The recrystallization and softening resistance of a Cu-6.5Fe-0.3Mg(mass fraction,%)alloy prepared by Process 1(cold rolling heat treatment)and Process 2(hot/cold rolling heat treatment)were studied using Vickers hardn...The recrystallization and softening resistance of a Cu-6.5Fe-0.3Mg(mass fraction,%)alloy prepared by Process 1(cold rolling heat treatment)and Process 2(hot/cold rolling heat treatment)were studied using Vickers hardness tests,tensile tests,scanning electron microscopy and transmission electron microscopy.The softening temperature,hardness and tensile strength of the alloy prepared by Process 2 were 110°C,HV 15 and 114 MPa higher,respectively,than those of the alloy prepared by Process 1 after aging at 300°C.The recrystallization activation energy of the alloys prepared by Process 1 and Process 2 were 72.83 and 98.11 kJ/mol,respectively.The pinning effects of the precipitates of the two alloys on grain boundaries and dislocations were basically the same.The softening mechanism was mainly attributed to the loss of dislocation strengthening.The higher Fe fiber density inhibited the average free migration path of dislocations and grain boundary migration in the alloy,which was the main reason for higher softening temperature of the alloy prepared by Process 2.展开更多
The isothermal corrosion testing, microscopic examination and the performance of Fe3Si alloy as materials of construction for bath hardware in continuous hot-dipping lines were studied. The corrosion of Fe3Si alloy in...The isothermal corrosion testing, microscopic examination and the performance of Fe3Si alloy as materials of construction for bath hardware in continuous hot-dipping lines were studied. The corrosion of Fe3Si alloy in molten zinc was controlled by attacking the grain boundaries preferentially. Aluminum reacted with iron of Fe3Si alloy firstly while the samples were immersed in molten zinc, although aluminum contents in the molten zinc were very low. The phase of reaction product was thought to be Fe2Al5. The corrosion rate of the Fe3Si alloy in molten zinc was determined to be approximately 2.9×10^-3 mm/h, therefore the liquid zinc corrosion resistance of Fe3Si alloy was very weak.展开更多
The effects of Sr,Mg,Cr,Sr/Mg and Sr/Cr combined additions on the Fe-containing intermetallic phase in a recycled Al-Si-Fe cast alloy are investigated.The experimental results show that the additions of Cr and Sr/Cr s...The effects of Sr,Mg,Cr,Sr/Mg and Sr/Cr combined additions on the Fe-containing intermetallic phase in a recycled Al-Si-Fe cast alloy are investigated.The experimental results show that the additions of Cr and Sr/Cr successfully modified the platelet and flake-likeβ-Al-5FeSi phases （β-compound） into the fibrousα-Al-8Fe-2Si （α-compound）.The additions of Sr and Sr/Mg were less effective to modify theβ-compound into theα-compound,while the eutectic Si was fully modified into the fibrous morphology.A small secondary dendrite arm spacing （DAS） was found in the Sr-added,Cr-added and Sr/Cr-added alloys,especially in a steel mold.The Sr,Sr/Cr and Sr/Mg combined additions modify the eutectic Si simultaneously.A sludge phase was found in the addition of Cr-added,Sr/Cr-added and Mg-added alloys,especially in the graphite mold casting.The volume fraction ofβ-compounds was decreased by the addition of various modifying elements. The Cr and Sr/Cr combined additions are very effective to modify theβ-compound for the recycled Al-Si-Fe based alloys.展开更多
基金financial supports from the Department of Science and Technology and other Provincial and Ministerial Level Projects,China(No.204306800086)Science and Technology Projects of Ganzhou Science and Technology Bureau,China(No.204301000194)the Science and Technology Project of Jiangxi Provincial Department of Education,China(No.204201400853)。
文摘The recrystallization and softening resistance of a Cu-6.5Fe-0.3Mg(mass fraction,%)alloy prepared by Process 1(cold rolling heat treatment)and Process 2(hot/cold rolling heat treatment)were studied using Vickers hardness tests,tensile tests,scanning electron microscopy and transmission electron microscopy.The softening temperature,hardness and tensile strength of the alloy prepared by Process 2 were 110°C,HV 15 and 114 MPa higher,respectively,than those of the alloy prepared by Process 1 after aging at 300°C.The recrystallization activation energy of the alloys prepared by Process 1 and Process 2 were 72.83 and 98.11 kJ/mol,respectively.The pinning effects of the precipitates of the two alloys on grain boundaries and dislocations were basically the same.The softening mechanism was mainly attributed to the loss of dislocation strengthening.The higher Fe fiber density inhibited the average free migration path of dislocations and grain boundary migration in the alloy,which was the main reason for higher softening temperature of the alloy prepared by Process 2.
基金financially supported by the Fundamental Research Funds for the Central Universities,China(No.2020CDJDPT001)the Chongqing Natural Science Foundation,China(No.cstc2021jcyj-msxm X0699)。
基金supported by the National Natural Science Foundation,China (No.52074131)the National Key R&D Project,China (No.2022YFC3900500)+2 种基金the International Technology Cooperation Program of Guangdong Academy of Sciences,China (No.2020GDASYL-20200504001)the Open Competition to Select the Best Candidate of Shangrao,China (No.2021A005)the BL13HB beamline of Shanghai Synchrotron Radiation Facility (SSRF)for providing synchrotron radiation beamtime (Nos.2020-SSRF-PT-011937,2021-SSRF-PT-017645).
基金This work was financially supported by the National Natural Science Foundation of China (No.50274005).
文摘The isothermal corrosion testing, microscopic examination and the performance of Fe3Si alloy as materials of construction for bath hardware in continuous hot-dipping lines were studied. The corrosion of Fe3Si alloy in molten zinc was controlled by attacking the grain boundaries preferentially. Aluminum reacted with iron of Fe3Si alloy firstly while the samples were immersed in molten zinc, although aluminum contents in the molten zinc were very low. The phase of reaction product was thought to be Fe2Al5. The corrosion rate of the Fe3Si alloy in molten zinc was determined to be approximately 2.9×10^-3 mm/h, therefore the liquid zinc corrosion resistance of Fe3Si alloy was very weak.
文摘The effects of Sr,Mg,Cr,Sr/Mg and Sr/Cr combined additions on the Fe-containing intermetallic phase in a recycled Al-Si-Fe cast alloy are investigated.The experimental results show that the additions of Cr and Sr/Cr successfully modified the platelet and flake-likeβ-Al-5FeSi phases （β-compound） into the fibrousα-Al-8Fe-2Si （α-compound）.The additions of Sr and Sr/Mg were less effective to modify theβ-compound into theα-compound,while the eutectic Si was fully modified into the fibrous morphology.A small secondary dendrite arm spacing （DAS） was found in the Sr-added,Cr-added and Sr/Cr-added alloys,especially in a steel mold.The Sr,Sr/Cr and Sr/Mg combined additions modify the eutectic Si simultaneously.A sludge phase was found in the addition of Cr-added,Sr/Cr-added and Mg-added alloys,especially in the graphite mold casting.The volume fraction ofβ-compounds was decreased by the addition of various modifying elements. The Cr and Sr/Cr combined additions are very effective to modify theβ-compound for the recycled Al-Si-Fe based alloys.