces.展开更多
Based on the fast freeze-thaw cycling test, the alkaline immersion test, the water immersion test and the wet-thermal exposure test, the influence of aggressive environments on mechanical behavior of FRP was studied. ...Based on the fast freeze-thaw cycling test, the alkaline immersion test, the water immersion test and the wet-thermal exposure test, the influence of aggressive environments on mechanical behavior of FRP was studied. CFRP specimens subjected to aggressive environments showed good durability with no significant degradation in tensile strength and modulus; however, GFRP specimens exhibited a little decrease in mechanical property after aggressive environments exposure. Based on the fast freeze-thaw cycling test and the wet-thermal exposure test, the influence of aggressive environments on the bond behavior between FRP and concrete, mechanical behavior of concrete beams and columns strengthened with FRP laminates was studied. The results showed that the bond strength had a significant decrease compared with those specimens kept at room temperature, and the specimens strengthened with FRP exhibited good durability.展开更多
This paper aims at exploring the effects of anti-seismic reinforcement with the fiber-reinforced polymer （FRP） material bonded to the dam surface in dam engineering. Time-history analysis was performed to simulate t...This paper aims at exploring the effects of anti-seismic reinforcement with the fiber-reinforced polymer （FRP） material bonded to the dam surface in dam engineering. Time-history analysis was performed to simulate the seismic failure process of a gravity dam that was assumed to be reinforced at the locations of slope discontinuity at the downstream surface, part of the upstream face, and the dam heel. A damage model considering the influence of concrete heterogeneity was used to model the nonlinearity of concrete. A bond-slip model was applied to the interface between FRP and concrete, and the reinforcement mechanism was analyzed through the bond stress and the stress in FRP. The results of the crack pattern, displacement, and acceleration of the reinforced dam were compared with those of the original one. It is shown that FRP, as a reinforcement material, postpones the occurrence of cracks and slows the crack propagation, and that cracks emanating from the upstream surface and downstream surface are not connected, meaning that the reinforced dam can retain water-impounding function when subjected to the earthquake. Anti-seismic reinforcement with FRP is therefore beneficial to improving the seismic resistant capability of concrete dams.展开更多
As a preliminary study for the erection of floating structures using high performance concrete, this paper examines the bond characteristics between concrete and the reinforcing bar. Since the floating structure is co...As a preliminary study for the erection of floating structures using high performance concrete, this paper examines the bond characteristics between concrete and the reinforcing bar. Since the floating structure is constructed in aquatic environment, corrosion of the reinforcing steel is likely to develop more prematurely than in onshore structure in case of concrete cracking. A solution to this corrosion problem could use FRP rebar instead of steel reinforcement. To that goal, an experimental study is conducted on the concrete-FRP bond strength to verify if such FRP rebar develops performance comparable to the conventional steel rebar. A series of tests are performed considering the bond length of ordinary steel rebar and G-FRP rebar as test variable with respect to the strength of concrete, and the results are presented.展开更多
Geopolymer is produced through the polymerization of active aluminosilicate material with an alkaline activator,leading to the formation of a green,inorganic polymer binder.Geopolymer concrete(GPC)has become a promisi...Geopolymer is produced through the polymerization of active aluminosilicate material with an alkaline activator,leading to the formation of a green,inorganic polymer binder.Geopolymer concrete(GPC)has become a promising low-carbon alternative to traditional Portland cement-based concrete(OPC).GPC-bonded reinforcing bars offer a promising alternative for concrete structures,boasting excellent geopolymer binder/reinforcement bonding and superior corrosion and high-temperature resistance compared to Portland cement.However,due to differences in the production process of GPC,there are distinct engineering property variations,including bonding characteristics.This literature review provides an examination of the manufacturing procedures of GPC,encompassing source materials,mix design,curing regimes,and other factors directly influencing concrete properties.Additionally,it delves into the bond mechanism,bond tests,and corresponding results that represent the bond characteristics.The main conclusions are that GPC generally has superior mechanical properties and bond performance compared to ordinary Portland cement concrete(OPC).However,proper standardization is needed for its production and performance tests to limit the contradictory results in the lab and on site.展开更多
基金partially supported by the National Science Foundation(Grant No.CMS-0002829)
文摘In this study, a work-of-fracture method using a three-point bend beam （3PBB） specimen, which is commonly used to determine the fracture energy of concrete, was adapted to evaluate the mode-I fracture and durability of fiber-reinforced polymer （FRP） composite-concrete bonded interfaces. Interface fracture properties were evaluated with established data reduction procedures. The proposed test method is primarily for use in evaluating the effects of freeze-thaw （F-T） and wet-dry （W-D） cycles that are the accelerated aging protocols on the mode-I fracture of carbon FRP-concrete bonded interfaces. The results of the mode-I fracture tests of F-T and W-D cycle-conditioned specimens show that both the critical load and fracture energy decrease as the number of cycles increases, and their degradation pattern has a nearly linear relationship with the number of cycles. However, compared with the effect of the F-T cycles, the critical load and fracture energy degrade at a slower rate with W-D cycles, which suggests that F-T cyclic conditioning causes more deterioration of carbon fiber-reinforced polymer （CFRP）-concrete bonded interface. After 50 and 100 conditioning cycles, scaling of concrete was observed in all the specimens subjected to F-T cycles, but not in those subjected to W-D cycles. The examination of interface fracture surfaces along the bonded interfaces with varying numbers of F-T and W-D conditioning cycles shows that （1） cohesive failure of CFRP composites is not observed in all fractured surfaces; （2） for the control specimens that have not been exposed to any conditioning cycles, the majority of interface failure is a result of cohesive fracture of concrete （peeling of concrete from the concrete substrate）, which means that the cracks mostly propagate within the concrete; and （3） as the number of F-T or W-D conditioning cycles increases, adhesive failure along the interface begins to emerge and gradually increases. It is thus concluded that the fracture properties （i.e., the critical load and fracture energy） of the bonded interface are controlled primarily by the concrete cohesive fracture before conditioning and by the adhesive interface fracture after many cycles of F-T or W-D conditioning. As demonstrated in this study, a test method using 3PBB specimens combined with a fictitious crack model and experimental conditioning protocols for durability can be used as an effective qualification method to test new hybrid material interface bonds and to evaluate durability-related effects on the interfaces.
