The effects of Sr,Mg,Cr,Sr/Mg and Sr/Cr combined additions on the Fe-containing intermetallic phase in a recycled Al-Si-Fe cast alloy are investigated.The experimental results show that the additions of Cr and Sr/Cr s...The effects of Sr,Mg,Cr,Sr/Mg and Sr/Cr combined additions on the Fe-containing intermetallic phase in a recycled Al-Si-Fe cast alloy are investigated.The experimental results show that the additions of Cr and Sr/Cr successfully modified the platelet and flake-likeβ-Al-5FeSi phases （β-compound） into the fibrousα-Al-8Fe-2Si （α-compound）.The additions of Sr and Sr/Mg were less effective to modify theβ-compound into theα-compound,while the eutectic Si was fully modified into the fibrous morphology.A small secondary dendrite arm spacing （DAS） was found in the Sr-added,Cr-added and Sr/Cr-added alloys,especially in a steel mold.The Sr,Sr/Cr and Sr/Mg combined additions modify the eutectic Si simultaneously.A sludge phase was found in the addition of Cr-added,Sr/Cr-added and Mg-added alloys,especially in the graphite mold casting.The volume fraction ofβ-compounds was decreased by the addition of various modifying elements. The Cr and Sr/Cr combined additions are very effective to modify theβ-compound for the recycled Al-Si-Fe based alloys.展开更多
The reduction diffusion method was performed for the sludge scrap of Nd-Fe-B sintered magnets with adding Ca metal to recover the oxidized Nd-Fe-B phase. After washing the resultant powders to remove Ca metal componen...The reduction diffusion method was performed for the sludge scrap of Nd-Fe-B sintered magnets with adding Ca metal to recover the oxidized Nd-Fe-B phase. After washing the resultant powders to remove Ca metal component, the powders obtained were recycled as an isotropic magnetic powder by the melt spinning method. The magnetic properties of powders as recycled were inferior, especially for the coercivity value, due to the deletion of rare earth metals during the washing process. The adjustment of metal composition, i.e., the addition of Nd metal, at the melt spinning process improved the magnetic properties to be B r=～0.75 T, H cj=～0.93 mA·m -1, and (BH) max=～91 kJ·m -3. The magnetic properties of the bonded magnets prepared from the composition-adjusted powders were B r=～0.66 T, H cj=～0.92 mA·m -1, and (BH) max=～70 kJ·m -3, which are approximately comparable to the commercially available MQPB boned one (B r=～0.73 T, H cj=～0.79 mA·m -1, and (BH) max=～86 kJ·m -3).展开更多
文摘The effects of Sr,Mg,Cr,Sr/Mg and Sr/Cr combined additions on the Fe-containing intermetallic phase in a recycled Al-Si-Fe cast alloy are investigated.The experimental results show that the additions of Cr and Sr/Cr successfully modified the platelet and flake-likeβ-Al-5FeSi phases （β-compound） into the fibrousα-Al-8Fe-2Si （α-compound）.The additions of Sr and Sr/Mg were less effective to modify theβ-compound into theα-compound,while the eutectic Si was fully modified into the fibrous morphology.A small secondary dendrite arm spacing （DAS） was found in the Sr-added,Cr-added and Sr/Cr-added alloys,especially in a steel mold.The Sr,Sr/Cr and Sr/Mg combined additions modify the eutectic Si simultaneously.A sludge phase was found in the addition of Cr-added,Sr/Cr-added and Mg-added alloys,especially in the graphite mold casting.The volume fraction ofβ-compounds was decreased by the addition of various modifying elements. The Cr and Sr/Cr combined additions are very effective to modify theβ-compound for the recycled Al-Si-Fe based alloys.
基金ProjectsupportedbyaGrant in AidfortheCreationofinnovationsthroughBusiness Academic PublicSectorCooperation
文摘The reduction diffusion method was performed for the sludge scrap of Nd-Fe-B sintered magnets with adding Ca metal to recover the oxidized Nd-Fe-B phase. After washing the resultant powders to remove Ca metal component, the powders obtained were recycled as an isotropic magnetic powder by the melt spinning method. The magnetic properties of powders as recycled were inferior, especially for the coercivity value, due to the deletion of rare earth metals during the washing process. The adjustment of metal composition, i.e., the addition of Nd metal, at the melt spinning process improved the magnetic properties to be B r=～0.75 T, H cj=～0.93 mA·m -1, and (BH) max=～91 kJ·m -3. The magnetic properties of the bonded magnets prepared from the composition-adjusted powders were B r=～0.66 T, H cj=～0.92 mA·m -1, and (BH) max=～70 kJ·m -3, which are approximately comparable to the commercially available MQPB boned one (B r=～0.73 T, H cj=～0.79 mA·m -1, and (BH) max=～86 kJ·m -3).