基金Sponsored by the National Natural Science Foundation of China(Grant No50608013)National Major Foundational Rearch(2004CCAO4100)
文摘Based on the fast freeze-thaw cycling test, the alkaline immersion test, the water immersion test and the wet-thermal exposure test, the influence of aggressive environments on mechanical behavior of FRP was studied. CFRP specimens subjected to aggressive environments showed good durability with no significant degradation in tensile strength and modulus; however, GFRP specimens exhibited a little decrease in mechanical property after aggressive environments exposure. Based on the fast freeze-thaw cycling test and the wet-thermal exposure test, the influence of aggressive environments on the bond behavior between FRP and concrete, mechanical behavior of concrete beams and columns strengthened with FRP laminates was studied. The results showed that the bond strength had a significant decrease compared with those specimens kept at room temperature, and the specimens strengthened with FRP exhibited good durability.
基金supported by the National Natural Science Foundation of China(Grant No.51009019)the State Key Development Program for Basic Research of China(Grant No.2013CB035905)
文摘This paper aims at exploring the effects of anti-seismic reinforcement with the fiber-reinforced polymer （FRP） material bonded to the dam surface in dam engineering. Time-history analysis was performed to simulate the seismic failure process of a gravity dam that was assumed to be reinforced at the locations of slope discontinuity at the downstream surface, part of the upstream face, and the dam heel. A damage model considering the influence of concrete heterogeneity was used to model the nonlinearity of concrete. A bond-slip model was applied to the interface between FRP and concrete, and the reinforcement mechanism was analyzed through the bond stress and the stress in FRP. The results of the crack pattern, displacement, and acceleration of the reinforced dam were compared with those of the original one. It is shown that FRP, as a reinforcement material, postpones the occurrence of cracks and slows the crack propagation, and that cracks emanating from the upstream surface and downstream surface are not connected, meaning that the reinforced dam can retain water-impounding function when subjected to the earthquake. Anti-seismic reinforcement with FRP is therefore beneficial to improving the seismic resistant capability of concrete dams.
文摘As a preliminary study for the erection of floating structures using high performance concrete, this paper examines the bond characteristics between concrete and the reinforcing bar. Since the floating structure is constructed in aquatic environment, corrosion of the reinforcing steel is likely to develop more prematurely than in onshore structure in case of concrete cracking. A solution to this corrosion problem could use FRP rebar instead of steel reinforcement. To that goal, an experimental study is conducted on the concrete-FRP bond strength to verify if such FRP rebar develops performance comparable to the conventional steel rebar. A series of tests are performed considering the bond length of ordinary steel rebar and G-FRP rebar as test variable with respect to the strength of concrete, and the results are presented.
基金supported by the ongoing projects provided by the National Key Research and Development Program(2021YFB2600704)the National Natural Science Foundation of China(52108223,U22A20244)+3 种基金the Outstanding Youth Fund of Shandong Province(ZR2021JQ17)the Natural Science Foundation of Shandong Province(ZR2020QE249)the 111 Project(D16006)the First-Class Discipline Project funded by the Education Department of Shandong Province are gratefully acknowledged.
文摘Geopolymer is produced through the polymerization of active aluminosilicate material with an alkaline activator,leading to the formation of a green,inorganic polymer binder.Geopolymer concrete(GPC)has become a promising low-carbon alternative to traditional Portland cement-based concrete(OPC).GPC-bonded reinforcing bars offer a promising alternative for concrete structures,boasting excellent geopolymer binder/reinforcement bonding and superior corrosion and high-temperature resistance compared to Portland cement.However,due to differences in the production process of GPC,there are distinct engineering property variations,including bonding characteristics.This literature review provides an examination of the manufacturing procedures of GPC,encompassing source materials,mix design,curing regimes,and other factors directly influencing concrete properties.Additionally,it delves into the bond mechanism,bond tests,and corresponding results that represent the bond characteristics.The main conclusions are that GPC generally has superior mechanical properties and bond performance compared to ordinary Portland cement concrete(OPC).However,proper standardization is needed for its production and performance tests to limit the contradictory results in the lab and on site.